Abstract:Two MgCl2-supported Ziegler-Natta model catalysts were prepared by contacting activated MgCl2 with deficient or excess amount of TiCl4. Ethylene/1-hexene copolymerization with the catalysts was conducted under different 1-hexene feed, and active center concentration of the reaction system was determined by quench-labeling method using thiophene-2-carbonyl chloride as the quencher. The catalytic activity was only moderately enhanced (increment <50%) by adding 1-hexene in ethylene polymerization with the model catalyst (Cat-1) of 0.1 wt% Ti content, and the active center ratio ([C*]/[Ti]) was only slightly increased (from 64 to 72 mol%). The comonomer activation effect in Cat-1 catalyzed copolymerization was mainly attributed to increase of apparent propagation rate constant by the comonomer, which can be explained by reduction of mass transfer barrier in the polymer/catalyst particles because of larger monomer diffusion coefficients in the copolymer phase than in the more crystalline polyethylene phase. In contrast, the activity was nearly tripled by adding 1-hexene when the catalyst of 1.47% Ti content (Cat-2) was used, meanwhile its [C*]/[Ti] was also tripled (from 15 to 49 mol%). The strong comonomer activation effect in Cat-2 catalyzed copolymerization was caused by marked increase of active center concentration. In this case, fragmentation of the polymer/catalyst particles was intensified by adding the comonomer, and more active centers that were originally inaccessible to the cocatalyst and monomer were exposed through the particle fragmentation. According to the results of this work, the comonomer effect in conventional supported Ziegler-Natta catalysts can be explained by the combination of physical factor (increase in diffusion coefficient) and chemical factor (exposure of inaccessible active center precursors through particle fragmentation). (C) 2018 Elsevier Inc. All rights reserved.

Study on Ethylene-α-Olefin Copolymerization Catalyzed by the MgCl2-Supported and Low Ti-Loading Ziegler–Natta Catalyst

Ethylene polymerization using a novel MgCl2/SiO2-supported Ziegler–Natta catalyst

High temperature polymerization of propylene catalyzed by MgCl2-supported Ziegler–Natta catalyst with various cocatalysts

Highly active Ziegler-Natta Catalysts for propylene polymerization (2) effects of Al/Ti ratio and polymerization temperature

Copolymerization of ethylene and 1-dodecene catalyzed by novel low-Ti-loading Ziegler–Natta catalysts and their microstructures

Influence of Cocatalyst on High Temperature Polymerization of Propylene Catalyzed by Ziegler-Natta Catalyst

With different structure ligands heterogeneous Ziegler–Natta catalysts for the preparation of copolymer of ethylene and 1-octene with high comonomer incorporation

Study on preparation of polyolefins over complex support catalysts I. Preparation of ethylene-propylene copolymer over VOCl3/MgCl2/NaY ( SiO2)

Low Isotactic Polypropylene Synthesized with A Mgcl2/Alcl3-Supported Ziegler Catalyst

Synthesis of polyethylene with broad molecular weight distribution by Ziegler-Natta catalysts supported on doped MgCl2

Copolymerization of ethylene and 1-octene catalyzed by a modified Ziegler-Natta catalyst

Mechanistic Study on Comonomer Effect in Ethylene/1-Hexene Copolymerization with TiCl4/MgCl2 Model Ziegler-Natta Catalysts

Ethylene/1‐hexene Copolymerization with Supported Ziegler–Natta Catalysts Prepared by Immobilizing TiCl3(OAr) Onto MgCl2

Studies on Vocl3/Mgcl2/Nay/Al(2)Et(3)Cl(3) Complex Support Catalysts for the Copolymerization of Ethylene and Propylene

TiCl4/MgCl2/MCM-41 Bi-Supported Ziegler–Natta Catalyst: Effects of Catalyst Composition on Ethylene/1-Hexene Copolymerization

Ethylene/1-hexene copolymerization with MgCl 2 -supported Ziegler–Natta catalysts containing aryloxy ligands. Part I: Catalysts prepared by immobilizing TiCl 3 (OAr) onto MgCl 2 in batch reaction

Syntheses of Novel Electron Donors and Their Application to Preparation of Catalysts for Polyethylene with Broad Relative Molecular Mass Distribution

Studies on Synthesis of Low Isotactic Polypropylene by Using a Novel MgCl2-supported and Low Ti-loading Catalyst

Negative Comonomer Effect Induced by TiCl3-like Clusters in MgCl2-based Ziegler-Natta Catalysts

Study on the Distribution of Active Centers in Novel Low Ti-loading MgCl2-supported Ziegler-Natta Catalyst.

Effects of Ti/Mg molar ratio on bi-supported SiO2/MgCl2 (ethoxide type)/TiCl4 catalysts in ethylene homopolymerization and ethylene/1-hexene copolymerization