Properties of Si 69 modified starch/natural rubber composites by gas membrane coating reaction

Ai Junwei,Liu Fang,Zeng Zongqiang,Zhu Lixin,Jia Demin

DOI: https://doi.org/10.3969/j.issn.1000-1255.2011.06.008

2011-01-01

Abstract:Bis[3(triethoxy)silylpropyl]tetrasulfide(Si 69) modified starch was prepared by gas membrane coating reaction and mixed with natural rubber(NR) to obtain starch/NR composites.The surface hydrophobicity of Si 69 modified starch and the influence of Si 69 content on the curing characteristics,mechanical properties,processability,and dynamic properties of the composites were investigated.The morphological structure of the composites was characterized.The results showed that after pulverized by airflow pulverizer,the average particle size of starch decreased,the size distribution became narrow and the small particles increased.After modified with Si 69,hydrophilic starch became hydrophobic,and the value of contact angle reached maximum when the mass fraction of Si 69 was 5.0%.With increasing the amount of Si 69,the scorch time and optimum cure time of rubber compound increased,tensile strength,tear strength,and Shore A hardness of modified starch/NR composite increased,but elongation at break and permanent set decreased after first vulcanization.The mechanical properties of the composites were improved after post vulcanization at 70 ℃ for 24 h,but deteriorated at 100 ℃ for 24 h.With increasing the amount of Si 69,Payne effect of composites decreased,dispersibility of filler and processability of composite were improved.The value of loss factor at 60 ℃ decreased,so that rolling resistance decreased,and compression fatigue property of composites ere improved.The dispersion of Si 69 modified starch in natural rubber was improved,and the interfacial bond between starch and NR was strengthened.