Abstract:Creep-fatigue interaction is identified as a primary failure mode for components operating under high temperatures. As operational durations extend, this interaction not only alters the material's microstructures but also initiates a gradual degradation in mechanical properties, significantly impacting its deformation and damage behaviors. In this work, the dynamic microstructural evolution of GH4169 superalloy during creep-fatigue was elucidated via qualitative characterization, and damage level evaluation method was subsequently developed by bridging microstructure degradation to mechanical property degradation. Creep-fatigue tests were performed at 650 °C with various tensile holding times and were interrupted at lifetime fractions of 10 %, 50 % and 80 % for further analysis and tensile evaluations. Results revealed that the prolonged exposure to holding times induced the coarsening of γ″ precipitates alongside an increase in low-angle grain boundaries, culminating a reduction in creep-fatigue strength. The development of voids and cracks exacerbated the degradation of elongation, leading to a hybrid fracture mode encompassing both intergranular and transgranular cracking paths. Synthesizing microstructural evolutions to qualitatively categorize diverse degradation levels imparted a robust physical basis for damage evaluation. A mapping model was established to correlate the average kernel average misorientation (micro-degradation indicator) with the tensile plastic strain energy density (macro-degradation indicator). The damage level evaluation method was endowed with quantitative metrics utilizing this model, and its generality was additionally validated in P92 steel. This work offers an insight into the quantitative damage evaluations of creep-fatigue-induced degradations in materials, thereby providing a theoretical basis for the development of operation management and inspection plans of components.

Interpretation of damage mechanics behaviour of two-bar structures for the life extension of high-temperature components

Damage Mechanics Considerations for Life Extension of High-Temperature Components

Some Mechanics Principles for Life Extension of Components at Elevated Temperature

A coupled creep damage evolution model and creep life evaluation

Strength design and life assessment of welded structures subjected to high temperature creep

Damage model of life prediction under creep-fatigue interaction

Time-Dependent Deformation and Fracture of Multi-Material Systems at High Temperature

Research on Fatigue-Creep Interaction Damage of Steel 1.25Cr0.5mo

Theory of Visco-elasto-plastic Damage Mechanics

A life prediction method and damage assessment for creep-fatigue combined with high-low cyclic loading

Creep-fatigue Damage Level Evaluation Based on the Relationship Between Microstructural Evolution and Mechanical Property Degradation

Nonlinear Continuum Damage Mechanics Model on High Temperature Creep Analysis

Creep damage and fracture of weldments at high temperature

A new creep damage assessment method for metallic material under variable load conditions at elevated temperature

Coupling Crystal Plasticity and Continuum Damage Mechanics for Creep Assessment in Cr-based Power-Plant Steel

Some Fundamental Aspects of Redesign and Remanufacture of High Temperature Components

Creep-fatigue Reliability Assessment for High-Temperature Components Fusing On-Line Monitoring Data and Physics-of-failure by Engineering Damage Mechanics Approach

Modelling for Creep Cavitation Damage and Life of Three Metallic Materials

RECENT PROGRESS IN HIGH TEMPERATURE MECHANICAL BEHAVIOR OF MATERIALS AND STRUCTURES

Some Fundamental Aspects of High Temperature Defect Assessment

Time-Dependent Fracture and Defect Assessment of Welded Structures at High Temperature