Abstract:Despite superior clinical handling, excellent biocompatibility, biodegradation property of calcium phosphate needs to be improved to coincide with the rate of new bone formation. In this study, spherical CaCO3 are fabricated in the presence of the silk sericin and then transformed into porous hydroxyapatite (HAP) microspheres via hydrothermal method. The degradation behavior of obtained CaCO3, HAP and their mixture is first investigated in vitro. The result demonstrates that the weight loss of HAP microspheres are almost 24.3% after immersing in pH 7.40 Tris-HCl buffer solution for 12 weeks, which is far slower than that of spherical CaCO3 (97.5%). The degradation speed of the mixtures depends on the proportion of CaCO3 and HAP. The mixture with higher content of CaCO3 possesses a quicker degradation speed. The obtained CaCO3 and HAP microspheres are injected into subcutaneous tissue of ICR mice with the assistance of sodium alginate. The result in vivo also shows an obvious difference of degradation speed between the obtained CaCO3 and HAP microspheres, implying it is feasible to modulate the degradation property of the mixture through changing the proportion of CaCO3 and HAP The good cytocompatibility of the two kinds of microspheres is proved and a mild inflammation response is observed only at early stage of implantation. The job offers a simple method to modify the degradation properties of biomaterial for potential use in bone tissue engineering.

The Discussion About the Degradation of Calcium Polyphosphate in the Simulated Body Fluid

Controllable Degradation And Cytotoxicity Of Calcium Polyphosphate Bone Scaffold

Mechanical Properties and Degradation Properties in Vitro of Carbon Fiber Reinforced Hydroxyapatite/polylactide Composite

The Effect of Polymeric Chain-Like Structure on the Degradation and Cellular Biocompatibility of Calcium Polyphosphate

A Comparative Study of the in Vitro Degradation of Poly(l-Lactic Acid)/β-Tricalcium Phosphate Scaffold in Static and Dynamic Simulated Body Fluid

Degradable Performance and Bio-Mineralization Function of β-Tricalcium Phosphate/Poly(Lactic Acid) Tissue Engineering Scaffold in SBF

Degradation Behavior of Porous Calcium Phosphates

Cell-mediated degradation of strontium-doped calcium polyphosphate scaffold for bone tissue engineering.

A Comparative Study of the in vitro Degradation of Porous Calcium Phosphate Cements Scaffold in Static and Dynamic Simulated Body Fluid

The study on the degradation and mineralization mechanism of ion-doped calcium polyphosphate in vitro.

Crystalline structure and its effects on the degradation of linear calcium polyphosphate bone substitute

Microstructure and Controllable Degradation of Bioglass Reinforced Calcium Phosphate Scaffolds

Fabrication and Characterization of Porous Calcium Polyphosphate Scaffolds

DEGRADABILITY OF POROUS COMPOSITE SCAFFOLDS BASED ON Β-Tricalcium PHOSPHATE-BIOGLASS-POLY LACTIC ACID

In Vitro Degradation Behavior of Porous Calcium Phosphates under Diametral Compression Loading

Degradation pattern of porous CaCO3 and hydroxyapatite microspheres in vitro and in vivo for potential application in bone tissue engineering

Biomineralization of three kinds of porous composites for bone tissue engineering scaffolds in simulated body fluid

In Vitro Bioactivity and Degradability of Β-Tricalcium Phosphate Porous Scaffold Fabricated Via Selective Laser Sintering.

In Vitro Degradation of Β-Tcp/plla Scaffolds with Different Proportions of Β-Tcp

Preparation and Properties of Calcium Polyphosphate-Based Composite Scaffold for Bone Tissue Engineering

Degradable Performance and Bio-Mineralization Function of PLA-PEG-PLA/PLA Tissue Engineering Scaffold in SBF