Abstract:Magnesium hydroxide nanoparticles with different morphological structures of needle-, lamellar- and rod-like nanocrystals have been synthesized by solution precipitation reactions of alkaline with magnesium chloride in the presence of complex dispersants and characterized in terms of morphology, particle size, crystal habits and thermal behaviour by transmission electron microscopy, x-ray diffraction and thermogravimetric analysis. The sizes and morphologies of magnesium hydroxide nanocrystals can be controlled mainly by the reaction conditions of temperature, alkaline-injection rate and the concentrations of reactants. The data show that the needle-like morphology is of size 10 x 100 nm(2), the lamellar shape 50 nm in diameter and estimated 10 nm in thickness, and the rod-like nanoparticles 4 mm in length and 95 nm in diameter, respectively. All three kinds of nanoparticles are of hexagonal structures. The needle- and lamellar-like nanoparticles can be obtained by the reactions of alkaline injected into magnesium chloride solution at about 2 and 20 degreesC, respectively, while the rod-like nanoparticles can be prepared by a slower alkaline-injection rate and lower aqueous ammonia concentration at about 10 degreesC. The results obtained from the ethylene-vinyl acetate nanocomposites blended with the lamellar-like nanoparticles show that magnesium hydroxide nanocrystals possess higher flame retardant efficiency and mechanical reinforcing effect by comparison with common micrometre grade magnesium hydroxide particles.

Hydrothermal Preparation of Flame Retardant Mg(On)2

Effect of Hydrothermal Modification Conditions on Preparation of Flame Retardant Mg(OH)2 in Large-Scale Experimental Set-Up

Hydrothermal preparation of magnesium hydroxide with high dispersion, high purity,and high flame retardancy

Studies on Preparation of Flame Retardant Mg(OH)2 in a Large-scale Experimental Set-up with Different Temperature

Hydrothermal Modification of Flame Retardant Mg(OH)_2 Synthesized Via NH_3·H_2O Route in a Large-Scale Experimental Set-up

The Particle Formation during Preparation of Globular-flower-like Magnesium Hydroxide Flame Retardant

Preparation of Organic-Inorganic Compound Flame Retardant Based on Magnesium Hydroxide

Preparation and Application of Flame - Retard Type Magnesium Hydroxide

Preparation of Rod-like Magnesium Hydroxide Flame Retardant by Basic Magnesium Chloride Precursor

Research Progress of Flame Retardant Magnesium Hydroxide

Progress on fabrication and surface modification of Mg(OH)2Nanometer flame retardant

Additives Applied for Preparation of Superfine Mg(Oh)(2) Particles by Light-Burned Mgo at Low Temperature

Synthesis of magnesium hydroxide flame retardant based on microcrystalline magnesite and its application in epoxy resin

Research Progress of Flame-Retardant Polymers with Magnesium Hydroxide

Controlled Synthesis Of Magnesium Hydroxide Nanoparticles With Different Morphological Structures And Related Properties In Flame Retardant Ethylene-Vinyl Acetate Blends

Low-temperature synthesis of Mg(OH)2 nanoparticles from MgO as halogen-free flame retardant for polypropylene

Progress in Application and Research of Magnesium Hydroxide Flame Retardants

Structure Characterization of Loose Nano Magnesium Hydroxide as Flame Retardant

Fire Resistant & Smoke Vanishing Mechanism and Production Method of Flame Retardant Type Magnesium Hydroxide

Advances on Research and Development in Inorganic Flame Retardant Mg(OH)_2

Preparation of Magnesium Hydroxide Flame Retardant from Hydromagnesite and Enhance the Flame Retardant Performance of EVA