Abstract:Magnesium hydroxide nanoparticles with different morphological structures of needle-, lamellar- and rod-like nanocrystals have been synthesized by solution precipitation reactions of alkaline with magnesium chloride in the presence of complex dispersants and characterized in terms of morphology, particle size, crystal habits and thermal behaviour by transmission electron microscopy, x-ray diffraction and thermogravimetric analysis. The sizes and morphologies of magnesium hydroxide nanocrystals can be controlled mainly by the reaction conditions of temperature, alkaline-injection rate and the concentrations of reactants. The data show that the needle-like morphology is of size 10 x 100 nm(2), the lamellar shape 50 nm in diameter and estimated 10 nm in thickness, and the rod-like nanoparticles 4 mm in length and 95 nm in diameter, respectively. All three kinds of nanoparticles are of hexagonal structures. The needle- and lamellar-like nanoparticles can be obtained by the reactions of alkaline injected into magnesium chloride solution at about 2 and 20 degreesC, respectively, while the rod-like nanoparticles can be prepared by a slower alkaline-injection rate and lower aqueous ammonia concentration at about 10 degreesC. The results obtained from the ethylene-vinyl acetate nanocomposites blended with the lamellar-like nanoparticles show that magnesium hydroxide nanocrystals possess higher flame retardant efficiency and mechanical reinforcing effect by comparison with common micrometre grade magnesium hydroxide particles.

The Particle Formation during Preparation of Globular-flower-like Magnesium Hydroxide Flame Retardant

Preparation of Rod-like Magnesium Hydroxide Flame Retardant by Basic Magnesium Chloride Precursor

Controlled Synthesis Of Magnesium Hydroxide Nanoparticles With Different Morphological Structures And Related Properties In Flame Retardant Ethylene-Vinyl Acetate Blends

Preparation of Organic-Inorganic Compound Flame Retardant Based on Magnesium Hydroxide

Preparation and Application of Flame - Retard Type Magnesium Hydroxide

Additives Applied for Preparation of Superfine Mg(Oh)(2) Particles by Light-Burned Mgo at Low Temperature

Fire Resistant & Smoke Vanishing Mechanism and Production Method of Flame Retardant Type Magnesium Hydroxide

Structural Characteristics and Flame-Retardant Properties of Nanosized Magnesium Hydroxide

Synthesis of magnesium hydroxide flame retardant based on microcrystalline magnesite and its application in epoxy resin

Progress on fabrication and surface modification of Mg(OH)2Nanometer flame retardant

Effect of Hydrothermal Modification Conditions on Preparation of Flame Retardant Mg(OH)2 in Large-Scale Experimental Set-Up

Studies on Preparation of Flame Retardant Mg(OH)2 in a Large-scale Experimental Set-up with Different Temperature

FMagnesium hydroxide-based flame-retardant fillers for polymer materials and the effect of particle size on the dehydration process at high temperatures

Hydrothermal Modification of Flame Retardant Mg(OH)_2 Synthesized Via NH_3·H_2O Route in a Large-Scale Experimental Set-up

Analysis of atomization characteristics and efficient synthesis of Mg(OH)2 in micron scale atomization reactor

Improving the flame retardance of hydrophobic silica aerogels through a facile post-doping of magnesium hydroxide

Low-temperature synthesis of Mg(OH)2 nanoparticles from MgO as halogen-free flame retardant for polypropylene

Preparation of Magnesium Hydroxide Dry Powder by Hydrating Method

Effect of dispersion of nano-magnesium hydroxide on the flammability of flame retardant ternary composites

Magnesium Hydroxide Sulfate Hydrate Whisker Flame Retardant Polyethylene/montmorillonite Nanocomposites

Preparation of Magnesium Hydroxide Flame Retardant from Hydromagnesite and Enhance the Flame Retardant Performance of EVA