Abstract:Low-cycle fatigue (LCF) behavior of nickel-based precipitation-strengthened superalloy GH4145/SQ was investigated systematically under fully reversed total strain amplitude control conditions at 538°C in laboratory air. It was shown that the alloy exhibited a pronounced initial fatigue hardening followed by continuous fatigue softening to failure at high strain amplitudes, while at low strain amplitudes the initial hardening was followed by a well-defined saturation stage. Microstructure observations using optical and transmission-electron microscopy revealed that slip band density increased with increasing total strain amplitudes and the size of the γ′precipitates tended to reduction due to repeated shearing by the dislocations with continuous cyclic straining. The above changes in microstructures during cycling were essentially responsible for the fatigue hardening–softening behavior of the alloy. Both optical and SEM micrographs indicated that at low strain amplitudes crack propagation was basically transgranular, while at high strain amplitudes crack propagation was essentially intergranular. Bilinear behavior with a change of slope at a plastic strain amplitude of about 0.2pct was observed in cyclic stress–strain (CSS), Coffin–Manson (C–M) and plastic strain energy–life plots. A change in the number of operating slip systems and the fracture modes with the strain amplitude employed was used to explain this two-slope characteristic. In both the companion specimens test (CST) and the incremental step test (IST) methods the alloy exhibited non-masing type behavior. It was suggested that, for the first approximation, the half-life plastic strain energy could be calculated directly according to the equation without reckoning in the non-masing behavior.

Dislocation structure in a single-crystal nickel-base superalloy during low cycle fatigue

Low cycle fatigue behavior of nickel-based superalloy GH4145/SQ at elevated temperature

Shearing Mechanisms of Stacking Fault and Anti-Phase-boundary Forming Dislocation Pairs in the Γ′ Phase in Ni-based Single Crystal Superalloy

Influence of Strain Amplitude on Low-Cycle Fatigue Behaviors of a Fourth-Generation Ni-Based Single-Crystal Superalloy at 980 °C

Dislocation Structure Due to High Temperature Deformation in Γ′ Phase of a Nickel-Base Superalloy

Cyclic Deformation Behavior of a Nickel-Base Superalloy under Fatigue Loading

Life Assessment of Anisotropic Low Cycle Fatigue of Nickel-Base Single Crystal Superalloy

High Temperature Low-Cycle Fatigue, Deformation Microstructure and Final Fracture Behavior of a Nickel-Base Superalloy

Fatigue Fracture Mechanism of a Nickel-Based Single Crystal Superalloy with Partially Recrystallized Grains at 550 C by In Situ SEM Studies

Deformation mechanisms of CoCrFeMnNi high-entropy alloy under low-cycle-fatigue loading

Formative and controlled mechanisms of nano-sized γ′ precipitates with local phase-transition within dislocation networks of nickel-based single crystal superalloys

Effect of Lattice Misfit on the Evolution of the Dislocation Structure in Ni-based Single Crystal Superalloys During Thermal Exposure

Evolution of fatigue mechanical properties and micro defects in nickel-based single crystal superalloys: A molecular dynamics research

High-Temperature Creep Behavior of a Nickel-Based Single-Crystal Superalloy with Small-Angle Deviation from [111] Orientation

Temperature Effect on Low-Cycle Fatigue Behavior of Nickel-Based Single Crystalline Superalloy

Interfacial dislocation evolution and yield mechanism of nickel-based single crystal superalloy: A molecular dynamics research

Low Cycle Fatigue and High Cycle Fatigue of K4750 Ni-based Superalloy at 600 °C: Analysis of Fracture Behavior and Deformation Mechanism

Micro-strain and cyclic slip accumulation in a polycrystalline nickel-based superalloy

Low cycle fatigue of a nickel based superalloy at high temperature: deformation microstructures

Deformation mechanisms of low cycle fatigue of a fourth generation Ni-based single crystal superalloy

Stable Configurations of Dislocations in Homogenized Nickel Aluminide Single Crystals