Abstract:A simple method for synthesis of titanium carbide (TiC) nanofibers by a modified carbothermal reduction of electrospun titanium-based fibers is reported. The effect of synthesis steps on the final product is discussed. Continuous TiC fibers synthesized have a smooth surface morphology, with average diameter of 148 nm and length in the centimeter range. X-ray diffraction and high-resolution transmission electron microscopy analysis results indicate that the fibers consist of TiC of high purity. Impact of heat treatment on the morphology and chemical and crystalline composition of the product is also investigated. Based on the experimental evidence, it is hypothesized that the carbothermal reduction of calcined electrospun fibers with precoated carbon proceeds through diffusion-limited shrinking core pathway while that of the as-spun fibers follows the reaction-limited solution precipitation mechanism. The TiC nanofibers also show superior sintering properties by increasing theoretical density of hot pressed TiB2 from 94.5% of theoretical density to 97.9% of theoretical density. When sintered with ceria, it improves the conductivity of the ceria by 18.29 times as compared to 2.94 times by TiC nanoparticles at 800 °C. The TiC nanofibers show metallic behavior as well as potential for application as electrochemical double layer capacitor supercapacitors.

Synthesis of titanium carbide nanowires

Synthesis and Field Emission Properties of Titanium Carbide Nanowires

Synthesis of carbon nanotubes filled with Fe3C nanowires by CVD with titanate modified palygorskite as catalyst

A gas-solid reaction growth of dense TiO 2 nanowire arrays on Ti foils at ambient atmosphere

Synthesis and Field Emission Characterization of Titanium Nitride Nanowires

In-situ Synthesis of Nanocrystalline TiC Powders, Nanorods, and Nanosheets in Molten Salt by Disproportionation Reaction of Ti(II) Species

Synthesis and Characterization of TiC Nanofibers Obtained via a Modified Carbothermal Process

Synthesis of Silicon Carbide Nanowires in a Catalyst-Assisted Process

A Simple Method to Synthesize Nanowires Titanium Dioxide from Layered Titanate Particles

Formation Of Nanocrystalline Tic By A Low-Temperature Route

Microwave Synthesis of Nano-Titanium Carbide

Cu-assisted Fast Synthesis of TiO_2 Nanowires in Ambient Pressure under Cu-Ti Eutectic Temperature

Using A Cobalt Activator to Synthesize Titanium Carbide (tic) Nanopowders

Synthesis of Tungsten Carbide Nanocrystal Via A Simple Reductive Reaction

Direct Synthesis of Controllable Microstructures of Thermally Stable and Ordered Mesoporous Crystalline Titanium Oxides and Carbide/Carbon Composites

A Simple Route to Prepare Nanocrystalline Titanium Carbonitride

Synthesis And Characterization Of Carbide Nanorods

Carbide Nanoparticles Encapsulated in the Caves of Carbon Nanotubes by an in Situ Reduction-Carbonization Route

Synthesis of Nanocrystalline Titanium Nitride Powders by Direct Nitridation of Titanium Oxide

Synthesis and Characterization of SiC Nanowires Using Silicon Evaporation

A Generic Bamboo-Based Carbothermal Method For Preparing Carbide (Sic, B4c, Tic, Tac, Nbc, Tixnb1-Xc, And Taxnb1-Xc) Nanowires