C-doped WO3 Microtubes Assembled by Nanoparticles with Ultrahigh Sensitivity to Toluene at Low Operating Temperature

Xiaohu Ding,Dawen Zeng,Shunping Zhang,Changsheng Xie

DOI: https://doi.org/10.1016/j.snb.2010.11.030

IF: 9.221

2010-01-01

Sensors and Actuators B Chemical

Abstract:Novel C-doped WO3 microtubes (MTs) were successfully synthesized by a facile infiltration and calcination process using the cotton fibers as templates. The prepared MTs were characterized by X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), field emission scanning electron microscopy (FESEM), N2 adsorption and desorption measurements and ultraviolet–visible spectroscopy. XPS spectra show the carbon was doped into the lattice of the WO3 phase, resulting in a decrease of the band gap of the C-doped WO3 MTs from 2.45eV to 2.12eV. Moreover, the WO3 MTs were assembled by nanoparticles in size of ca. 40nm and had larger specific surface area (21.3m2/g) due to existence of meso/macro-pores inside them. At low operating temperature of 90°C, the gas sensor based on the C-doped WO3 MTs had a detected limit of 50ppb to the toluene gas (response of 2.0). The enhancement of toluene sensing performance of C-doped WO3 MTs was attributed to a larger surface area and higher porosity, which arises from its unique MTs. Furthermore, the band gap reduction and a new intragap band formation for C-doped WO3 MTs were proposed as the reason for the decrease in optimal operating temperature.