Tuning the sensing selectivity of mesoporous hierarchical Ti-doped Co 3 O 4 to toluene and xylene via controlling the oxygen defects

Huan Liu,Shao Jin,Kun Zhang,Yu Jiang,Yongjun Feng,Dianqing Li,Pinggui Tang

DOI: https://doi.org/10.1016/j.apsusc.2022.156079

IF: 6.7

2022-12-26

Applied Surface Science

Abstract:Vast efforts have been made to develop high-performance gas sensing materials for the detection of harmful volatile organic compounds (VOCs) like toluene and xylene. However, it is challenging to selectively detect toluene and xylene simultaneously. Herein, the hierarchical Ti-doped cobalt layered hydroxides miscrospheres were synthesized first and sintered at high temperature consequently to prepare hierarchical Ti-doped Co 3 O 4 miscrospheres. The incorporation of Ti into the lattice of Co 3 O 4 decreased the crystal sizes and crystallinity, resulting in higher specific surface area and more oxygen defects. Interestingly, the 3 at.% Ti-doped Co 3 O 4 miscrospheres sintered at 450 °C exhibited the highest response of 64.9 to 50 ppm of xylene at 210 °C, while the 1 at.% Ti-doped Co 3 O 4 miscrospheres calcined at 500 °C displayed the highest response of 57.2 to 50 ppm of toluene at 240 °C, which were about 11.8 and 7.8 times higher in comparison with pristine Co 3 O 4 . The different selectivity of Ti-doped Co 3 O 4 to toluene and xylene arises from the different amounts of oxygen vacancies and defect oxygen ions. The obtained Ti-doped Co 3 O 4 microspheres also showed the merits of good selectivity, repeatability and long-term stability, indicating the promising applications of Ti-doped Co 3 O 4 miscrospheres in the detection of toluene and xylene.

chemistry, physical,physics, applied, condensed matter,materials science, coatings & films