Mircostructure and Properties of Laser Cladding FeCoCrMoCBY Coating with Different Pulse Frequencies
Gong Yubing,Wang Shanlin,Huang Yong,Li Hongxiang,Nie Guimao,Chen Yuhua
DOI: https://doi.org/10.13373/j.cnki.cjrm.XY16060021
2017-01-01
Abstract:High-density Fe-based alloy amorphous coating was fabricated on the surface of mild steel by laser cladding , and then the effect of pulse frequency on the microstructure and properties of the coatings were studied .The formation, microstructure characterization , microhardness and corrosion resistance of the coatings were investigated by optical microscope ( OM) , X-ray diffraction ( XRD) , scanning electron microscopy (SEM), microhardness tester and electrochemical workstation , respectively.The results showed that the coatings were mainly constituted by amorphous materials .With the decrease of pulse frequency , the thickness of the coatings decreased , and the dilution rate also got lower , and the amorphization in coating happened easily .Moreover , the dilution rate dramatically went down by a-bout 50%and no distinct crystallization phase was observed when frequency was 1.0 Hz.With the decrease of pulse frequency , fusion zone width increased and the tendency of columnar crystals along the epitaxial growth got low , in addition the microhardness increased firstly and then decreased and the corrosion resistance firstly obviously got strong and then vulnerable , which had more excellent corrosion resistance than 316L stainless steel in the 3.5%NaCl solution.When frequency was 1.0 Hz, there were compact structure of the coat-ing, and average microhardness exceeded HV 1315, which was about 9 times as much as the substrate .When the low corrosion current density and passive current density were about 1.81 ×10-8 , 7.10 ×10-7 A· cm-2 , the corrosion resistance was best .