Formation and Decomposition of Surface Ethoxy Species on Acidic Zeolite Y.
W Wang,J Jiao,YJ Jiang,SS Ray,M Hunger
DOI: https://doi.org/10.1002/cphc.200500262
IF: 3.52
2005-01-01
ChemPhysChem
Abstract:It is generally accepted that free carbenium cations mostly exist as transition states rather than as long-lived intermediates in acid-catalyzed reactions performed on acidic zeolites. Surface alkoxy species with carbenium-like properties are suggested to be, most likely, the catalytic intermediates in zeolite chemistry. However, these surface alkoxy species on acidic zeolite catalysts are not easy to detect by solid-state NMR spectroscopy, which hinders further elucidation of their catalytic role in heterogeneous catalysis. For example, the C NMR observation of simple surface ethoxy species has never been reported on acidic zeolites, although it has been predicted that the stability of surface alkoxy species on acidic zeolites follows the order of ethoxy>propoxy> tert-butoxy. The difficulties in observing surface alkoxy species on acidic zeolites by NMR spectroscopy may lie in two aspects: In the case of olefin adsorption on acidic zeolites, fast oligomerization of olefins takes place even at ambient temperature in comparison with the slow detection by NMR spectroscopy. In the case of alcohol adsorption on acidic zeolites, on the other hand, removal of water is necessary because water will readily quench-off surface alkoxy species to the corresponding alcohols. However, most solid-state NMR investigations were performed under batch conditions with samples in fused glass ampoules or in gas-tight rotors, where further evacuation in vacuum at proper temperatures can hardly be achieved to remove water and to prevent the further reaction of surface alkoxy species. Herein, the first solid-state C magic-angle spinning (MAS) NMR evidence for the existence of surface ethoxy species on acidic zeolite Y by applying a stopped-flow protocol is presented. Moreover, the further decomposition of surface ethoxy species to hydrocarbons and carbenium cations at elevated reaction temperatures was studied by the new developed in situ MAS NMR–UV/Vis spectroscopy. Figure 1a shows the in situ C cross-polarization (CP)/MAS NMR spectrum recorded at 295 K after continuous injection of C-1-enriched ethanol, CH3 CH2OH, into the MAS NMR rotor reactor, containing calcined zeolite H-Y, and subsequent purging with dry nitrogen (200 mLmin ). The spectrum is dominated by a signal at 60.5 ppm, due to the C-enriched methylene carbon of ethanol, and spinning sidebands marked by asterisks. The weak signal at 15.8 ppm is caused by the methyl carbon of ethanol. No conversion of ethanol was observed at 295 K. After purging the loaded catalyst with dry nitrogen (200 mLmin ) at 453 K to remove water and physisorbed ethanol, the C CP/MAS NMR spectrum is dominated by a signal at 72.6 ppm with spinning sidebands characteristic for strongly bound surface species (Figure 1b). The signal at 72.6 ppm was therefore assigned to surface ethoxy species [SiO(CH2CH3)Al] , while the signal at 61.7 ppm was due to terminal ethoxy species [SiO(CH2CH3)] and/or strongly bonded ethanol. Similar to surface methoxy species, the above-mentioned assignment of the signal at 72.6 ppm to surface ethoxy species was strongly supported by their reaction with water. Figure 1c shows the in situ C CP/MAS NMR spectrum recorded after water was deliberately loaded onto the working catalyst at 295 K. The reoccurrence of the ethanol signal at 60.5 ppm confirms the former formation of surface ethoxy species via the stopped-flow protocol. Therefore, assignments of the signals at 72.6 and 61.7 ppm to other species, for example, diethyl ether or oligomeric alkoxy species, can be excluded. The deconvolution of the C CP/MAS NMR spectrum of surface ethoxy species on acidic zeolite Y (Figure 1d) allows the determination of the chemical shift anisotropy Ds, the asymmetry parameter h, and the relative intensity I for each signal Figure 1. C CP/MAS NMR spectra of zeolite H-Y recorded after continuous injection of CH3 CH2OH into the MAS NMR rotor reactor at 295 K and subsequent purging with dry nitrogen at 295 K for 2 h (a), after subsequent purging with dry nitrogen at 453 K for 2 h (b), and after injection of water into the MAS NMR rotor reactor at 295 K (c). Spectrum d) shows the deconvolution and simulation of the C CP/MAS NMR spectrum b) of surface ethoxy species on zeolite H-Y using the Bruker software WINFIT. Asterisks denote spinning sidebands.