Crystallization kinetics of polyetheretherketone during high temperature-selective laser sintering
Peng Chen,Haosong Cai,Zhaoqing Li,Maoyuan Li,Hongzhi Wu,Jin Su,Shifeng Wen,Yan Zhou,Jie Liu,Congjun Wang,Chunze Yan,Yusheng Shi
DOI: https://doi.org/10.1016/j.addma.2020.101615
IF: 11
2020-12-01
Additive Manufacturing
Abstract:<p>Understanding the complicated crystallization process is important for controlling the performance reproducibility and stability in high temperature-selective laser sintering (HT-SLS). Therefore, in this paper, the performance of HT-SLS processed polyetheretherketone (PEEK) is analyzed from the perspective of crystallization kinetics. It is found that each layer of sintered powder undergoes the dynamic non-isothermal crystallization promoted by cold powder coating (CPC) and the quasi-static isothermal crystallization during the part bed temperature (<em>T<sub>b</sub></em>) maintenance of HT-SLS. The kinetic analysis shows 321 °C is a theoretical <em>T<sub>b</sub></em> for PEEK. However, due to the great sensitivity to the temperature drop of CPC, the practical <em>T<sub>b</sub></em> is set around 332 °C, at which the <span class="math"><math>1/t1/2</math></span> approaches zero according to the extrapolated analysis of Hoffman-Lauritzen theory. The shrinkage is only caused by the dynamic non-isothermal crystallization of CPC, and the minimum powder feeding temperature is found to be 250 °C by Nakamura analysis. In addition, the quasi-static maintaining of <em>T<sub>b</sub></em> during HT-SLS can lead to extended planar subunit along <em>c</em>-axis, increased crystallite size perpendicular to (1 1 0) and (2 0 0), and higher mechanical strength.</p>
engineering, manufacturing,materials science, multidisciplinary