Abstract:The anodic polarization response of magnesium alloy AZ31 was first characterized during exposure to aerated 0.1 M NaCl solutions with millimolar additions of NaVO3, Na3PO4, Na2HPO4, NaF and various pairings to assess their ability to inhibit corrosion kinetics and retard localized corrosion. Each of the candidate inhibitors reduced the corrosion rate of the alloy to some degree. A Na3PO4–NaVO3 pair produced a good inhibiting effect decreasing the corrosion rate to about 10−7 A/cm2, which was two orders of magnitude lower than the uninhibited control case. A Bliss Independence assessment indicated that this inhibitor pair acted synergistically. A Na2HPO4–NaVO3 pair reduced the corrosion rate to 10−6 A/cm2 but was not assessed to be acting synergistically. The NaVO3–NaF pair did not reduce the corrosion rate significantly compared to the control case and was an antagonistic pairing. SEM imaging showed film formation due to exposure, which appears to be the origin of the observed inhibition. The resistance to localized corrosion was assessed as the difference in the breakdown potential and the corrosion potential, with larger values indicating a lower probability of localized corrosion during free corrosion exposures. The effects of the inhibitors on this characteristic were mixed, but each of the inhibitor pairs yielded potential differences in excess of 100 mV. A conceptual conversion coating process based on a mixture of vanadate and phosphate compounds were demonstrated. A fluoride-bearing formulation produced coatings whose total impedance was increased by a factor of two compared to an uncoated control. A fluoride-free formulation produced coatings whose corrosion resistance was increased by more than a factor of three.

Effect of KF Trace Addition on Corrosion Behaviors of Magnesium Alloys in a Commercial Coolant

Effect of Potassium Fluoride in Electrolytic Solution on the Structure and Properties of Microarc Oxidation Coatings on Magnesium Alloy

The Effects of ECAP, Mn and Ca Elements on the Microstructure and Corrosion Properties of Magnesium Alloys Were Investigated

The Corrosion Behaviours of AZ61 Magnesium Alloy with the Ca Addition

Effect of Fluoride Treatment on Corrosion Property of AZ31 Magnesium Alloy in Hank's Solution

Protective Effects of a New Type Cover Gas on Molten Magnesium Alloy

Effect of Heat Treatment on Corrosion and Electrochemical Behaviour of Mg–3Nd–0.2Zn–0.4Zr (wt.%) Alloy

Effects of Sodium Fluoride on Structure and Corrosion Resistance of Plasma Electrolytic Oxidation Ceramic Coatings on Magnesium Alloys

Corrosion Behaviors of Fluoride Treated Cast Magnesium Alloy in Hank’s Solution

Corrosion Behavior of Fluorine-Doped Calcium Phosphorus Coating on AZ31 Alloy with Various Chemical Conversion Parameters

Corrosion behavior of AZ31 magnesium alloy with calcium addition

Effect of Calcium Content on Corrosion Resistance of Az61-1.2y Magnesium Alloys

The Effect of Vanadate, Phosphate, Fluoride Compounds on the Aqueous Corrosion of Magnesium Alloy AZ31 in Dilute Chloride Solutions

Modulation effects of K2ZrF6 additive on microstructure and heat resistance of micro-arc oxide coatings fabricated on LY12 aluminum alloy

INFLUENCE OF YTTRIUM AND GADOLINIUM ON CORROSION RESISTANCE OF AZS1 MAGNESIUM ALLOYS

Micro-arc oxidization of a novel Mg-1Ca alloy in three alkaline KF electrolytes: Corrosion resistance and cytotoxicity

Effect of Potassium Fluoride on the In-Situ Sealing Pores of Plasma Electrolytic Oxidation Film on AM50 Mg Alloy

Modulation Effects of K_2ZrF_6 Additive on Microstructure and Heat Resistance of Micro-arc Oxide Coatings Fabricated on LY12 Aluminum Alloy

Corrosion Properties of AZ31 Magnesium Alloy and Protective Effects of Chemical Conversion Layers and Anodized Coatings

Improvement of bio-compatible AZ61 magnesium alloy corrosion resistance by fluoride conversion coating

INFLUENCE OF YTTRIUM AND GADOLINIUM ON CORROSION RESISTANCE OF AZ81 MAGNESIUM ALLOYS