Abstract:Since the period required for testing the atmospheric corrosion of steel is long, most studies have focused on the corrosion behavior in less than three years, making exploring long-term atmospheric corrosion particularly valuable. This study investigates the corrosion behaviors, corrosion models, and mechanical properties of Q235 welded steel pipes collapsing due to corrosion after 25-year service in an urban industrial atmospheric environment using SEM, XRD, electrochemical methods, 3-D noncontact surface profilometry, and static tensile testing. The typical morphologies of & alpha;-FeOOH, & gamma;-FeOOH, and Fe3O4 and the effect of the content of various corrosive materials on the corrosion rate of the steel pipes are identified and analyzed. Then, the influence of different corrosion degrees on the mechanical properties of the steel pipes is examined by considering the morphologies of the rust pits. The results show that the wetting-drying cycles affect the structures of the rust layers and their protective properties. The rust layers on the sheltered surface are thicker but less protective than those on the exposed surface. In the wet state, FeSO4 accelerates ion transfer, while Fe3O4 facilitates electron transfer. These processes collectively contribute to the corrosion of Q235 steel. Moreover, as the time-of-wetness of the rust layers on sheltered specimens increases, the corrosion rate of Q235 steel also accelerates. The corrosion model combines pitting and uniform corrosion and gradually changes from predominated by pitting to thickness as the corrosion degree increases. The corrosion morphology impacts the mechanical properties of the welded steel pipes, and the influences of the thickness loss and maximum rust pit depth on these properties are profound.

Corrosion Behavior and Corrosion Products of a Low-Alloy Weathering Steel in Qingdao and Wanning

Corrosion Behaviors of the Exposed Side and Underside of Low Alloy Weathering Steel in Qingdao and Wanning for 18 Months

Investigation of marine atmospheric corrosion of a new developed low carbon bainitic steel

Corrosion Behaviors and Mechanical Properties of Q235 Steel Pipes Collapsing Due to Corrosion after 25-Year Service in Urban Industrial Atmospheric Environment

Corrosion behavior of weathering steel in marine atmosphere

Corrosion Behaviors and Mechanisms of New Weathering Steel and Carbon Steel in Simulated Industrial Atmosphere

Investigation of Microstructure and Corrosion Behavior of Weathering Steel in Aqueous Solution Containing Different Anions for Simulating Service Environments

Corrosion Behavior of New Weathering Steel in the Environment Simulating Coastal Industrial Atmosphere

Corrosion Behaviors of Weathering Steels in the Actual Marine Atmospheric Zone and Immersion Zone

Short-term Exposure of Low-Alloyed Steels in Qinghai Salt Lake Atmosphere

Insight to atmosphere corrosion behavior of Q345NH steel in Wenchang tropical marine environment

Analysis of Corrosion Data of Four Kinds of Weathering Steels Exposed to Atmosphere in Qingdao for 6 Years

Corrosion Behavior of Low-Alloy Weathering Steel in Environment Containing Chloride Ions

Atmospheric Corrosion Behavior of Low-Alloy Steels in a Tropical Marine Environment

Corrosion behavior of the low alloy weathering steels coupled with stainless steel in simulated open atmosphere

Corrosion behavior of the low alloy weathering steels in stagnant water

Characterization of the Corrosion Products Formed on Carbon Steel in Qinghai Salt Lake Atmosphere

ANALYSIS FOR THE REASON OF CORROSION RESISTANCE "REVERSION" OF CONTAINING CHROMIUM LOW ALLOY STEELS IN SEAWATER

Corrosion behavior of high strength weathering steels in simulated industrial atmosphere environment

Corrosion Behavior of Hot-Dip Galvanized Sheet Steel in Different Seawater Zones in Qingdao

Investigation of the Corrosion Resistance of Weathering Steel at Different Atmospheric Environment