Microstructure Control and Corrosion Properties of AlCoCrFeNiTi0.5 High-Entropy Alloy

Yu Yuan,Xie Faqin,Zhang Tiebang,Kou Hongchao,Hu Rui,Li Jinshan
DOI: https://doi.org/10.3969/j.issn.1002-185X.2012.05.023
2012-01-01
Rare Metal Materials and Engineering
Abstract:The microstructures, hardness and electrochemical properties of AlCoCrFeNiTi0.5 high-entropy alloys fabricated by cold crucible levitation melting (CCLM) with as-cast structure and tempering treated structures were investigated. The results show that in contrast to suction casting using copper molds, CCLM causes the growth of dendrite phase and separation of omega phase. As the increase of temperature, the dendrite grains grow up, the amount of eutectic structures increases, and the intensity of BCC peak shows a rising trend after the first drop. At the temperature of 800 degrees C, the dendrite grains become refined. And then, as the temperature increases, the element segregation of interdendrite is weakened. The alloy exhibits a superior resistance to tempering and softening property. Furthermore, pitting corrosions are mainly concentrated in the place between dendrite phase and eutectic alpha phase. The tempering treatment improves corrosion properties in a 3.5% NaCl solution, and the alloy tempered at 700 exhibits the best corrosion property among the experimental alloys.
What problem does this paper attempt to address?