Abstract:From the viewpoint of welding mechanics, a new welding technology-trailing peening was applied firstly to weld aluminum alloy LY12CZ sheet with high susceptibility to hot cracking. Trailing peening can exert a transverse extrusion strain on the metal in brittle temperature region (BTR) Which can compensate for the tensioning strain during the cooling procedure post welding. So, welding hot cracking of LY12CZ sheet can be controlled effectively on the special fig for hot cracking experiment, and the phenomenon of hot cracking can't be found in specimens with large dimensions finally. At the same time, welding with trailing peening can decrease welding distortion caused by longitudinal and transverse shrinkage of weld obviously. Due to strengthening the poor position-weld toe during the process of welding, the residual stress distribution of welded joint is more reasonable. Contrast with conventional welding, mechanical properties such as tensile Strength, prolongation ratio and cold-bending angle of welded joint with trailing peening can be improved obviously, and rupture position of welded joint transits from weld toe at conventional welding to weld metal at trailing peening. So, welding with trailing peening can be regarded as a dynamic welding method with low stress, little distortion and hot cracking-free really. As far as theoretical analysis is concerned, the technology of trailing peening can be used to weld the materials with high susceptibility to hot cracking such as LY12CZ and LD10, and solve the welding distortion of thin plate-shell welded structures which contain closed welds such as flange. In addition, the technology of trailing peening has many advantages: simple device, high efficiency, low cost and flexible application which make the welding method hove widely applied foreground in the field of aeronautics and aerospace.

New Method to Control Residual Stresses and Distortion by Welding with Trailing Rotating Extrusion

A New Method to Control Welding Distortion with Impactive Rotating

Method to control welding stress and distortion with trailing impact rolling

Several new in-process control methods for the welding of aluminum alloy thin-plate structures

Reverse Deformation Design for Bending Control in Welding of Ring Stiffeners

Controlling of Welding Residual Stress and Deflection Distortion for Flat Plate by Longitudinal Pre-stress Method

Strain Field Analysis of Weld with Trailing Impact Rolling to Control Residual Stress and Distortion and Prevent Hot Cracking

Numerical Prediction and Control of Deformation and Residual Stress in Double-Sided Arc Welding of Large Pressure Hull

Finite element analysis of controlling the TC4 thin plate weldment wave-like deformation by welding with impacting rotation

Controlling of stress and distortion in thin copper plate by welding with trailing peening

Controlling welding residual stress and distortion by a hybrid technology of transient thermal tensioning and trailing intensive cooling

Control of Titanium Alloy Thin Plate Welding Distortion by Trailing Peening

Mechanism of Weld with Trailing Impact Rolling to Control Residual Stresses Deformation and Hot Cracking

Control of Buckling Distortion of TC4 Thin Plate by Impact Revolution Pressing During Welding Process

Welding Distortion Control of Thin Al Alloy Plate by Static Thermal Tensioning

Welding Deformation Controlling of Aluminum-Alloy Thin Plate by Two-Direction Pre-Stress Method

New Technique To Control Welding Buckling Distortion And Residual Stress With Non-Contact Electromagnetic Impact

New development in welding thin-shell aluminum alloy structures with high strength

Numerical simulation of controlling in titanium alloy sheets welding residual stress by trailing peening

Welding TC4 Thin Plates by Revolution Pressing in Welding Process

A new method for welding aluminum alloy LY12CZ sheet with high strength