Morphology Study o f Bioactive Glass Affecting Mice Osteoblast Proliferating in vitro

YANG Yu-sheng,SUN Jun-ying

DOI: https://doi.org/10.3969/j.issn.1672-6278.2007.02.011

2007-01-01

Journal of Biomedical Engineering Research

Abstract:To observe the effects of bioglass to osteoblast proliferating by adding bioactive glass(bioglass) to culture fluid.Bioglass crystal were dissolved to Dulbecco's modified eagle medium(DMEM) fluid,the four ionics concentration viz Na、Ca、P、Si were determined.The mice osteoblastes were cultured by the control group and the experimental group respectively to observe cell growth shape.The osteoblast growth index were determined and growth curves were drawn.The fromazan shape in cell was observed kineticaly.The ultramicrostructure of osteoblast were also observed.Results showed that the Si ionic concentration was 26.12% in experimental groups relative to control groups(P<0.01),Ca ionic concentration was 88.03%(P<0.01),P isonic concentration was 73.23%(P<0.01),there was no difference in Na ionic concentration(P>0.05).The comparative results of general cell body in control groups and experimental one were: the general osteoblast volume of experimental groups was bigger than that of the control one at the beginning 2days;as time on,the cell density of experimental groups was higher than that of the control one;the osteoblasts proliferation of experimental groups was more active than that of the control one during observing the fromazan shape kineticaly.The quantitae index I.e.cell growth index showed up the apparente difference after culturing 2days(P<0.01) and as time on the difference was displayed more obviously,the two growth curve assumed separating tendency as time on.There were more rough endoplasic reticulums,ribosomes and chondrosomes in experimental groups than that in control groups comparing their ultramicrostructure.It proves that bioglass can promote osteoblast to proliferate.