Preparation of Lignin-based Superplasticizer and Its Application in Mortar

魏民,易聪华,邓永红,杨东杰,邱学青
DOI: https://doi.org/10.3321/j.issn:0253-2417.2009.06.007
2009-01-01
Abstract:Lignosulfonate-modified sulfonated melamine formaldehyde resin (LSMF) has been synthesized as a superplasticizer used in mortar, and its effects on the performance of mortar have been systematically investigated. To obtain a new superplasticizer LSMF, lignosulfonates originated from wood, straw, bamboo and bagasse were selected to react with sulfonated melamine formaldehyde through a four-step reaction. The effects of LSMF on the performances of the superplasticized mortar were studied through measuring water-reducing ratio, compressive strength, flexural strength, and accelerated carbonation depth. The result shows that straw-based LSMF with sulfonic group content of 3.663 mmol/g and intrinsic viscosity of 7.24 mL/g has the best water-reducing and reinforcement effects. When LSMF is used in dosage of 0.7% by weight of cement, water-reducing ratio reaches 21.1%. Compared with that of the control mortar, compressive strength and flexural strength of the superplasticized mortar increase 37 % and 18 % at 28 d, respectively. The minimum carbonation depth of superplasticized mortar at 28 d is 13 mm, while that of the control mortar is 34.5 mm. This understanding can lead to push forward the utilization of lignin with high efficiency.
What problem does this paper attempt to address?