Abstract:The as-cast Ti44Al6Nb1.0Cr2.0V alloy master ingot was prepared by vacuum consumable melting technology. Some bars were cut from this ingot and they were directionally solidified by cold crucible under different pulling velocities. The samples could be well directionally solidified when the power (P) was 45kW and the pulling velocity (V) was 8.33μm/s or 11.67μm/s. The results show that the interlamellar space of the directionally solidified samples decreases from the average 1650nm of as-cast to less than 565nm and is more homogeneous. The microcrack in the master ingot can be eliminated completely and the room temperature (RT) tensile property is also improved after cold crucible directional solidification (CCDS). The ultimate tensile strength (UTS) is 602.5MPa and the elongation is 1.20% as P=45kW and V=11.67μm/s, compared with as-cast 499MPa of UTS and 0.53% of elongation. Trans-granular and trans-lamella fractures are predominant modes. The relationship between CCDS interlamellar space (d) and the pulling velocity can be described as d=1783.2V−0.554 and r12=0.972, where r12 is the corresponding regression coefficient. The CCDS interlamellar space and nanoindentation hardness (HN) in the lamella region can be described as HN=17.95d−0.145 and r22=0.986, and they are changed as HN′=14.03d′−0.104 and r32=0.975 when the cast condition is considered. The nanoindentation hardness of the B2 phase and the block γ phase are about 8.89GPa and 8.15GPa, respectively; both of them keep almost the same in different conditions.

Research on Composition Uniformity of TC4 Alloys During Electron Beam Cold Hearth Melting

Electron Beam Cold Hearth Melting of TC4

Temperature Field Simulation of Electron Beam Cold Hearth Melting TC4 Alloy

Heat Balance Analysis of Electron Beam Cold Hearth Melting of TC4 Alloy

Simulation study on temperature field and microstructure of Ti-6Al-4V alloy round ingot during EBCHM

Heat Balance Calculation of Electron Beam Cold Hearth Melting Process of TC4 Alloy

Investigations of microstructures and properties in electron beam welded joints of TiAl to TC4

High-throughput analysis of Al and Nb effects on mechanical behaviour of TiAl alloys using electromagnetic cold crucible continuous casting

Research on homogeneous nucleation and microstructure evolution of aluminium alloy melt

Calculation of Flow, Heat Transfer and Evaporation During the Electron Beam Cold Hearth Melting of Ti-6Al-4V Alloy

Improving element uniformity and mechanical properties of Al–Mg–Si alloy fabricated by twin roll casting with superheat melt treatment

Effect of Aging Treatment on Microstructural Evolution and Mechanical Properties of the Electron Beam Cold Hearth Melting Ti-6Al-4V Alloy

Influence of Aluminum Content on the Microstructure and Properties of Electron Beam Welded Joints of TiAl/TC4 Alloy

Study on Microstructure and Its Evolution of Electron Beam Welded TC4 Joint

MICROSTRUCTURE EVOLUTION OF Ti44Al6Nb ALLOY DIRECTIONALLY SOLIDIFIED WITH COLD CRUCIBLE

Microstructure Homogeneity and Mechanical Properties of Large-Size As-Cast High Nb Containing TiAl Alloy Ingot

Flow Field and Its Effect on Microstructure in Cold Crucible Directional Solidification of Nb Containing TiAl Alloy

Microstructure Control and Mechanical Properties of Ti44al6nb1.0cr2.0v Alloy by Cold Crucible Directional Solidification

3D ATOM PROBE CHARACTERIZATION OF ALLOYINGELEMENTS PARTITIONING IN CEMENTITE OF Nb-V MICROALLOYING STEEL

Electron Beam Welding of New Pattern Tial Intermetallic Light Alloy

Verification and Refinement of Local Difference in TC4 Hollow Blade Pressing with Low Melting Point Alloy Mandrel