Abstract:Tungsten oxide (WO3) nanoparticles with monoclinic structure have been synthesized by using an inexpensive coprecipitation process. The obtained nanoparticles were annealed at 400°C, 500°C, 600°C, 700°C, 800°C, and 900°C for 1 h under the same physical conditions. The morphology, structure, and optical properties of the synthesized nanoparticles were studied by x-ray diffraction (XRD) analysis, scanning electron microscopy (SEM), high-resolution transmission electron microscopy (HRTEM), ultraviolet–visible (UV–Vis) spectrophotometry, and Raman spectroscopy. The XRD results confirmed that the synthesized nanomaterial was crystalline in nature with monoclinic phase. The crystallite size varied from 14 nm to 87 nm when changing the annealing temperature. Williamson–Hall analysis was used to investigate the change in lattice strain and crystallite size. The optical performance was investigated by using UV–visible spectroscopy. The bandgap of the prepared nanomaterials varied from 2.51 eV to 3.77 eV with the annealing temperature, due to the variation of the effect of oxygen vacancies on the electronic band structure. SEM revealed formation of uniform and irregular-sized nanoparticles. HRTEM analysis revealed that the nanoparticles grew along the [002] plane with d-spacing of 0.39 nm for the material annealed at 500°C and along the [200] plane with spacing of 0.36 nm when annealed at 800°C. The crystalline nature of the synthesized nanomaterial was confirmed by uniform and clear fringes obtained in TEM micrographs. The correlation between the peak position and width of the key band at 806 cm−1 in Raman spectroscopy band is discussed. These enhancements in the properties of WO3 nanomaterial make it an efficient material for many potential applications, e.g., in photocatalysis, electro- and photochromic devices, etc.

Study of Preparation and Photochromic Properties of Monoclinic and Orthorhombic Tungsten Trioxide

Preparation of WO<sub>x</sub>-TiO<sub>2</sub> and the Photocatalytic Activity under Visible Irradiation

Synthesis and Photocatalytic Properties of Tungsten Trioxide Nanoflakes

Preparation and Photoelectrochemical Properties of Nano-Porous Tungsten Trioxide Films Electrode

Synthesis and Optical Properties of Single Crystal WO3 Nanoplates with Nano-Pits

Synthesis, Characterization And Photocatalytical Properties Of Oxygen-Deficient Tungsten Oxide Nano/Micro-Structures Prepared By Simple Thermal Evaporation

A Comparative Study of Microstructures on the Photoelectric Properties of Tungsten Trioxide Films with Plate-Like Arrays

Preparation and Characterization of Microporous Nano-Tungsten Trioxide and Its Photocatalytic Activity after Doping Rare Earth

Electrochromics of Nanocrystalline Tungsten Trioxide

Preparation, Characterization and Properties of Thermochromic Tungsten-Doped Vanadium Dioxide by Thermal Reduction and Annealing

Deep Eutectic Solvent Assisted Hydrothermal Synthesis of Photochromic and Nontoxic Tungsten Oxide Nanoparticles

Study on visible light photocatalytic performance of nano tungsten trioxide

WO3 Nanostructures Synthesized by a Sonochemical Strategy

Structure and Photocatalytic Activity of the Products Obtained by Thermal Treating Tungstic Acid

Preparation and Photocatalytic Activity of Dysprosium Doped Tungsten Trioxide Nanoparticles

Synthesis And Characterization Of Tungsten Oxide-Doped Titania Nanocrystallites

A Simple, Green Synthesis of Photochromic, Monoclinic Tungsten Oxide Fiber

Hydrothermal Synthesis and Photochromism Property of Superfine Powders of Metastable Tungsten Oxide

Effect of Annealing on the Surface Morphology, Optical and and Structural Properties of Nanodimensional Tungsten Oxide Prepared by Coprecipitation Technique

Photoelectrochemical Properties of Cubic Tungsten Trioxide Films Obtained by the Polymeric Precursor Method