In-Situ Polymerization And Characterization Of Poly (Epsilon -Caprolactone) Urethane/Sio2 Nanocomposites

Xiao-dong Chen,Nan-qiao Zhou,Hai Zhang

DOI: https://doi.org/10.1088/1742-6596/188/1/012025

2009-01-01

Abstract:Nanocomposites of poly(epsilon -caprolactone) (PCL) castable polyurethane elastomer (CPUE) with nano-SiO2 particles of different surface properties were prepared via in-situ polymerization. An electronmechanical universal testing machine, a durometer, a rubber resilience experimental machine, a dynamic-mechanical analyzer, a thermogravimetric analysis and a scanning electron microscope were used to investigate the macro -static/dynamic mechanical properties, micro-dispersed state and thermostability. The results showed that the modulus at 100% and 300%, elongation at break, tensile strength and tear strength of poly(epsilon -caprolactone) urethane nanocomposites were increased by introducing a certain amount of nano-SiO2. Especially the tensile strength and tear strength at 100 degrees C of the PCL CPUE with 5% nano-SiO2 pretreated by gamma-glycidochloropropyl methyl trimethoxy silane (trade name A-187) were 1.50 and 1.94 times than those of the pure PCL CPUE, respectively. The addition of the nano-SiO2 had little effect on the hardness, but the impact resilience decreased slightly. The loss factor peaks of two nano-SiO2 polyurethane composites were higher obviously than the pure PCL CPUE and the glass transition temperature (T-g) of the two nano-SiO2 polyurethane composites increased to higher temperature region. The surface treatment by the optimum silane coupling agent influenced the dispersibility of nano-SiO2 in the PCL CPUE distinctly. The agglomerating phenomenon, and even some nano-agglomerates with more than 1 mu m diameter can be observed in the PCL CPUE with 5% untreated nano-SiO2, but the nano-SiO2 pretreated by A-187 was dispersed in the PCL CPUE at nano-scale.