Effect of Sintering Time on the Performance of LiNixMn2-xO-coated LiCoO2

姚晓林,张承平,陈春华

DOI: https://doi.org/10.3969/j.issn.1003-5060.2008.05.015

2008-01-01

Abstract:The LiNixMn2-xO4 film was coated on the surface of LiCoO2 cathode material and sintered at 850 ℃ for 2 h,4 h,7 h and 10 h respectively.The effects of sintering time on the electrochemical behavior of LiCoO2 were discussed.The structures of the coated LiCoO2 were characterized by XRD and the electrochemical performance was tested after assembling these samples into Li-ion batteries.It could be seen from the results that sintering time affects the electrochemical performance of LiCoO2 to a certain extent.The surface modified LiCoO2 cathode material had increased actual specific capacity and stabilized cycling performance.The electrochemical measurements showed that the product obtained from sintering for 7 h has the best cycling behavior.The initial capacity of 3.5% LiNixMn2-xO4 coated LiCoO2 was 139.3 mA·h/g.The capacity amount of LiNixMn2-xO4 coated LiCoO2 after 120 cycles was 139.5 mA·h/g.The LiNixMn2-xO4 coated LiCoO2 has the excellent cycling performance and the capacity retention attains to almost 100% after 120 cycles.Moreover,it is found that the discharge capacity gradually increases with the increment of the cycle number,especially in the initial 10 cycles.The discharge capacity and plateau efficiency of 10% LiNixMn2-xO4 coated LiCoO2 were lower.