Behavior of Alloy Ti – 24% Al – 15% Nb – 1% Mo under Conditions of Low-Cycle Fatigue at High Temperatures

Bai Fang,Cao Jingxia,Li Peijie

DOI: https://doi.org/10.1007/s11041-010-9195-8

2009-01-01

Metal Science and Heat Treatment

Abstract:The low-cycle fatigue resistance of alloy Ti – 24% Al – 15% Nb – 1%Mo with structure consisting of primary α2 -phase, lamellar O-phase, and transformed β-phase is investigated.

What problem does this paper attempt to address?

Low cycle fatigue behavior of nickel-based superalloy GH4145/SQ at elevated temperature

Duyi Ye,Dehai Ping,Zhenlin Wang,Haohao Xu,Xiaoyu Mei,Changwei Xu,Xiaolin Chen

DOI: https://doi.org/10.1016/j.msea.2004.01.045

2004-01-01

Abstract:Low-cycle fatigue (LCF) behavior of nickel-based precipitation-strengthened superalloy GH4145/SQ was investigated systematically under fully reversed total strain amplitude control conditions at 538°C in laboratory air. It was shown that the alloy exhibited a pronounced initial fatigue hardening followed by continuous fatigue softening to failure at high strain amplitudes, while at low strain amplitudes the initial hardening was followed by a well-defined saturation stage. Microstructure observations using optical and transmission-electron microscopy revealed that slip band density increased with increasing total strain amplitudes and the size of the γ′precipitates tended to reduction due to repeated shearing by the dislocations with continuous cyclic straining. The above changes in microstructures during cycling were essentially responsible for the fatigue hardening–softening behavior of the alloy. Both optical and SEM micrographs indicated that at low strain amplitudes crack propagation was basically transgranular, while at high strain amplitudes crack propagation was essentially intergranular. Bilinear behavior with a change of slope at a plastic strain amplitude of about 0.2pct was observed in cyclic stress–strain (CSS), Coffin–Manson (C–M) and plastic strain energy–life plots. A change in the number of operating slip systems and the fracture modes with the strain amplitude employed was used to explain this two-slope characteristic. In both the companion specimens test (CST) and the incremental step test (IST) methods the alloy exhibited non-masing type behavior. It was suggested that, for the first approximation, the half-life plastic strain energy could be calculated directly according to the equation without reckoning in the non-masing behavior.
A Study of the Back Stress and the Friction Stress Behaviors of Ti-6Al-4V Alloy During Low Cycle Fatigue at Room Temperature

Haifeng Xu,Duyi Ye,Linbo Mei

DOI: https://doi.org/10.1016/j.msea.2017.06.051

IF: 6.044

2017-01-01

Materials Science and Engineering A

Abstract:Low cycle fatigue (LCF) tests were performed on Ti-6Al-4V alloy at room temperature. The fatigue hardening/softening of the Ti-alloy were determined. Both the back stress (X) and the friction stress (σF) were evaluated from analysis of fatigue hysteresis loops and their cycle-dependent behaviors during fatigue tests were obtained experimentally. It is shown that the cyclic stress response or the fatigue hardening/softening of the Ti-alloy actually results from the competition effect of the back and the friction stress behaviors during fatigue cycling. A two-slope behavior in both the εpa-2Nf and the X-2Nf plots was also obtained. The micro-mechanisms associated with the back and friction stress behaviors as well as the two-slope behavior in the εpa-2Nf and X-2Nf plots were further discussed with the help of OM and TEM observations of fatigue failure specimens at representative strain amplitudes. In this study, the DIC technique was also introduced to characterize quantitatively the cyclic deformation heterogeneity of the Ti-alloy at the grain scale.
Investigation on the Microstructure and Mechanical Behaviors of a Laser Formed Nb-Ti-Al Alloy

Zhiwu Shi,Jinlai Liu,Hua Wei,Hongyu Zhang,Xiaofeng Sun,Qi Zheng

DOI: https://doi.org/10.1016/j.matchar.2020.110193

IF: 4.537

2020-01-01

Materials Characterization

Abstract:Nb-Ti-Al alloys have attracted much attention as a potential candidate for high-temperature structural applications beyond the scope of Ni-based superalloys. Previously, Nb-Ti-Al alloys were prepared by arc-melting or hot-pressing. In this study, laser forming of the Nb-23Ti-15Al alloy is explored, and the microstructure and mechanical behaviors are systematically investigated. The results indicate that the nearly defectless Nb-Ti-Al alloy with fine dendrites could be obtained through laser forming. Three phases, β, δ and Ti(O,C), present in the alloy, and the β/δ matrix displays a columnar microstructure. Moreover, the Ti(O,C) phase, a solid-solution of TiO or TiC, appears in the alloy. Ti(O,C) is formed due to the introduction of the O and C from the elemental powder, which has a face-centered cubic (FCC) structure and a moderate lattice parameter between that of TiO and TiC. Two morphologies of Ti(O,C), large cobblestone-like particles and small dispersive particles, are observed in the alloy. Forbidden reflections of δ phase occur due to double diffraction and slight superlattice reflections of β phase arise. Furthermore, refined β/δ phases and dispersed small Ti(O,C) result in higher microhardness and fracture toughness. In brief, our results indicate that laser forming is a potential method for manufacturing Nb-Ti-Al alloys with prominent properties.
Thermal Stability and Lattice Strain Evolution of High‐Nb‐Containing TiAl Alloy under Low‐Cycle‐Fatigue Loading

Jie Ding,Shuntian Huang,Zhili Dong,Junpin Lin,Yang Ren,Xiaodong Wu,Hui Chang

DOI: https://doi.org/10.1002/adem.202001337

IF: 3.6

2021-06-23

Advanced Engineering Materials

Abstract:The micro‐mechanical behavior and the effect of temperature on micro‐mechanical mechanism of high Nb‐containing TiAl alloy during low cycle fatigue still remains uncertain. In‐situ and ex‐situ synchrotron‐based high energy X‐ray (HEXRD) experiment results revealed that γ and ωo phases suffer compressive lattice strains but lattice strain in α2 phase was evolved from tensile to compressive during low cycle fatigue at 900 °C. Besides, the three phases suffer compressive lattice strains during cooling to room temperature, which could result in larger compressive lattice strains in γ and ωo phases and the change of lattice strain state in α2 phase. The peak broadening results showed γ recrystallization was dominant in the interrupted low cycle fatigue samples while inhomogeneous deformation occurred in the failed low cycle fatigue samples. The performed synchrotron diffraction experiments offered a deeper insight into the phase transformations and micro‐mechanism of TiAl alloy during low cycle fatigue.This article is protected by copyright. All rights reserved.

materials science, multidisciplinary
Cyclic Deformation and Lattice Strain Distribution of High Nb Containing TiAl Alloy

Jie Ding,Shan Shi,Zhili Dong,Junpin Lin,Yang Ren,Xiaodong Wu,Hui Chang,Lian Zhou

DOI: https://doi.org/10.1080/02670836.2020.1795994

IF: 1.8

2020-01-01

Materials Science and Technology

Abstract:Low cycle fatigue of lamellar TiAl with 8.5 at.-%Nb was studied with a total strain amplitude of 0.28% at three temperatures: room temperature, 750°C and 900°C. At room temperature, the material exhibited cyclic hardening and the fracture mode was mainly interlamellar. At 750°C and 900°C, the material showed cyclic softening and the fracture mode was translamellar. The lattice strain in γ phase was almost tensile and larger tensile lattice strain in γ phase seems detrimental. Besides, the opposite direction of {201}γ and {100}α2 lead to crack propagation along α2/γ interfaces. B2/βo phase always suffered compressive lattice strain in the tests. The destruction of lamellar microstructure was the reason for colony refinement at 750°C and 900°C.
Influence of α-Phase Morphology on Mechanical Characteristics, Cycle Oxidation, and Hot Corrosion Behavior of Ti-6Al-3Mo-2Nb-2Zr-2Sn-1.5Cr Alloy

Fathy S. Ahmed,Mohamed A. El-Zomor,Magdy S. Abo Ghazala,Ramadan N. Elshaer

DOI: https://doi.org/10.1007/s13632-022-00884-5

2022-09-01

Metallography, Microstructure, and Analysis

Abstract:The influence of α-phase morphology (equiaxed and lamellar) on the mechanical characteristics, cycle oxidation, and hot corrosion behavior of Ti-6Al-3Mo-2Nb-2Zr-2Sn-1.5Cr (TC21) alloy was investigated. The morphology and distribution of microstructure constituents were characterized by optical microscopy and scanning electron microscopy, while constituent compositions were determined with energy-dispersive spectroscopy. The phases in the oxide scale and corrosion products after different treatments were identified by XRD technique. The initial microstructure consists of equiaxed α-phase and intergranular β-grains. However, after heat treatment, the microstructure changed to lamellar, consisting of large grains of β-phase containing colonies of different orientations. The results showed that the microstructure change from equiaxed to lamellar has a small enhancement on microhardness and wear rate. Surface characterization demonstrates that the β-phase is more resistant to corrosion than the α-phase owing to a higher concentration of Nb, Mo, and Zr. Adhered, compact and thin oxide film was formed and grew in thickness with time during cycle oxidation at 600 °C for 50 h. The weight gain of samples with equiaxed and lamellar microstructures after oxidation was 0.3 and 0.28 mg/cm 2 , respectively, where the variation of weight change was tiny. After NaCl hot corrosion test, the weight loss of samples with equiaxed and lamellar microstructures was 13.2 and 6.4 mg/cm 2 . However, the weight change after hot corrosion with a mixture of NaCl + Na 2 SO 4 salts was − 0.88 and 0.07 mg/cm 2 , respectively. The main corrosion products were rutile TiO 2 , Na 4 O 12 Ti 5 , NaTiS 2 , and Ti 6 O, as well as a small amount of NaCl, as identified by XRD on the corroded surfaces depending on the sprayed salt type.
Hot Deformation Behavior of a Novel Near-β Titanium Alloy Ti-5.5Mo-6V-7Cr-4Al-2Sn-1Fe in (α+β) Phase Region

Jinyang Gai,Jun Cheng,Jinshan Li,Zhaoxin Du,Wen Zhang,Sen Yu,Zhentao Yu

DOI: https://doi.org/10.3389/fmats.2019.00343

2020-01-14

Frontiers in Materials

Abstract:The hot deformation behavior of a novel near-beta titanium alloy Ti-5.5Mo-6V-7Cr-4Al-2Sn-1Fe in (α+β) phase region in the temperature of 605~755°C and strain rate range of 10−3~10−1/s−1 was investigated on the Gleeble-3800 thermo-mechanical simulator. The results showed that the deformation parameters can have a significant influence on flow softening behavior and the microstructure evolution, as well as dynamic recrystallization is remarkable at temperature 755°C and strain rate 10−3s−1. The flow stress decreases with the increase of temperature and decrease of strain rate. With the rise of temperature and strain rate, the content of α phase gradually decreases. During the thermal deformation process, the α phase content decreases with the increase of the strain rate and the size of α phase decreases with increasing temperature. αGB is short rod or spherical. And α phase precipitated after short-term aging preferentially nucleated within the grains after aging treatment. Moreover, the thermal-mechanical process does not induce α phase generation compared to general heat treatment.

materials science, multidisciplinary
Mechanical Properties and Oxidation Characteristics of TiNiAl(Nb) Intermetallics

H. B. Xu,L. J. Meng,J. Xu,Y. Li,X. Q. Zhao

DOI: https://doi.org/10.1016/j.intermet.2006.10.005

IF: 4.075

2007-01-01

Intermetallics

Abstract:The structural evolution, mechanical properties and the oxidation characteristics of Ti50Ni50−xAlx alloys were investigated. The influence of additive Nb on the microstructure, mechanical properties as well as the high temperature oxidation resistance was examined. It is found that the substitution of Al for Ni can remarkably reinforce the TiNi-based intermetallics by precipitation of (Ti,Al)2Ni phase and by solid-solution strengthening effects. It is also found that the addition of Nb has beneficial influence on the mechanical properties of TiNiAl intermetallics, and that the oxidation resistance of TiNiAl(Nb) alloys can be effectively improved by the Nb addition. The effect of Nb on the high temperature oxidation behavior of TiNiAl(Nb) alloys has been discussed.
Low-Cycle Fatigue Behavior and Fracture Characteristics of Low-Cost Ti-2Fe-0.1B Alloy

Chu Wang,Yangyang Sun,Yaoyao Mi,Yuecheng Dong,Hui Chang,I. V. Alexandrov

DOI: https://doi.org/10.3390/met13071208

IF: 2.695

2023-06-29

Metals

Abstract:In recent decades, the effect of Fe element addition on titanium alloy has been investigated extensively due to the development of low-cost titanium alloys, as well as B microalloying, which could decrease the grain size of titanium alloys during the casting process. As a key structural material, the study of the fatigue behavior of titanium alloys is crucial and always attractive for scientists. Hence, in this paper, the low cycle fatigue (LCF) behavior and fracture characteristics of a low-cost Ti-2Fe-0.1B alloy with a lamellar structure were investigated systematically, five different strain amplitudes (Δεt/2) in the range from 0.6% to 1.4% were selected to control the LCF process. It was found that the Ti-2Fe-0.1B alloy exhibits continuous cyclic softening behavior in the cycle as a whole at Δεt/2 ≤ 1.2%, while at Δεt/2 = 1.4%, it exhibits slight cyclic hardening at the initial stage of the cycle, then shows cyclic softening. Compared with pure titanium and other typical titanium alloys, the Ti-2Fe-0.1B alloy indicated maximum fatigue life under the same strain amplitude, it can be attributed to the fine grain size result from the effect of Fe element and trace B, which could hinder the dislocation movement and crack propagation.

materials science, multidisciplinary,metallurgy & metallurgical engineering
Cyclic deformation response and strain-induced martensitic transformation of β single phase Ti-35421 alloy

Yangyang Sun,Kai Chen,I.V. Alexandrov,Hang Zhang,Liang Feng,Jie Ding,Yuecheng Dong,Hui Chang,Lian Zhou

DOI: https://doi.org/10.1016/j.ijfatigue.2022.107497

IF: 5.489

2023-01-01

International Journal of Fatigue

Abstract:Compared with bimodal microstructure, the low-cycle fatigue (LCF) behavior and cyclic deformation mechanism of a near β Ti-3Al-5Mo-4Cr-2Zr-1Fe (Ti-35421) alloy with single β were systematically investigated. Lower strength, but higher ductility and longer LCF life were found for Single β. The nanoscale α" martensite was detected in Single β by selected area electron diffraction pattern. Besides, slips and strain induced martensitic transformation played the major deformation mechanisms in Single β. Moreover, the existence of α" contributed to the limit of microcracks nucleation in Single β, which resulted in a better fatigue life.

materials science, multidisciplinary,engineering, mechanical
Improved Thermo-Mechanical Fatigue Resistance of Al-Si-Cu 319 Alloys by Microalloying with Mo

Kun Liu,Shuai Wang,Peng Hu,Lei Pan,X.-Grant Chen

DOI: https://doi.org/10.3390/ma16093515

IF: 3.4

2023-05-04

Materials

Abstract:Thermo-mechanical fatigue (TMF) is one of the most detrimental failures of critical engine components and greatly limits their service life. In this study, the out-of-phase TMF (OP-TMF) behavior in Al-Si-Cu 319 cast alloys microalloyed with Mo was systematically investigated under various strain amplitudes ranging from 0.1–0.6% and temperature cycling at 60–300 °C and compared with the base 319 alloy free of Mo. Cyclic stress softening occurred in both experimental alloys when applying the TMF loading, resulting from the coarsening of θ'-Al2Cu precipitates. However, the softening rate of the Mo-containing alloy was lower than that of the base 319 alloy because of its lower θ'-Al2Cu precipitate coarsening rate per cycle. The Mo-containing alloy exhibited a longer TMF lifetime than the base alloy at the same strain amplitude. Microalloying 319 alloy with Mo enhanced the TMF resistance mainly by slowing the coarsening of θ'-Al2Cu precipitates and providing supplementary strengthening from thermally stable Mo-containing α-dispersoids distributed in the Al matrix. The energy-based model was successfully applied for predicting the TMF lifetime with a low life predictor factor, which agreed well with the experimentally measured fatigue cycles.

materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,metallurgy & metallurgical engineering
Fatigue Crack Growth Behavior of Beta-Annealed Ti–6Al–2Sn–4Zr–xMo (x = 2, 4 and 6) Alloys: Influence of Microstructure and Stress Ratio

Jianke Qiu,Xin Feng,Yingjie Ma,Jiafeng Lei,Yuyin Liu,Aijun Huang,David Rugg,Rui Yang

DOI: https://doi.org/10.1016/j.ijfatigue.2015.10.009

IF: 5.489

2015-01-01

International Journal of Fatigue

Abstract:The influence of microstructures (β grain size, α/β colony size and width of α lath) and stress ratios (R=0.1, 0.7) on fatigue crack growth (FCG) behavior of beta-annealed Ti624x (x=2, 4 and 6) alloys was investigated. The FCG rate curves, crack paths, and the plastic zone ahead of the crack tip were compared. The reducing FCG resistance from Ti6242 to Ti6246 was found to stem from decreasing α/β colony size. Increasing stress ratio also reduced crack deflection and crack closure, and thus decreased the FCG resistance. The relevant mechanisms were discussed in terms of Kmax and crack closure effect.
Effects of Aging Treatment on Microstructure Evolution and Mechanical Properties of Ti-6Al-3Nb-2Zr-Mo Alloy

Jiang Haiyang,Jiang Fuqing,Wang Bing,Xu Bin,Sun Mingyuel

2023-01-01

Rare Metal Materials and Engineering

Abstract:In order to understand the influence of the different aging parameters on the microstructure and mechanical properties of Ti6Al-3Nb-2Zr-Mo (Ti6321) alloy, the microstructures and mechanical properties under different aging parameters (temperatures ranging from 500 degrees C to 650 degrees C, 3 - 24 h) were investigated by optical microscopy (OM), scanning electron microscopy (SEM), transmission electron microscopy (TEM), and mechanical properties tests. The results reveal that the secondary alpha phase (alpha(s)) is more sensitive to the aging parameters than the primary alpha phase (alpha(p)). Moreover, the thickness of alpha(s) phase is positively correlated with aging temperature or aging time. As the aging temperature and aging time increase, the segregation of Ti and Al elements in the beta transformation phase (beta(t)) becomes obvious, and the alpha(s) phase changes from fine needle-like to long rod-like. When the alloy is aged at 600 degrees C for 12 h, the alloy shows good comprehensive mechanical performance. The tensile strength, yield strength, and elongation are 907 MPa, 796 MPa, and 16%, respectively, and the impact energy is 55 J.
Microstructural evolution and high-temperature oxidation mechanisms of a titanium aluminide based alloy

S.J. Qu,S.Q. Tang,A.H. Feng,C. Feng,J. Shen,D.L. Chen

DOI: https://doi.org/10.1016/j.actamat.2018.02.013

IF: 9.4

2018-04-01

Acta Materialia

Abstract:Oxidation resistance of titanium aluminide (TiAl) based alloys is a fundamental aspect for the high-temperature structural applications such as in the advanced hypersonic aircraft engines and gas turbines. The aim of this study was to identify oxidation kinetics and mechanisms through detailed microstructural characterization of a newly-developed Ti-44Al-4Nb-1.5Cr-0.5Mo-0.1B-0.1Y alloy via focused ion beam (FIB), transmission electron microscopy (TEM), X-ray diffraction (XRD), electron probe microanalysis (EPMA), scanning transmission electron microscopy (STEM), along with density functional theory (DFT) calculations. The alloy consisting mainly of γ-TiAl/α2-Ti3Al lamellar structure exhibited a superior oxidation resistance at 700 °C, and followed parabolic oxidation kinetics at 800 °C and 900 °C. The observed multi-layered scale structure consisted of TiO2, Al2O3-rich, Al2O3+TiO2, H-Ti2AlN+Al2O3+α2-Ti3Al, Z-Ti5Al3O2+AlNb2+Laves-(Ti,Nb)Cr2, and H-Ti2AlN/α2-Ti3Al lamellae from the outside to inside after high-temperature oxidation. The γ-TiAl/α2-Ti3Al lamellae near the scale/substrate interface were first transformed into H-Ti2AlN/α2-Ti3Al lamellae, with orientation relationships identified as ( 0001 ) α 2 / / ( 0001 ) T i 2 A l N , ( 10 1 ¯ 0 ) α 2 / / ( 10 1 ¯ 0 ) T i 2 A l N and [ 1 2 ¯ 10 ] α 2 / / [ 1 2 ¯ 10 ] T i 2 A l N . The H-Ti2AlN/α2-Ti3Al lamellae were then transformed into a metastable Z-Ti5Al3O2 phase at the scale/substrate interface. The Z-phase was decomposed to Ti3Al and Al2O3 as the scale/substrate interface moved inwardly. Ti3Al reacted further with oxygen and nitrogen to form Ti2AlN, which was finally oxidized to form TiO2 and α-Al2O3. A Nb-rich layer was present beneath the scale along with the formation of AlNb2 and Laves phase, and the doping effect of Nb to suppress the diffusion of oxygen occurred mainly in the TiO2+Al2O3 compound layer. The results obtained in this study would pave the way for the development of advanced oxidation-resistant TiAl-based materials for high-temperature applications.

materials science, multidisciplinary,metallurgy & metallurgical engineering
High-temperature, low-cycle fatigue behavior of an Al-Mg-Si based heat-resistant aluminum alloy

Kyu-Sik Kim,Si-Young Sung,Bum-Suck Han,Joong-Cheol Park,Kee-Ahn Lee

DOI: https://doi.org/10.1007/s12540-015-5225-9

IF: 3.451

2015-11-01

Metals and Materials International

Abstract:High-temperature, low-cycle fatigue behavior of the new heat-resistant aluminum alloy was investigated in this study. The aluminum alloy consists of aluminum matrix and small amount of precipitated Mg2Si and (Co, Ni)3Al4 strengthening particles. At room temperature and 523 K, the yield and tensile strengths of Al-Mg-Si-(Co, Ni) the aluminum alloy were maintained with no significant decrease, and elongation increased slightly. Low-cycle fatigue tests controlled by total strain were performed with strain ratio (R) = −1, strain rate = 2×10-3 s-1 at 523 K. The fatigue limit of the low-cycle fatigue of this alloy showed plastic strain amplitude (Δεpa) of 0.22% at 103 cycles. This value was superior to that of conventional aluminum alloy such as A319. The results of the fractographical observation showed that second phases, especially (Co, Ni)3Al4 particles, affected fatigue behavior. This study also attempted to clarify the mechanism of high-temperature, low-cycle fatigue deformation of Al-Mg-Si-(Co, Ni) alloy in relation to its microstructure and energy dissipation analysis.

materials science, multidisciplinary,metallurgy & metallurgical engineering
Fatigue Failure Analyses On A Ti-45al-8nb-0.2w-0.2b-0.1y Alloy At Different Temperatures

Xi-Shu Wang,Min Zhang,Xi-Ping Song,Su Jia,Qiang Chen,Norio Kawagoishi

DOI: https://doi.org/10.3390/ma5112280

IF: 3.4

2012-01-01

Materials

Abstract:The fatigue micro crack initiation and propagation tests of a TiAl alloy with 8% Nb content were carried out by using scanning electron microscopy in situ technology at room temperature and at 750 degrees C. These results indicated that the fatigue micro crack initiation was mainly caused by the stress concentration at room temperature, but at an elevated temperature (750 degrees C) the multi-cracks were caused by the coupled factors of both lamellar microstructure and stress concentration. Therefore, fatigue micro crack initiation behavior is much more dependent on the lamellar structure at an elevated temperature. One of the reasons is that the elevated temperature degrades the interface strength between the lamellar of the TiAl alloy with 8% Nb content. Therefore, the small fatigue crack propagation behavior of the alloy exhibited a mixture damage model of interlamellar and translamellar at a micro scale. The crack growth path and fracture characteristics provided a proof of crack deflection, branching and/or bridging induced either by interlamellar or by translamellar failure mode.
Thermal Cycling Behavior of Aged FeNiCoAlTiNb Cold-Rolled Shape Memory Alloys

Li-Wei Tseng,Wei-Cheng Chen

DOI: https://doi.org/10.3390/mi15111338

IF: 3.4

2024-11-01

Micromachines

Abstract:Fe–Ni–Co–Al-based systems have attracted a lot of interest due to their large recoverable strain. In this study, the microstructure and thermal cycling behaviors of Fe41Ni28Co17Al11.5Ti1.25Nb1.25 (at.%) 98.5% cold-rolled alloys after annealing treatment at 1277 °C for 1 h, followed by aging for 48 h at 600 °C, were investigated. From the electron backscatter diffraction results, we see that the texture intensity increased from 9.4 to 16.5 mud and the average grain size increased from 300 to 400 μm as the annealing time increased from 0.5 h to 1 h. The hardness results for different aging heat treatment conditions show the maximum value was reached for samples aged at 600 °C for 48 h (peak aging condition). The orientation distribution functions (ODFs) displayed by Goss, brass, and copper were the main textural features in the FeNiCoAlTiNb cold-rolled alloy. After annealing, strong Goss and brass textures were formed. The transmission electron microscopy (TEM) results show that the precipitate size was ~10 nm. The X-ray diffraction (XRD) results show a strong peak in the (111) and (200) planes of the austenite (⁠⁠γ, FCC) structure for the annealed sample. After aging, a new peak in the (111) plane of the precipitate (⁠⁠γ′, L12) structure emerged, and the peak intensity of austenite (⁠⁠γ, FCC) decreased. The magnetization–temperature curves of the aged sample show that both the magnetization and transformation temperature increased with the increasing magnetic fields. The shape memory properties show a fully recoverable strain of up to 2% at 400 MPa stress produced in the three-point bending test. However, the experimental recoverable strain values were lower than the theoretical values, possibly due to the fact that the volume fraction of the low-angle grain boundary (LABs) was small compared to the reported values (60%), and it was insufficient to suppress the beta phases. The beta phases made the grain boundaries brittle and deteriorated the ductility. On the fracture surface of samples after the three-point bending test, the fracture spread along the grain boundary, and the cross-section microstructural results show that the faces of the grain boundary were smooth, indicating that the grain boundary was brittle with an intergranular fracture.

chemistry, analytical,nanoscience & nanotechnology,instruments & instrumentation,physics, applied
High-Temperature Rheological Behavior and Microstructure Evolution of Mo-12Si-8.5B Alloy Reinforced by Layered Mo2TiAlC2 Phase

Xiaohui Lin,Guojun Zhang,Wen Zhang,Yanchao Li,Bin Li,Boyan Wang

DOI: https://doi.org/10.1007/s11837-023-06022-y

2023-08-17

JOM

Abstract:The rheological behavior of Mo-12Si-8.5B alloy reinforced by a layered Mo 2 TiAlC 2 phase has been studied at temperatures ranging from 1200°C to 1400°C and strain rates ranging from 0.01 s −1 to 0.0001 s −1 . The flow stress and microstructure evolution were investigated and the constitutive model was established. The results indicated that the Mo 2 TiAlC 2 strengthens the Mo-12Si-8.5B alloy mainly by particle strengthening and grain boundary strengthening at high temperatures. With the increase of Mo 2 TiAlC 2 content, the peak stress of the alloys improved. As the temperature increases or the strain rate decreases, the peak stress of the alloys decreases significantly. The microstructure reveals that the deformation of the Mo-12Si-8.5B-Mo 2 TiAlC 2 alloy at high temperatures is mainly provided by the deformation of the α -Mo phase and grain boundary sliding. As the temperature rises to 1300–1400°C, the intermetallic phase gradually participates in the deforming but contributes less to the total deformation. Dynamic recovery and recrystallization greatly reduce dislocations at high temperatures. The Mo 2 TiAlC 2 particles can inhibit recrystallization grain growth. In addition, the flow stress values of the Mo-12Si-8.5B-2 wt.% Mo 2 TiAlC 2 alloy calculated by the constitutive model are in good agreement with the experimental values. Hence, it is reasonable to believe that the constitutive model can effectively predict the rheological behavior of alloys at high temperatures.

materials science, multidisciplinary,metallurgy & metallurgical engineering,mining & mineral processing,mineralogy
Microstructure stability and damage mechanisms in an α/β Ti-6Al-4V-0.55Fe alloy during low cycle dwell-fatigue at room temperature

Shan Shi,Qinghua Deng,Hang Zhang,Liang Feng,Xiangjun Xu,Jie Ding,Hui Chang,Lian Zhou

DOI: https://doi.org/10.1016/j.ijfatigue.2021.106585

IF: 5.489

2022-02-01

International Journal of Fatigue

Abstract:The cyclic behavior and microstructure evolution of Ti-6Al-4V-0.55Fe alloy were investigated with three different total strain amplitudes. A slight softening was occurred with Δεt/2=1.20%, and the alloy mainly suffered α recrystallization. Besides, a gentle softening can be observed with Δεt/2=1.60%, which led to more substructure deformation. Furthermore, a sudden drop of the stress amplitude was occurred with Δεt/2=4.00% which resulted in more plastic deformation. The phase transformation and α recrystallization were observed. Cracks were propagated along the α grain boundaries and the α/β lamellar interfaces due to the concentrated dislocations at the α/β lamellar interfaces.

materials science, multidisciplinary,engineering, mechanical
The role of the ω phase on the microstructure evolution of precipitation and mechanical property in Ti-3Al-5Mo-4Cr-2Zr-1Fe

Feng Li,Jingqi Zhang,Bohan Zhang,Bing Lu,Jie Ding,Liang Feng,Hui Chang

DOI: https://doi.org/10.1016/j.jmrt.2023.05.129

IF: 6.267

2023-05-20

Journal of Materials Research and Technology

Abstract:This study investigates the effect of the ω phase on the microstructure evolution and mechanical properties of the Ti-3Al-5Mo-4Cr-2Zr-1Fe (Ti-35421) near β titanium alloy. The study employed a solution treatment at 850°C followed by two aging treatments, namely, Double Aging (DA) and Isothermal Annealing (IA). The results show that the DA alloy had finer precipitation and fewer Precipitation-Free Zones (PFZs) than the IA alloy. While the Ultimate Tensile Strength (UTS) of the DA alloy was higher (1376 MPa) than that of the IA alloy (1272 MPa), its plasticity was lower. On the other hand, the IA alloy exhibited a better balance between UTS (1272 MPa) and ductility (8.12%). The nucleation mechanism of DA was attributed to the presence of the α stable element Al, which diffused in the microstructure and aggregated in the ω phase, creating favorable nucleation sites for the precipitation of the secondary α phase during low temperature aging. As a result, the PFZs decreased, and the dispersion distribution strengthened the β matrix structure. Conversely, the high aging temperature during IA made it difficult to form the ω phase, resulting in coarser precipitation and increased PFZs as the temperature increased. This paper revealed the influence of ω on the relative precipitation during the phase transition, the microstructure and properties of the Ti-3Al-5Mo-4Cr-2Zr-1Fe, providing valuable insights for optimizing its heat treatment process.

materials science, multidisciplinary,metallurgy & metallurgical engineering

Behavior of Alloy Ti – 24% Al – 15% Nb – 1% Mo under Conditions of Low-Cycle Fatigue at High Temperatures

Low cycle fatigue behavior of nickel-based superalloy GH4145/SQ at elevated temperature

A Study of the Back Stress and the Friction Stress Behaviors of Ti-6Al-4V Alloy During Low Cycle Fatigue at Room Temperature

Investigation on the Microstructure and Mechanical Behaviors of a Laser Formed Nb-Ti-Al Alloy

Thermal Stability and Lattice Strain Evolution of High‐Nb‐Containing TiAl Alloy under Low‐Cycle‐Fatigue Loading

Cyclic Deformation and Lattice Strain Distribution of High Nb Containing TiAl Alloy

Influence of α-Phase Morphology on Mechanical Characteristics, Cycle Oxidation, and Hot Corrosion Behavior of Ti-6Al-3Mo-2Nb-2Zr-2Sn-1.5Cr Alloy

Hot Deformation Behavior of a Novel Near-β Titanium Alloy Ti-5.5Mo-6V-7Cr-4Al-2Sn-1Fe in (α+β) Phase Region

Mechanical Properties and Oxidation Characteristics of TiNiAl(Nb) Intermetallics

Low-Cycle Fatigue Behavior and Fracture Characteristics of Low-Cost Ti-2Fe-0.1B Alloy

Cyclic deformation response and strain-induced martensitic transformation of β single phase Ti-35421 alloy

Improved Thermo-Mechanical Fatigue Resistance of Al-Si-Cu 319 Alloys by Microalloying with Mo

Fatigue Crack Growth Behavior of Beta-Annealed Ti–6Al–2Sn–4Zr–xMo (x = 2, 4 and 6) Alloys: Influence of Microstructure and Stress Ratio

Effects of Aging Treatment on Microstructure Evolution and Mechanical Properties of Ti-6Al-3Nb-2Zr-Mo Alloy

Microstructural evolution and high-temperature oxidation mechanisms of a titanium aluminide based alloy

High-temperature, low-cycle fatigue behavior of an Al-Mg-Si based heat-resistant aluminum alloy

Fatigue Failure Analyses On A Ti-45al-8nb-0.2w-0.2b-0.1y Alloy At Different Temperatures

Thermal Cycling Behavior of Aged FeNiCoAlTiNb Cold-Rolled Shape Memory Alloys

High-Temperature Rheological Behavior and Microstructure Evolution of Mo-12Si-8.5B Alloy Reinforced by Layered Mo2TiAlC2 Phase

Microstructure stability and damage mechanisms in an α/β Ti-6Al-4V-0.55Fe alloy during low cycle dwell-fatigue at room temperature

The role of the ω phase on the microstructure evolution of precipitation and mechanical property in Ti-3Al-5Mo-4Cr-2Zr-1Fe