Abstract:Fe3O4 magnetic nanocrystals were prepared by coprecipitating Fe2+ and Fe3+ ions in an ammonia solution with ultrasonic enhancement and modification by the anionic surfactant sodium dodecyl sulfate (SDS). The product was characterized by X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FT-IR), high resolution transmission electron microscopy (HRTEM), N2 absorption-desorption, and thermogravimetric-differential scanning calorimetry (TG-DSC), respectively. The surface electrical properties and magnetic properties of the Fe3O4 magnetic nanocrystals were systematically investigated. The growth mechanism of the Fe3O4 magnetic nanocrystals was discussed. The results show that the Fe3O4 magnetic nanoparticles obtained are well-crystallized particles, with an average size of 10 nm, which have good dispersivity. The specific surface area of particles can reach as much as 91.6 m2 · g-1. The obtained nanoparticles also have good thermostability, and the isoelectric point (IEP) under water conditions is at pHpzc=5.7. Magnetic measurement reveals the magnetic nanoparticles are superparamagnetic with a saturation magnetization of 65.0 emu · g-1. The ultrasonic enhancement and the surfactant modification play an important role in the growth mechanism of the Fe3O4 superparamagnetic nanocrystals. These superparamagnetic nanocrystals might be applied to biological and medical fields such as cell or enzyme immobilization.

Study on Preparation of Magnetic Fe3O4 Nano-Particle with Double Micro-Emulsion

Study on Preparation of Nano- Fe3O4 by Microemulsion Method

Microemulsion Synthesis and Characterization of Nano-Fe3O4Particles and Fe3O4Nanocrystalline

Polyol Synthesis of Superparamagnetic Fe_3O_4 Nanoparticles for Magnetic Resonance Imaging

Preparation and Characterization of Magnetic Nanoparticles of Fe-3 O-4 Coated with Mesoporous Sio2

Fabrication and Characterization of Organic-based Fe_3O_4 Magnetic Fluid

Preparation and surface modification of magnetic nano-Fe_3O_4

Preparation and Application of Magnetic Fe3O4 Nano-Crystalline

Preparation and Magnetic Properties of Magnetic Magnetite Nano Particles

Preparation and Surface Modification of Magnetic Fe3O4 Nanoparticles

Preparation of magnetic nanometer Fe3O4 with the method of complex compound-hydrolyzation deposition

Preparation and Characterization of the Novel Magnetic Nano-Sized Ferrite(Fe_3O_4) Particles Modified by C_(16)H_(33)NaO_2

Selection of Preparation Conditions of Fe3O4 Magnetic Nanoparticles Based on Orthogonal Method

Preparation and Characterization of Nano-size Fe3O4 Particles with Strong Magnetism

Preparation of nano-Fe304 particles with microemulsion method

Study on Preparation of Fe3O4Particles by Electromagnetic Wave Auxiliary

Synthesis of Fe3O4 Nanoparticles and Preparation of Magnetic Fluids

Orthogonal experimental study and properties on nanometer Fe3O4 prepared by co-precipitation method

Preparation and Property of Nano-Porous Fe3O4/SiO2 Composited Magnetic Microspheres by Supercritical Technique

Preparation of Fe3O4 superparamagnetic nanocrystals by coprecipitation with ultrasonic enhancement and their characterization

Preparation and Property Characterization of Fe3O4 Magnetic Nanoparticles