High-temperature phase transition and magnetic property of LaFe11.6Si1.4 compound
Xiang Chen,Yungui Chen,Yongbai Tang
DOI: https://doi.org/10.1016/j.jallcom.2011.05.054
IF: 6.2
2011-01-01
Journal of Alloys and Compounds
Abstract:The LaFe 11.6 Si 1.4 compounds are prepared by arc-melting and then annealed at different high temperatures from 1323 K(5 h) to 1623 K(2 h). The powder X-ray diffraction and metallographic microscopy show that 1423 K and 1523 K are two curial temperatures, at which large amount of 1:13 phase begins to form and the most amount of 1:13 phase is obtained, respectively. With annealing temperature increasing to 1573 K and 1623 K, a new phase of La 5 Si 3 is detected in LaFe 11.6 Si 1.4 compound. According to the DSC curve of as-cast LaFe 11.6 Si 1.4 compound and the X-ray patterns of annealed LaFe 11.6 Si 1.4 compounds, the high-temperature phase transition process is analyzed. For studying the influence of different high-temperature and short-time annealing on magnetic property, the Curie temperature, thermal and magnetic hysteresis, magnetocaloric effect of LaFe 11.6 Si 1.4 compound annealed at different temperatures are also investigated. Keywords LaFe11.6Si1.4 compound High-temperature and short-time annealing Phase transition Magnetic property 1 Introduction LaFe 13− x Si x compounds with 1.1 ≤ x ≤ 1.6 are enjoying interest in the magnetic materials community due to the observation of a large MCE in LaFe 11.4 Si 1.6 compound [1] . Those compounds undergo a first-order magnetic transition at T C about 200 K, and an itinerant-electron metamagnetic (IEM) transition just above T C [2,3] , which result in a large magnetocaloric effect (MCE). Because of the low price of starting materials and excluding deleterious elements, LaFe 13− x Si x compounds are the hot research points in magnetic refrigerant materials field for long time [4–9] . Recently, the main studies about LaFe 13− x Si x compounds focused on how to enhance T C , improve magnetocaloric properties, reduce the large thermal and magnetic hysteresis, and improve the corrosion resistant property. Researches found that the T C can adjust according to the hydrogen content in LaFe 13− x Si x hydrides while the large magnetic entropy change is retained, and both thermal and magnetic hysteresis are remarkably reduced because of the weakness of the itinerant-electron metamagnetic transition after hydrogenation [10–12] . The doping of B as interstitial can help to form 1:13 phase in as-cast LaFe 13− x Si x B y compounds accompanied Fe 2 B phase appearance [13] , and the thermal and magnetic hysteresis of LaFe 13− x Si x B y compounds is less than that of mother alloy [14–16] . But the Fe 2 B phase cannot be eliminated after the as-cast LaFe 13− x Si x B y compounds being annealed and the magnetocaloric effect decrease. The corrosion behavior and inhibition corrosion of La(Fe 0.94 Co 0.06 ) 11.7 Si 1.3 compound and LaFe 11.6 Si 1.4 in different solutions have been investigated [17–19] . The result shows that these alkaline solutions is necessary to ensure that a protection film can be formed on the surface of metal and have a good inhibition effect on the LaFe 13− x Si x compounds in a certain. Although the La(Fe 1− x Co x ) 11.9 Si 1.1 compounds with 0.055 < x < 0.122 produced by powder metallurgy, La(Fe0 .745 Co 0.17 Si 0.085 ) 13 ribbons prepared by melt spinning and annealed for a shorter time, and the LaFe 13– x Si x ( x = 1.4, 1.6, 1.8, 2.0) series synthesized by high energy ball-milling have been investigated [20–22] , most of LaFe 13− x Si x compounds with NaZn13-type structure (hereinafter 1:13 phase) are prepared by long time annealing for several weeks at between 1173 K and 1373 K, and then quenching rapidly in medium. In the LaFe 13− x Si x compounds, 1:13 phase is hard to be obtained directly from common solidification process due to the intrinsic incompleteness of a peritectic reaction: γ-Fe + L → La(Fe,Si)13( τ 1a ), which often results in the mixed microstructure of α-Fe + La(Fe,Si)13( τ 1a ) + LaFeSi( τ 4 ) [23] . For shorting the annealing time, some researchers used melt-spun or rapid quenching/short-time annealing at about 1273 K to prepare 1:13 phase [24–26] . Compared with the arc-melting/long time annealing, the annealing time reduces to a few minutes or a few hours, but the preparation process is more complex, and most of annealed LaFe 13− x Si x compounds contained a small amount of α-Fe phase. Recently, our group used the arc-melting/high-temperature and short-time annealing to prepare 1:13 phase, the result showed the samples also contained a small amount of α-Fe phase [27] . For further improving the preparation process of La(Fe, Si) 13 compounds, the study of high-temperature phase transition of as-cast La(Fe, Si) 13 compounds is necessary. Up to now, no elaborate study of the phase transition is made when the as-cast La(Fe,Si) 13 compounds are annealed. In this paper, the influence of different short-time and high-temperature annealing of as-cast LaFe 11.6 Si 1.4 compound from 1323 K to 1623 K on phase relation is investigated. According to the DSC curve of as-cast compound and the X-ray patterns of annealed compounds, the high-temperature phase transition process is analyzed. In addition, the phase relation, microstructure, thermal and magnetic hysteresis, and magnetocaloric effects of LaFe 11.6 Si 1.4 compounds prepared by the two stages annealing are also studied. 2 Experimental details Approximately 10 g polycrystalline LaFe 11.6 Si 1.4 buttons were fabricated by conventional arc melting in a high purity argon atmosphere using high purity (La: 99.4 wt%, Fe: 99.9 wt%, and Si: 99.9999 wt%) elements, the compounds were re-melted five times to achieve a homogeneous composition. The as-cast compounds were annealed as followed process: 1323 K for 5 h (hereinafter h), 1373 K(5 h),1423 K, 1453 K(5 h), 1473 K(5 h), 1503 K(5 h), 1523 K(5 h), 1373 K(2 h) + 1523 K(5 h), 1523 K(5 h) + 1373 K(2 h), 1543 K(5 h), 1573 K(4 h), 1623 K(2 h), 1523 K(5 h) + 1623 K(2 h), and 1373 K(2 h) + 1523 K(5 h), and 1523 K(7 h) + 1373 K(2 h), respectively, in a molybdenum wire furnace of 3 × 10 −3 Pa vacuum, and then by furnace cooling down to room temperature. The phase purity and crystal structures observation were determined by powder x-ray diffraction (XRD) using Cu ( K α ) radiation. Scanning electron microscope (SEM) and energy disperse spectroscopy (EDS) observation are carried by Hitachi-S-3400 N. The phase transition of the compound was studied by Differential Scanning Calorimetry (DSC) in Ar gas atmosphere from 300 to 1773 K at 10 K/min. Magnetic measurements were performed using a vibrating-sample magnetometer (VSM, Lakeshore 7410). The Curie temperature ( T C ) were determined from the maxima of dM / dT of the M – T curves, which were measured in an applied magnetic field of H = 0.02 T. The magnetic entropy changes Δ S M ( T , H ) were calculated from isothermal magnetization curves ( M – H curves) under a magnetic fields of 0–2 T in the vicinity of the Curie temperature using the thermodynamic Maxwell relation [28] . 3 Result and discussion 3.1 The phase relation and microstructure of the single stage high-temperature and short-time annealing The long time annealing at about 1323 K is often used to prepare the LaFe 13− x Si x compounds with 1:13 phase, detailed studies of the heat treatment of LaFe 13− x Si x compounds are reported in few articles. For studying the effect of different higher-temperature and short-time heat treatment on the phase relation of LaFe 11.6 Si 1.4 compounds, different annealing temperatures were experimented. Fig. 1 shows the XRD patterns of LaFe 11.6 Si 1.4 compounds annealed at different high temperatures from 1323 K to 1623 K, and the as-cast compound respectively. One can find that the as-cast LaFe 11.6 Si 1.4 compound mainly consists of α-Fe and LaFeSi phases. In addition, the appearance of three minor peaks at 2 θ = 35, 38.5, and 46.8 indicates that there is a small amount of the third phase crystallized as 1:13 phase. It is well known that the temperature of annealing is higher, and the speed of diffusion of atoms is just larger during the high-temperature and solid-phase diffusion reaction. Thus, with increasing of annealing temperature from 1323 K to 1423 K, the amount of 1:13 phase gradually increases and α-Fe and LaFeSi phases gradually reduce. But compared the XRD patterns, one can find that the amount of 1:13 phase in the compound annealed at 1423 K is obviously more than that of other compounds annealed at lower temperatures. It indicates that 1423 K is a critical temperature to form 1:13 phase. The speed of phase transforming to form 1:13 phase is very slow when the annealing temperatures are lower than 1423 K. With the temperature increasing from 1423 K to 1523 K, α-Fe and LaFeSi phases in the LaFe 11.6 Si 1.4 compounds reduce in turn. The LaFeSi phase is rarely observed in the XRD pattern when the annealing temperatures reach 1503 K and 1523 K. Although the α-Fe always exists in the LaFe 11.6 Si 1.4 compounds, the amount of α-Fe is very small in the compounds annealed at 1503 K and 1523 K, especially at 1523 K. Thus, 1523 K is also a critical temperature for obtaining the 1:13 phase during the high-temperature and short-time annealing of as-cast LaFe 11.6 Si 1.4 compound. Our result that there is a small amount of α-Fe besides 1:13 main phase in the XRD patterns is accordant to some references, which reported that the La(Fe,Si) 13 compounds prepared by annealing for long time and then quenching rapidly in medium or furnace cooling to room temperature also contained the 1:13 main phase and small amount of α-Fe [29–32] . This indicates that high-temperature and short-time annealing at 1523 K is an effective and feasible method to prepare LaFe 11.6 Si 1.4 compounds with 1:13 phase. To further observe the effect of annealing temperature on the phase relation, the as-cast LaFe 11.6 Si 1.4 compounds are annealed at 1543 K(5 h), 1573 K(4 h), 1623 K(2 h), and 1523 K(5 h) + 1623 K(2 h), respectively. When the annealing temperature increases to 1573 K and 1623 K, there is a new phase crystallized as La 5 Si 3 phase whose the strongest diffraction peak is at 2 θ = 31.5, and more La 5 Si 3 phase appears with higher annealing temperature. The LaFe 11.6 Si 1.4 compound annealed at 1523 K(5 h) + 1623 K(2 h) also contains a certain amount of La 5 Si 3 phase, which is not observed in the XRD pattern of LaFe 11.6 Si 1.4 compound annealed at 1523 K(5 h). The amount of α-Fe in the LaFe 11.6 Si 1.4 compounds annealed at 1573 K(4 h), 1623 K(2 h), and 1523 K(5 h) + 1623 K(2 h) is obviously more than that in the compound annealed at 1523 K(5 h). In addition, there is no diffraction peaks of La 5 Si 3 phase in the compound annealed at 1543 K(5 h), but the amount of α-Fe is more than that of LaFe 11.6 Si 1.4 compound annealed at 1523 K(5 h). In all, the most amount of 1:13 phase is obtained when the as cast LaFe 11.6 Si 1.4 compounds is annealed at 1523 K among the above single stage annealing under the same time. Fig. 2 demonstrates the backscattered SEM micrographs of the annealed LaFe 11.6 Si 1.4 compounds and as-cast compound. The different phases in these compounds can be identified by XRD and EDS analysis. The phase relation and the amount of different phases are in agreement with the XRD patterns, as shown in Figs. 1 and 2 . Through the refine analysis, we find the 1:13 phase locates between α-Fe and LaFeSi phase, but the amount is so small that it hard to be observed in the SEM micrographs of the annealed LaFe 11.6 Si 1.4 at 1373 K(5 h) and as-cast compounds, as shown in Fig. 2 (a) and (b). The SEM micrographs also shows that 1423 K and 1523 K are two critical temperatures during the high-temperature and short-time annealing of as-cast LaFe 11.6 Si 1.4 compounds, at which large amount of 1:13 phase begins to form and the most amount of 1:13 phase is obtained, respectively. 3.2 The analysis of high-temperature phase transition of as-cast LaFe 11.6 Si 1.4 compound In order to study high-temperature phase transition during the annealing process, DSC measurement was performed. Fig. 3 shows the DSC curve of massive as-cast LaFe 11.6 Si 1.4 compound during the heating process. There are four main endothermal peaks; the temperature of peaks is 1407.6 K, 1530.5 K, 1593.1 K, and 1739.3 K, respectively. In as-cast LaFe 11.6 Si 1.4 compound, α-Fe is primary phase, La(Fe,Si) 13 is peritectic phase, and LaFeSi is solidifying phase of residual liquid, respectively. It is universally acknowledged that the 1:13 phase should be formed through γ-Fe and LaFeSi phase if the annealing temperature is higher than 1185 K, which is the temperature of structural transition between α-Fe and γ-Fe. Based on the analysis of EDS, we find that α-Fe in as-cast LaFe 11.6 Si 1.4 compound is Fe(Si) solid solution, the atomic percent of Fe and Si is 94.85 at% and 5.15 at%, respectively. In the Fe–Si binary phase diagram, there exists the phase transition between γ-Fe and α-Fe only when the Si at% is less than 3.8 at% in Fe(Si) solid solution [33] . Thus, there is only α-Fe during the annealing process of as-cast LaFe 11.6 Si 1.4 compound, and the 1:13 phase is formed through α-Fe + LaFeSi → La(Fe,Si) 13 . According to the phase rule, the melting point of α-Fe is the highest, that of LaFeSi phase is the lowest in as-cast LaFe 11.6 Si 1.4 compound, and that of peritectic phase is between the melting point of primary phase (α-Fe) and the temperature of peritectic reaction. Combining with the Fe–Si binary phase diagram, one can easily come to the conclusion that 1739.3 K in the DSC curve is the melting point of Fe(Si) solid solution. Based on the result that large amount of 1:13 phase begins to form and the most amount of 1:13 phase is obtained when the as-cast LaFe 11.6 Si 1.4 compound is annealed at 1423 K and 1523 K, respectively, 1407.6 K and 1530.5 K are the melting point of LaFeSi phase and the temperature of peritectic reaction: α-Fe + L → La(Fe,Si) 13 , respectively. In addition, 1593.1 K is the melting point of 1:13 phase. Thus, when the annealing temperature is near 1593.1 K, the non-equilibrium freezing of liquid 1:13 phase leads to the appearance of La 5 Si 3 phase. The tradition method of preparing LaFe 11.6 Si 1.4 compound is by long-time annealing at about between 1173 K and 1373 K, and the annealing temperature is lower than melting point of LaFeSi phase (about the 1407.6 K). Under this situation, the 1:13 phase is formed through a peritectoid reaction between the α-Fe and the solid LaFeSi phases; it needs long time to complete solid state diffusion reaction. But when the annealing temperature is near the point of peritectic reaction, the 1:13 phase is formed through a peritectic reaction between the α-Fe and liquid phase, which is faster than the peritectoid reaction between α-Fe and solid state LaFeSi phase. Thus, there is the most amount of 1:13 phase in the LaFe 11.6 Si 1.4 compound annealed at 1523 K under the same annealing time. 3.3 The two stages high-temperature and short-time annealing Combining the result that most amount of 1:13 phase is obtained when the as cast LaFe 11.6 Si 1.4 compound is annealed at 1523 K in high-temperature and short-time annealing process with the traditional preparation method that the as-cast La(Fe,Si) 13 compound is annealed at about 1373 K for long time. Two stages annealing are carried, they are 1373 K(2 h) + 1523 K(5 h), and 1523 K(7 h) + 1373 K(2 h), respectively. The aims of annealing of low temperature (1373 K) and high temperature (1523 K) are increasing the chemic driving force and diffused driving force of phase transition, respectively. Figs. 4 and 5 are the XRD patterns and SEM micrographs of the LaFe 11.6 Si 1.4 compounds annealed at 1523 K(5 h) and different two stages. Three compounds consist of the main 1:13 phase and a certain amount impurities. Although it is hard to be observed from XRD patterns, very small amount of LaFeSi phase (white phase) can be observed in SEM micrographs. In the SEM micrographs, the black phase (α-Fe) and white phase (LaFeSi) in LaFe 11.6 Si 1.4 compound annealed at 1523K(7 h) + 1373K(2 h) are obviously less than that of others, which attributes to the annealing time at 1523 K is longer than others. In traditional preparation method, the single 1:13 phase compounds are almost prepared through long time annealing and then quenched in ice water or liquid nitrogen, and slow cooling is believed to induce the lower-temperature phases, such as 1:1:1 phase. But in our work, LaFeSi phase in the compounds annealed at 1523 K(7 h) + 1373 K(2 h) is not more than that in the compound annealed at 1523 K(5 h). Thus, the LaFeSi phase also can come from the incompleteness of peritectoid reaction, and not the slow cooling process. Up to now, there has no report to discuss whether the α-Fe and LaFeSi phases come from the incompleteness of peritectoid reaction or the slow cooling process. 3.4 Magnetic property Fig. 6 (a–c) displays the temperature dependent magnetization measured under 0.02 T in heating and cooling processes for LaFe 11.6 Si 1.4 compounds annealed at 1523 K(5 h), 1373 K(2 h) + 1523 K(5 h), and 1523 K(7 h) + 1373 K(2 h), respectively. T C is defined as the maximum of dM / dT in heating process. The difference of above three compounds’ T C is little, they are about 190 K. Temperature hysteresis is an important index for magnetic refrigeration material, and it is defined as the difference between T C (heating process) and T C (cooling process). To some extent, the value of temperature hysteresis is response to the first-order magnetic transition intensity. From Fig. 6 (a–c), one can find that three compounds have the temperature hysteresis phenomenon, and the value is about 2 K. The isothermal magnetization curves measured at different temperature in the vicinity of T C are shown in Fig. 7 (a–c) for three LaFe 11.6 Si 1.4 compounds. The measurements were performed in field increasing process. In order to check whether the isothermal magnetization process involves magnetic hysteresis, one of M – H curves was measured during field up and down at near T C . There is a field-induced itinerant-electron metamagnetic (IEM) transition from the paramagnetic state to the ferromagnetic state in the range of 2 K above T C . It indicates that the initiated critical field ( H C ) of field-induced IEM transition is lower than 2 T. Magnetic hysteresis is also response to the first-order magnetic transition intensity, which is defined as the enclosed area between the ascending and descending branches of magnetization curve. The magnetic hysteresis loss of compounds annealed at 1523 K(5 h) and 1373 K(2 h) + 1523 K(5 h) is smaller than that of compound annealed at 1523 K(7 h) + 1373 K(2 h), their value are 36.5, 39.7, and 46.8 J/kg, at 189, 190, and 191 K, respectively. Fig. 8 shows the compared Arrott plots of the samples. One can find that negative slopes appear in all samples, and the value of slope increases in sequential order. According to the I – S model, negative slope in Arrott plots curve often indicates a first order transition and the linear relation in Arrott plot above T C implies that a second-order magnetic transition occurs. Thus, all samples have the first order of magnetic transition behavior, and the first-order of magnetic transition behavior becomes intensity in sequential order. Because the first-order magnetic refrigerant materials have magnetoelastic coupling or magnetovolume coupling characteristic, there still exists the issue about whether the Maxwell equations suits to calculate the magnetic entropy change of those materials. Sun et al. pointed out that the Maxwell relation and the Clausius–Clapeyron equation can give similar magnetic entropy change for an idealized first-order transition [5,34] . But in reality, a first-order phase transition occurs in a finite temperature range, and two phases may coexist in the transition process. In this case, the Maxwell relation could yield a spurious Δ S peak in the vicinity of the Curie temperature T C . Considering the fact that magnetic field affects only the magnetic state of PM phase, which coexists with the FM phase near T C , only the PM phase contributes to the thermal effect. Liu et al. established a modified equation for calculating Δ S in reference [31] : Δ S [( T 1 + T 2 )/2] = ∑ 1 /( T 1 − T 2 ). Fig. 9 shows the Δ S M ( T , H ) calculated by using Maxwell relation based on the magnetization data as functions of temperature and magnetic field for LaFe 11.6 Si 1.4 annealed by different processes. Because the experimental field is higher than the H C of field-induced IEM transition, Δ S M ( T , H ) peaks have asymmetrical broad phenomenon to higher temperature above T C . The value of maximum Δ S M ( T , H ) is 18.5, 21.5, and 25.3 J/kg K for three compounds near T C , the change trend of maximum Δ S M ( T , H ) is same to the first-order behavior of the magnetic transition in compounds. But from the M – H curves, as shown in Fig. 7 , one can find that the compound LaFe 11.6 Si 1.4 present a mixed magnetic phase in the temperature range near T C , especially in the samples annealed at 1523 K(5 h) and 1523 K(7 h) + 1373 K(2 h). Thus, the use of the Maxwell relation for the evaluation of the entropy change close to the magnetic transition is not valid. More realistic values of the entropy change can be obtained based on the approaches developed in Ref. [35] . The result showed realistic values of the entropy change near T C obtained as in Ref. [35] is 11.3 and 17.8 J/kg K for 1523 K(5 h) and 1523 K(7 h) + 1373 K(2 h), respectively, they are smaller than those obtained by using the Maxwell relation. In addition, according to the Fe–Si binary phase diagram, the Curie temperature of α-Fe(Si) is far higher than room temperature, α-Fe(Si) is at ferromagnetic state and has no the magnetic transition between ferromagnetic and paramagnetic. Thus, the magnetic entropy change of α-Fe(Si) is very small during magnetization and demagnetization process, and it is negligible in the calculation of the magnetic entropy change Δ S in this work. 4 Conclusions Combining the DSC of as-cast massive LaFe 11.6 Si 1.4 compound with the X-ray patterns of LaFe 11.6 Si 1.4 compounds annealed at different high temperatures from 1323 K(5 h) to 1623 K(2 h), the high temperature phase transition process is analyzed. Large amount of 1:13 phase begins to form in LaFe 11.6 Si 1.4 compounds when the annealing temperature is higher than the melting point of LaFeSi phase (about the 1407 K). Because 1523 K is close to the temperature of peritectic reaction: α-Fe + L → La(Fe, Si)13, thus the most amount of 1:13 phase is obtained in the LaFe 11.6 Si 1.4 compounds annealed at 1523 K under the same annealing time. The non-equilibrium freezing of liquid 1:13 phase leads to the appearance of La 5 Si 3 phase when the annealing temperature is near the melting point of 1:13 phase. The phase relation and microstructure of the LaFe 11.6 Si 1.4 compounds annealed at 1523 K(5 h), 1373 K(2 h) + 1523 K(5 h) and 1523 K(7 h) + 1373 K(2 h), show that longer annealing time is helpful to decrease the impurity phases, especially at 1523 K. The magnetic measurement shows that above three compounds keep the first-order of magnetic transition behavior at T C (about 190 K). The values of the maximal magnetic entropy change Δ S M ( T , H ) of the samples obtained by Maxwell relation are 18.5, 21.5, and 25.3 J ˜ kg K , respectively under the field of 0–2 T. Acknowledgments The present work was supported by the Key Project of National Natural Science Foundation of China (grant number 50731007 ) and the National High Technology Research and Development Program of China (grant number 2007AA03Z440 ). References [1] F.X. Hu B.G. Shen J.R. Sun Z.H. Cheng G.H. Rao X.X. Zhang Appl Phys Lett. 78 2001 3675 [2] K. Fukamichi A. Fujita S. Fujieda J. Alloys Compd. 408 2006 307 [3] A. Fujita K. Fukamichi J. Alloys Compd. 404 2005 554 [4] A. Fujita S. Koiwai S. Fujieda K. Fukamichi T. Kobayashi H. Tsuji J. Appl. Phys. 105 2009 07A936 [5] B.G. Shen J.R. Sun F.X. Hu H.W. Zhang Z.H. Cheng Adv. Mater. 21 2009 4545 [6] H. Zhang Y. Long Q. Cao M. Zou K.A. Gschneidner Jr. V.K. Pecharsky J. Alloys Compd. 509 2011 3746 [7] A. Fujita S. Fujieda K. Fukamichi J. Phys. D: Appl. Phys. 44 2011 064013 [8] K. Morrison J. Lyubina J.D. Moore A.D. Caplin1 K.G. Sandeman O. Gutfleisch L.F. Cohen J. Phys. D: Appl. Phys. 43 2010 132001 [9] S.J. Kim K.J. Lee M.H. Jung H.J. Oh Y.S. Kwon J. Magn. Magn. Mater. 323 2011 1094 [10] M. Rosca M. Balli D. Fruchart D. Gignoux E.K. Hlil S. Miraglia B. Ouladdiaf P. Wolfers J. Alloys Compd. 490 2010 50 [11] C. Wang Y. Long T. Ma B. Fu R. Ye Y. Chang F. Hu J. Shen J. Appl. Phys. 109 2011 07A910 [12] J.-l. Zhao J. Shen F.-x. Hu Y.-x. Li J.-r. Sun B.-g. Shen J. Appl. Phys. 107 2010 113911 [13] H. Zhang Y. Long Q. Cao Ya. Mudryk M. Zou K.A. Gschneidner Jr. V.K. Pecharsky J. Magn. Magn. Mater. 322 2010 1710 [14] S. Jun W. Fang J.-L. Zhao J.-F. Wu M.-Q. Gong F.-X. Hu Y.-X. Li J.-R. Sun B.-G. Shen J. Appl. Phys. 107 2010 09A909 [15] Z. Lin S. Li M. Liu S.-Y. Tsai J.-G. Duh M. Liu F. Xu J. Magn. Magn. Mater. 323 2011 1741 [16] X. Chen Y. Chen Y. Tang J. Alloys Compd. 509 2011 2864 [17] M. Zhang Y. Long R.-c. Ye Y.-q. Chang J. Alloys Compd. 509 2011 3627 [18] E.Y. Zhang Y.G. Chenand Y.B. Tang Mater. Chem. Phys. 127 2011 1 [19] M. Zhang R. Ye Y. Long Y. Chang J. Rare Earth 29 2011 138 [20] B.R. Hansen L. Theil Kuhn C.R.H. Bahl M. Lundberg C. Ancona-Torres M. Katter J. Magn. Magn. Mater. 322 2010 3447 [21] M. Jasinski J. Liu S. Jacobs C. Zimm J. Appl. Phys. 107 2010 09A953 [22] V. Paul-Boncour L. Bessais Intermetallics 18 2010 2301 [23] V. Raghavan J. Phase Equilib. 22 2001 158 [24] A. Yan K.-H. Müller O. Gutfleisch J. Appl. Phys. 97 2005 036102 [25] X.B. Liu Z. Altounian GHTu J. Phys.: Condens. Matter 16 2004 8043 [26] Y. Zhu K. Xie X. Song Z. Sun W. Lv J. Alloys Compd. 392 2005 20 [27] T. Liu Y. Chen Y. Tang S. Xiao E. Zhang J.w. Wang J. Alloys Compd. 475 2008 672 [28] M. Foldeaki R. Chahine T.K. Bose J. Appl. Phys. 77 1995 3528 [29] F.X. Hu M. Ilyn A.M. Tishin J. Appl. Phys. 93 2003 5503 [30] F.X. Hu X.L. Qian J.R. Sun G.J. Wang X.X. Zhang Z.H. Cheng etal J. Appl. Phys. 92 2002 3620 [31] S.H. Xie J.Q. Li Y.H. Zhuang J. Magn. Magn. Mater. 311 2007 589 [32] G.F. Wang L. Song F.A. Li Z.Q. Ou O. Tegus E. BrÜck K.H.J. Buschow J. Magn. Magn. Mater. 321 2009 3548 [33] F.A. Shunk Constitution of Binary Alloys second supplement 1969 Mcgraw-Hill Book Co New York [34] J.R. Sun F.X. Hu B.G. Shen Phys. Rev. Lett. 85 2000 4191 [35] G.J. Liu J.R. Sun J. Shen B. Gao H.W. Zhang F.X. Hu B.G. Shen Appl. Phys. Lett. 90 2007 032507
What problem does this paper attempt to address?
-
Effect of Co Addition on the Phase Structure and Magnetic Properties of Fe-Si-Al Alloys
Wang Wei,Ma Tianyu,Luo Wei,Yan Mi
DOI: https://doi.org/10.3321/j.issn:1002-185x.2008.06.032
2008-01-01
Abstract:(Fe1-xCox)(85)Si9.6Al5.4 (x=0, 0.05, 0.10, 0.15, 0.20) nanocrystalline flakes with large aspect ratio have been prepared by high-energy planetary ball milling method from melt spun ribbons. Annealing at 773 K for 30 min has been employed to the as-milled powder under the protection of nitrogen. The annealed powder is then mixed with resin to get toroidal samples of Phi 19 mm x Phi 10 mm, x 3 mm at 30 MPa. The effects of Co addition on the phase structure and magnetic properties have been discussed detailed. The results show that the Co addition doesn't change the phase structure of alloy ribbons. However, The Curie temperature has been greatly increased by Co addition; the maximum saturation magnetization is achieved when x=0.15. The toroidal samples show a good anti electromagnetic interference (EMI) performance at about 1GHz. The cutoff frequency reaches 1.154 GHz when x=0.15.
-
Structure and Magnetic Properties of Shortly High Temperature Annealing LaFe11.6Si1.4 Compound
Tao Liu,Yungui Chen,Yongbai Tang,Sufen Xiao,Enyao Zhang,Jinwei Wang
DOI: https://doi.org/10.1016/j.jallcom.2008.07.139
IF: 6.2
2009-01-01
Journal of Alloys and Compounds
Abstract:The LaFe11.6Si1.4 compound was prepared by arc-melting method and annealed at high temperatures of 1423K, 1473K and 1573K for an hour, respectively. The metallographic microscopy and powder X-ray diffraction analyses show that the as-cast LaFe11.6Si1.4 compound mainly consists of α-Fe and LaFeSi phases. However, the main phase of the annealed LaFe11.6Si1.4 compound is cubic NaZn13-type phase, which increases with the increase in annealing temperature. The maximal magnetic entropy change (−ΔSM) of the sample annealed at 1573K is 17.56J/kgK at a magnetic field change of 0–5T.
-
Microstructure of LaFe13-xSix alloys annealed at high temperature for a short time
Tao Liu,Yungui Chen,Yongbai Tang,Sufen Xiao,Enyao Zhang,Jinwei Wang,Mingjing Tu
DOI: https://doi.org/10.3321/j.issn:1002-185x.2009.05.030
2009-01-01
Rare Metal Materials and Engineering
Abstract:The microstructures of the as-cast and the shortly annealed LaFe13-xSix (x=1.43, 1.56, 2.4) alloys at high temperature were investigate by X-ray diffraction, scanning electron microscope and energy dispersive spectroscopy. It was demonstrated that the microstructure of the as-cast LaFe11.570Si1.43 was characterized by dendrite grains, which contained a large amount of alpha-Fe and LaFeSi. LaFe11.44Si (1.56) had not only dendrite grains but also most amount of phases crystallized in NaZn13-type structure besides alpha-Fe and LaFeSi. The NaZn13-type structure of the as-cast LaFe10.6Si2.4 could be directly obtained and characterized by cellular grains. After annealing at 1350 degrees C for half an hour, the dendrite grains were turned into equiaxed ones, and NaZn13-type structure phases were formed as the matrix phase, with the existence of alpha-Fe and impurity phase LaFeSi.
-
One-Step Sintering Process for the Production of Magnetocaloric La(Fe,Si)13-Based Composites
Xi-Chun Zhong,Xu-Tao Dong,Jiao-Hong Huang,Cui-Lan Liu,Hu Zhang,You-Lin Huang,Hong-Ya Yu,Raju V. Ramanujan
DOI: https://doi.org/10.3390/met12010112
IF: 2.695
2022-01-06
Metals
Abstract:A one-step sintering process was developed to produce magnetocaloric La(Fe,Si)13/Ce-Co composites. The effects of Ce2Co7 content and sintering time on the relevant phase transformations were determined. Following sintering at 1373 K/30 MPa for 1–6 h, the NaZn13-type (La,Ce)(Fe,Co,Si)13 phase formed, the mass fraction of α-Fe phase reduced and the CeFe7-type (La,Ce)(Fe,Co,Si)7 phase appeared. The mass fraction of the (La,Ce)(Fe,Co,Si)7 phase increased, and the α-Fe phase content decreased with increasing Ce2Co7 content. However, the mass fraction of the (La,Ce)(Fe,Co,Si)7 phase reduced with increasing sintering time. The EDS results showed a difference in concentration between Co and Ce at the interphase boundary between the 1:13 phase and the 1:7 phase, indicating that the diffusion mode of Ce is reaction diffusion, while that of Co is the usual vacancy mechanism. Interestingly, almost 100 % single phase (La,Ce)(Fe,Co,Si)13 was obtained by appropriate Ce2Co7 addition. After 6 h sintering at 1373 K, the Ce and Co content in the (La,Ce)(Fe,Co,Si)13 phase increased for larger Ce2Co7 content. Therefore, the Curie temperature increased from 212 K (binder-free sample) to 331 K (15 wt.% Ce2Co7 sample). The maximum magnetic entropy change (−ΔSM)max decreased from 8.8 (binder-free sample) to 6.0 J/kg·K (15 wt.% Ce2Co7 sample) under 5 T field. High values of compressive strength (σbc)max of up to 450 MPa and high thermal conductivity (λ) of up to 7.5 W/m·K were obtained. A feasible route to produce high quality La(Fe,Si)13 based magnetocaloric composites with large MCE, good mechanical properties, attractive thermal conductivity and tunable TC by a one-step sintering process has been demonstrated.
materials science, multidisciplinary,metallurgy & metallurgical engineering
-
Preparation and magnetocaloric performance of La(Fe,Co,Si) 13 alloys with wide transition temperature range
Liang Xian,Jian Yu,Weixiao Lin,Shaoqiu Ke,Chengshan Liu,Xiaolei Nie,Wanting Zhu,Ping Wei,Danqi He,Wenyu Zhao,Qingjie Zhang
DOI: https://doi.org/10.1016/j.intermet.2023.107827
IF: 4.075
2023-01-09
Intermetallics
Abstract:NaZn 13 -type La(Fe,Si) 13 alloys are one of the most promising magnetocaloric materials for room-temperature magnetic refrigeration. However, the narrow ferromagnetic-to-paramagnetic transition temperature range of La(Fe,Si) 13 alloys severely limited their magnetic refrigeration application. Herein, a series of La 1.4 Fe 11.8- x Co x Si 1.2 ( x = 0.88, 0.94, 0.98, 1.02, 1.06) alloys were designed and prepared by high-energy ball milling and annealing. It is discovered that all the samples are composed of La(Fe,Co,Si) 13 main phase and a small amount of α -Fe phase. The Curie temperature of the ferromagnetic-to-paramagnetic transition was well adjusted to room temperature by optimizing the x . A maximum magnetic entropy change (- ΔS M ) of 4.0 J kg −1 K −1 for the sample with x = 0.98 was obtained at a magnetic field of 2 T. Meanwhile, all the samples exhibit a significant increase in the half-height width of - ΔS M reaching approximately 35 K, increased by more than 41% compared with that of the reference sample prepared by arc melting. The broadened temperature range originates from the lattice distortion induced by the ball milling process. Our work indicates that La(Fe,Si) 13 alloys with relatively large - ΔS M and wide transition temperature range can be simultaneously obtained around room temperature by optimizing the composition and the ball milling process.
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering
-
Phase Diagram and Annealing Effect for Fe1+δTe1−xSxsingle Crystals
Chiheng Dong,Hangdong Wang,Qianhui Mao,Rajwali Khan,Xi Zhou,Chenxia Li,Jinghu Yang,Bin Chen,Minghu Fang
DOI: https://doi.org/10.1088/0953-8984/25/38/385701
2013-01-01
Journal of Physics Condensed Matter
Abstract:The excess Fe atoms which unavoidably exist in the Fe(Te, Se, S) crystal lattice result in a complicated antiferromagnetic ground state as well as the suppression of superconductivity. As a result, there are still discrepancies on their phase diagrams. In this paper, we report the synthesis of Fe1+delta Te1-xSx (0 <= x <= 0.12) single crystals by a melting method. Superconductivity was greatly improved after air annealing by which we partially removed the excess Fe atoms. Based on the resistivity and susceptibility measurements, we concluded a phase diagram of the Fe1+delta Te1-xSx (0 <= x <= 0.12) system with fewer excess iron atoms. We found a coexisting region (0.07 <= x <= 0.11) of antiferromagnetic order and bulk superconductivity. This phase diagram is similar to that of the K- or Co-doped BaFe2As2 system, as well as the Fe(Te, Se) system, implying a commonality of the iron-based superconductors.
-
Synthesis and properties of La-Fe-Si/La-Co magnetocaloric composites
Yu-Cai Wu,Xi-Chun Zhong,Yuan-Xin Li,Xuan Huang,Jiao-Hong Huang,Cui-Lan Liu,Zhong-Wu Liu,Wan-Qi Qiu,Ming-Long Zhong,Zhen-Chen Zhong,R.V. Ramanujan
DOI: https://doi.org/10.1016/j.materresbull.2023.112338
IF: 5.6
2023-05-14
Materials Research Bulletin
Abstract:LaFe 11.8 Si 1.2 /16wt%La 65 Co 35 samples were prepared by spark plasma sintering (SPS) and subsequent annealing. The La 65 Co 35 binder increased the desired 1:13 phase content in these samples during annealing at 1323 K. Interestingly, the α-Fe phase formed between the LaFe 11.8 Si 1.2 particles and the La 65 Co 35 binder and then disappeared as the annealing time extended. The sample annealed for 0.5 h had a distinct core-shell structure with Co in the shell, a desirable table-like (−∆ S M )− T curve was obtained and its RC (153 J·kg −1 ) was 107% higher compared to the sample before annealing. The diffusion of Co from La 3 Co to the 1:13 phase was hampered by the growth of La 5 Si 3 phase. Relatively large (−∆ S M ) max of ∼8.51 J·kg −1 ·K −1 (Δμ 0 H =2 T) and ( σ bc ) max of 374 MPa for the sample annealed for 24 h were obtained. These results indicated that the method combining SPS and diffusion annealing is promising to prepare La-Fe-Si based magnetocaloric composites with good properties.
materials science, multidisciplinary
-
Annealing temperature effects on microstructure and magnetic properties of Fe-6.5wt. %Si alloy strips prepared by TSTRC process
Dongpo Xuan,Xuming Liu,Ning Xu,Han Guo,Zhiyu Geng,Yitong Wang,Feng Xue
DOI: https://doi.org/10.1016/j.jmmm.2024.172141
IF: 3.097
2024-05-13
Journal of Magnetism and Magnetic Materials
Abstract:The Fe-6.5wt.%Si alloy exhibits remarkable soft magnetic characteristics, such as high magnetic permeability, low coercivity, high resistivity, and nearly zero magnetostriction. These attributes establish it as an ideal material for low-power, low-noise electric motors and transformers. This investigation aimed to assess the impact of annealing temperature (ranging from 800 to 1200 °C for 1 h) on the microstructure, texture, and magnetic properties of a 0.15 mm thick Fe-6.5wt.%Si alloy sheet, which was obtained by subjecting the strips produced through the top side-pouring twin-roll casting (TSTRC) process to multi-pass warm rolling in the temperature range of 600 ∼ 800 °C, avoiding hot rolling. Additionally, the recrystallization mechanism of the annealed sheet at 1100 °C for 1 h was explored. The findings indicate that enhancing the annealing temperature corresponded to a reduction in magnetic induction (B 8 and B 50 ) as well as iron losses (P 10/50 , P 10/400 , and P 2/1000 ). The annealed sheet at 1200 °C for 1 h demonstrated the most favorable magnetic properties, displaying iron losses of 0.486 W/kg, 6.895 W/kg, and 1.232 W/kg for P 10/50 , P 10/400 , and P 2/1000 , respectively. These results illustrate excellent overall magnetic characteristics. The coercivity (Hc) of both B 8 and B 50 decreased as the annealing temperature increased in the hysteresis loop measurements. Specifically, for B 8 , it decreased from 62.84 A/m to 24.50 A/m, and for B 50 , it decreased from 78.10 A/m to 35.50 A/m. The average grain size of the samples gradually increased as the annealing temperature ranged from 800 to 1200 °C. The dominant texture observed was {1 1 1}, and the volume fraction of {1 1 1} texture increased while the volume fractions of {1 0 0} and {1 1 0} textures decreased. Upon annealing at 1100 °C for 8 s, the elongated and flattened deformed structures were mainly replaced by equiaxed grains, indicating the completion of the recrystallization process. However, there was a noticeable distinction in the coarsening degree of equiaxed grains based on their orientations. The presence of λ-oriented grains was less prominent, while α-oriented and γ-oriented grains were relatively more abundant. As the annealing time increased from 8 s to 1 h, there was a decrease in the presence of λ-oriented and α-oriented grains, while the presence of γ-oriented grains significantly increased.
materials science, multidisciplinary,physics, condensed matter
-
Effect of annealing on microstructure and magnetocaloric properties of plastically deformed La0.7Ce0.3Fe13.68Mn0.2Si1.4 alloys
Xiang Lu,Shuang Zeng,Yifei Zhang,Pengna Zhang,Qiuxiao Jiang,Jian Liu
DOI: https://doi.org/10.1016/j.jmrt.2022.03.097
IF: 6.267
2022-05-01
Journal of Materials Research and Technology
Abstract:In this study, we have employed a near-net-shape hot forging deformation with ∼67% reduction ratio, and an annealing process at 1223–1423 K to prepare bulk La0.7Ce0.3Fe13.68Mn0.2Si1.4 alloys. The deformed samples are featured by a unique microstructure consisting of layered α-Fe and La-rich phases. These layered phases gradually degrade during the subsequent annealing, and eventually appear as the magnetocaloric phase (the 1:13 phase) matrix embedded mainly with the α-Fe particles. Upon annealing at 1323 K, the deformed sample has the largest 1:13 phase formation rate. Significant magnetic entropy change of 15.6 J/kg K and a relatively small magnetic hysteresis of 30.9 J/kg at 5 T are achieved in the current forged La-Ce-Fe-Mn-Si alloy on an optimal annealing condition, i.e., 1323 K for 24 h. The large magnetic entropy, rapid 1:13 phase formation rate and near-net shape make the hot-forged La-Ce-Fe-Mn-Si alloys promising magnetic refrigerants.
materials science, multidisciplinary,metallurgy & metallurgical engineering
-
Effect of Si addition on the magnetic properties of FeNi-based alloys with L10 phase through annealing amorphous precursor
Ziyan Hao,Linzhuo Wei,Yaocen Wang,Yoshiyuki Kawazoe,Xiaoyu Liang,Rie Umetsu,Noriharu Yodoshi,Xing Tong,Weixing Xia,Yan Zhang,Chongde Cao
DOI: https://doi.org/10.1016/j.jallcom.2022.166029
IF: 6.2
2022-11-05
Journal of Alloys and Compounds
Abstract:As a promising candidate of rare-earth free hard magnetic materials, L10-FeNi has been paid much attention in the last decades. However, it is difficult to be artificially fabricated due to its low thermal stability and sluggish diffusion ability of atoms below the crucial temperature of 320 °C. In this study, a promising method of annealing amorphous precursor was extensively developed through (Fe50Ni50)84−xSixP16 (x = 0, 4 at%) and (Fe50Ni50)86−xSixP14 (x = 2, 4, 8 at%) alloys. Especially, the effect of Si on the formation of L10 phase in annealed FeNi-based alloys was investigated and clarified. It is found Fe42Ni42P16 with a much low crystallization temperature could be an appropriate basic amorphous alloy for the formation of L10 phase. The addition of Si enhanced the thermal stability of Fe-Ni-P amorphous alloys. Interestingly, Si could stabilize the L10 phase in annealed samples and increase its disordering temperature above which L10-FeNi phase could deteriorate into soft magnetic phase. As expected, appropriate Si addition indeed improved the hard magnetic properties of the annealed alloys and samples with high coercivity above 900 Oe was obtained. Further Si addition would deteriorate the magnetic-crystalline anisotropy of L10 phase and decrease the coercivity of annealed Fe-Ni-Si-P alloys. Nevertheless, the results indicate that increasing the order-disorder transition temperature through element doping in L10 lattice would be a promising strategy for the massive formation of L10-FeNi like other ordered phases (i.e. L12-FeNi, L10-CoPt), and could substantively contribute to the artificial fabrication of FeNi-based rare-earth free magnets in future.
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering
-
Effect of Fe addition on transformation temperatures and hardness of NiMnGa magnetic shape memory alloys
F. Chen,H. B. Wang,Y. F. Zheng,W. Cai,L. C. Zhao
DOI: https://doi.org/10.1007/s10853-005-5712-3
IF: 4.5
2005-01-01
Journal of Materials Science
Abstract:In recent years, ferromagnetic shape memory alloys (FSMAs) have been widely investigated in many countries [1–4]. Of the developed FSMAs, NiMnGa alloys have been found to exhibit nearly 10% magnetic-fieldinduced strain which is the maximum obtained MFIS in these FSMAs [5]. Based on NiMnGa alloys, researchers have developed new ferromagnetic shape memory alloys, i.e., NiMnFeGa alloys [6, 7]. The structure, shape memory effect, and magnetic properties of Fe-doped NiMnGa alloys have been studied. It is assumed that the addition of Fe element enhances the alloy plasticity without sacrificing its magnetic and thermoelastic properties [6]. However, little work has been devoted to studying transformation behavior and the mechanical properties of polycrystalline Fe-doped NiMnGa alloys. The aim of the present letter is to study the effect of additions of Fe on transformation behavior and the hardness of NiMnGa alloys. A range of alloys with the nominal composition of Ni48.7Mn30.1−x Fex Ga21.2 (at%) (x = 0, 2, 5, 8, 11), each weighing about 80 g, were prepared. The alloys were fabricated by arc melting under an argon atmosphere using appropriate quantities of nickel (99.99% purity), manganese (99.9% purity), iron (99.9% purity) and gallium (99.99% purity). The ingots obtained were sealed in a quartz tube under a vacuum, followed by annealing at 1123 K for 24 hrs and quenched into ice water for homogeneity. Rectangular samples 4×4×6 mm were cut from the post-treated ingots for hardness measurements. Some 10 mg samples were taken from the ingots for DSC measurements. The transformation temperatures were determined by differential scanning calorimetry using a TA-2920. The heating and cooling rates were 10 K/min. The crystal structure at room temperature was confirmed by powder X-ray diffraction using D/MAX-RA X-ray diffractometer with Cu Kα radiation. Micro Vickers hardness (HV) of eight points was measured using a Akashi HM-102 Vickers Hardness Tester. The applied load and time were 200 g and 15 s, respectively. The HV values were averaged excluding the highest and lowest values [8]. Table I summarizes the transformation temperatures measured by DSC analysis in Ni48.7Mn30.1−x Fex Ga21.2 alloys (x = 0, 2, 5, 8, 11). It can be seen, at room temperature, that the parent phase and martensite coexist in the Ni48.7Mn30.1Ga21.2 alloy and the Ni48.7Mn28.1Fe2Ga21.2 alloys, whereas in the other three alloys only the parent phase exists. The results are in agreement with X-ray diffraction results in Fig. 1. X-ray patterns depict that the cubic parent phase and tetragonal martensite coexist when x = 0, 2, while only the cubic parent phase exists when x = 5, 8, 11. As shown in Table I, the thermal hysteresis of these five alloys are −1.38, −3.30, 0.46, 2.60 and 2.20 ◦C, respectively. For the Ni48.7Mn30.1Ga21.2 alloy and the Ni48.7Mn28.1Fe2Ga21.2 alloys, the thermal hysteresis is negative. Hence Fe-doped NiMnGa alloys exhibit very narrow thermal hysteresis which means that the chemical energy of the phase transformation is very small. The narrow thermal hysteresis also shows that the driving force for inducing the martensitic transformation in Fe-doped NiMnGa alloy is very small. Wayman [9] divided thermal transformations into two types: the first is Af > As > Ms > Mf while the second is Af > Ms > As > Mf. From Table I it can be seen that the first two alloys belong to the second type of thermal transformation, while the other three alloys belong to the first type of thermal transformation. In addition, only single forward and reverse transformation are determined by DSC curves. Fig. 2 depicts the phase transformation temperatures vs. Fe content for Ni48.7Mn30.1−x Fex Ga21.2 alloys (x = 0, 2, 5, 8, 11). It can be seen that with increase of Fe content all the transformation temperatures, Ms (martensitic transformation start temperature), Mf (martensitic transformation finish temperature), As (reverse martensitic transformation start temperature), and A f (reverse martensitic transformation finish temperature), decrease. The relationship between Ms temperature and Fe content is nearly linear, varing from 26.40 ◦C for Ni48.7Mn30.1Ga21.2 without Fe to −55.00 ◦C for Ni48.7Mn19.1Fe11Ga21.2 which has the maximum Fe content. Fig. 3 exhibits the relationship between transformation temperatures and valence electron numbers per atom of Ni48.7Mn30.1−x Fex Ga21.2 alloys (x = 0, 2, 5, 8, 11) and the shape of the curves is similar to Fig. 2. The tendency is clear that all transformation temperatures decrease with increase of electronic concentration in these five alloys, and the increasing rate is also basically consistent with the change of the electronic concentration. Here, it is assumed that the number of valence electrons per atom for Ni, Mn, Fe, and Ga atoms is 10(3d84s2),7(3d54s2),8(3d64s2) and 3(3s24p1), respectively. It is believed that two factors, the conduction electronic concentrations [10] and the size factor [11],
-
Microstructure evolution and accelerated magnetocaloric phase formation of LaFe13.1Co0.7Si1.4 alloy by forging deformation at room temperature
RuZhao Chen,Bin Fu,Hu Zhang,Jie Hu,Xu Yang,LianQi Zhang,RuZhao Chen,Bin Fu,Hu Zhang,Jie Hu,Xu Yang,LianQi Zhang
DOI: https://doi.org/10.1016/j.jallcom.2022.166621
IF: 6.2
2022-12-05
Journal of Alloys and Compounds
Abstract:In order to improve the preparation process and practical process of magnetic refrigerant, a method of accelerating phase formation by cold compression plastic deformation at room temperature is proposed. To determine the significance of this method, the grain structure, phase composition and magneto-thermal effects of LaFe13.1Co0.7Si1.4 alloy were systematically studied. The results show that with the increase of compression ratio, the number of grains per unit volume increases and the grain size tends to be uniform. Compared with the uncompressed sample, the proportion of magnetothermal phase in the pre-compressed samples increases after annealing under the same conditions. When the deformation is 40%, the ratio of 1:13 phase in pre-deformed sample after 1 day annealing is 72 vol%, which is significantly better than that of the undeformed sample. After annealing for 3 days, the Curie temperature (TC) of 40% pre-deformed LaFe13.1Co0.7Si1.4 samples is 330 K, and the magnetic entropy changes to − 4.70 J/kg K and − 5.42 J/kg K under 2 T and 3 T magnetic fields, respectively. The appropriate Curie temperature and value of ∆SM make it an attractive potential candidate for magnetic refrigeration application at room or even high temperature.
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering
-
Magnetocaloric effect and phase transformation of LaFe11.0M0.5Si1.5 (M = Cu, Ni, Mg) alloys
Bo-Yu Song,Yong-Quan Han,Lei Gao,Juan Cheng,Cui-Lan Liu,Jiao-Hong Huang
DOI: https://doi.org/10.1016/j.jallcom.2023.171365
IF: 6.2
2023-11-01
Journal of Alloys and Compounds
Abstract:La (Fe,Si)13 is a promising magnetic refrigerant material. In this paper, the effects of Cu, Ni and Mg substitution of Fe on the magnetocaloric effect and phase transition properties of LaFe11.5Si1.5 alloys were studied by first-principles calculations combined with experiments. Through scanning electron microscopy–energy-dispersive spectroscopy analysis, it was concluded that after Cu partially replaced Fe, the content of the 1:13 main phase significantly decreased to 61.49%, and the contents of the α-Fe and LaFeSi phases increased. Cu was not conducive to the formation of the main phase. After Mg partially replaced Fe, the content of the 1:13 main phase increased to 99.12%, and Mg promoted the formation of the main phase. The electronic structure of the alloy was reconstructed by density functional theory (DFT), and the effects of the doping atoms on the magnetic properties of the alloys were studied. The calculation results showed that Ni atoms had the same weak magnetism as that in the magnetic moment vector direction of Fe atoms, Cu and Mg atoms had magnetism opposite to that in the magnetic moment vector direction of Fe atoms, and all alloys showed a lower total magnetic moment. According to the Arrott curve and the field dependence method of the magnetocaloric effect (MCE), when Cu = 0.5 and Ni = 0.5, the alloy phase transition changed from a first-order phase transition to a second-order phase transition, and when Mg = 0.5, the alloy still had a first-order phase transition.
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering
-
High-throughput Computation on Relationship Between Composition and Magnetic Phase Transition Temperature of LaFe11.5Si1.5-based Magnetic Refrigeration Materials
Su Wen-Xia,Lu Hai-Ming,Zeng Zi-Rui,Zhang Yi-Fei,Liu Jian,Xu Kun,Wang Dun-Hui,Du You-Wei
DOI: https://doi.org/10.7498/aps.70.20211085
IF: 0.906
2021-01-01
Acta Physica Sinica
Abstract:La(Fe, Si)13-based alloys have attracted more and more attention, for they exhibit giant magnetocaloric effects. In order to broaden their magnetic refrigeration temperatureranges, achieving a series of La(Fe, Si)13-based alloys with different magnetic phase transition temperatures is of great significance. Unlike the traditional research method, in this paper, a high-throughput first-principles computation is performed to estimate the magnetic phase transition temperature of the LaFe11.5Si1.5-based alloy by employing AMS-BAND software and the mean field theory. We investigate the effects of doping Mn, Co, Ni, Al atoms and Fe-vacancies on the magnetic phase transition temperature of LaFe11.5Si1.5-based alloy, and give the phase diagrams between the composition and magnetic phase transition temperature. The calculated results demonstrate that the magnetic phase transition temperature of the LaFe11.5Si1.5-based alloy increases with the increase of Co and Ni content. However, it shows an opposite result when Mn atom is doped. As for the LaFe11.5Si1.5-based alloy with the Fe-vacancies, the research results indicate that the absence of Fe atoms will reduce the magnetic phase transition temperature. Furthermore, when Mn, Co, Ni and Al atoms are doped in the alloys with Fe-vacancies, the variation tendency of the magnetic phase transition temperature with the change of the doping content is similar to that without the Fe-vacancies. Some estimated results are compared with the experimental or reported results, showing that they are in good agreement with each other. The PDOS and the magnetic moments of Fe atoms in the Mn, Co, Ni, Al-doped LaFe11.5Si1.5-based alloys are calculated, in which only the doping of Mn atoms can increase the magnetic moments of Fe atoms. Using the method of high-throughput first-principles calculation can effectively reduce the research cost and improve the working efficiency. In addition, it can provide technical support for the experimental selection of magnetocaloric materials with appropriate magnetic phase transition temperatures.
-
On the microstructural evolution and accelerated magnetocaloric phase formation in La-Fe-Si alloys by hot forging deformation
Xiang Lu,Yifei Zhang,Fengqing Wang,Mingxiao Zhang,Jian Liu
DOI: https://doi.org/10.1016/j.actamat.2021.117334
IF: 9.4
2021-12-01
Acta Materialia
Abstract:To solve the difficulty in forming magnetocaloric phase in La-Fe-Si alloys due to intrinsic incompleteness of peritectic reaction and slow diffusion rate, we proposed here a new approach of hot forging deformation to accelerate the phase formation. The evolution of phase constitution, grain structure and magnetocaloric effect has been systematically investigated, and the underlying mechanism was revealed. It was found that a novel microstructure, consisting of refined layer phases and high-density grain boundaries, formed during the forging deformation and played a key role in promoting the phase formation process. As a result, a dominant La(Fe, Si)13 phase with a volume fraction of 82.2% was obtained in the 84.4% deformed sample after annealing at 1323 K for only 1 h. This led to a large magnetic entropy change of 14.6 J/kg K at 2 T compared with 1.3 J/kg K for the non-deformed sample. A prominent magnetic entropy change of 19.4 J/kg K at 2 T was obtained after annealing for 12 h and hydrogenating, and the integrity of the sample was maintained. The current results suggest that the forging deformation effectively facilitates the magnetocaloric phase formation in La-Fe-Si alloys, and becomes a promising route for mass production of near-net-shape magnetic refrigerants.
materials science, multidisciplinary,metallurgy & metallurgical engineering
-
Optimization of microstructure and magnetocaloric effect by heat treatment process in LaFe11.7Si1.3 microwire
Ruochen Zhang,Xuexi Zhang,Mingfang Qian,Christian R.H. Bahl
DOI: https://doi.org/10.1016/j.jallcom.2021.161845
IF: 6.2
2022-01-01
Journal of Alloys and Compounds
Abstract:A large magnetocaloric effect and significantly shortened annealing process were obtained simultaneously in melt-extracted LaFe11.7Si1.3 microwires. Large amounts of La(Fe,Si)13 phases were formed within 5 min when annealed at 1353 K via a rapid peritectic reaction, because the nanoscale dendrites and a small amount of nanoscale La(Fe,Si)13 phases discovered inside grains could provide a lot of nucleation sites. Thereby, the main phase in LaFe11.7Si1.3 microwire after annealed at 1353 K for 5 min was La(Fe,Si)13 phase, although a small quantity of α-Fe and La-rich phases still remained in the microstructure. The annealed LaFe11.7Si1.3 microwires exhibited a first-order magnetic transition behavior and a large maximum magnetic entropy change of 7.7 J/kg K under a magnetic field of 1.4 T with negligible magnetic hysteresis. However, the strength of the first-order transition became weakened with the extension of annealing time. Finally, the working temperature range of LaFe11.7Si1.3 microwires was elevated to room temperature by hydrogenation, which expanded the application of LaFe11.7Si1.3 microwires in active magnetic regenerator.
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering
-
Curie Temperature Mechanism in La(Fe,Si)(13) Compound
Wang Fang,Wang Jin-Zhi,Feng Tang-Fu,Sun Ren-Bing,Yu Sheng
DOI: https://doi.org/10.7498/aps.63.127501
IF: 0.906
2014-01-01
Acta Physica Sinica
Abstract:In NaZn13 type La(Fe,Si)(13) compound, the phase transition nature varies from the first order to the second order, the cell volume contracts, the saturated magnetization decreases and the Curie temperature increases with increasing Si content. In this paper, the relation between the Curie temperature and the cell volume is investigated systematically by introducing the interstitial carbon atoms, which is an efficient method to control the cell volume and the Curie temperature. It is found that the relation between the Curie temperature and the cell volume is consistent with the Jaccarino-Walker model, in which only 5% or less 3d electrons are considered as the itinerant electrons and the others are regarded as the localized ones. With the polarized itinerant electrons used as a medium, the interaction between the 3d localized electrons is similar to Ruderman-Kittel-Kasuya-Yosida interaction, whose sign and magnitude oscillate periodically with distance. The number of the itinerant electrons of the La (Fe,Si)(13) increases with the increase of Si content. The Curie temperature is dependent on both the cell volume and the number of itinerant electrons.
-
High-temperature strengthening mechanism and thermal stability of Laves phase in ferritic matrix
Taotao Ruan,Junjie Shen,Bo Li,Zhihang Zhao,Dechang Zhang
DOI: https://doi.org/10.1016/j.msea.2022.144183
2022-11-24
Abstract:The high-temperature creep strengthening mechanism and thermal stability of Laves phase are the key factors that affect its strengthening property in ferritic matrix. Therefore, in this study, two types of C14 Laves phase alloys, namely, Fe2Nb Laves phase Alloy S1 (Fe–9Cr–4Al–2Nb) (wt.%) and Fe2W Laves phase Alloy S2 (Fe–9Cr–4Al–2W) (wt.%) were prepared to investigate the strengthening mechanism and strengthening effect of Laves phase with different compositions in ferritic matrix. The creep properties and microstructure characteristics of the two alloys, in particular, the interfacial structure characteristics between Laves phases (Fe2Nb and Fe2W) and ferritic matrix were analyzed. The true stress exponent n for both Alloys S1 and S2 is 5, and the true activation energies Q of Alloys S1 and S2 are 372.47 and 365.82 kJ mol−1, respectively. The creep mechanisms of Alloys S1 and Alloy S2 are both dislocation climbing-dominated processes reinforced with precipitated phases. Alloy S1 exhibits higher high-temperature creep resistance than that of Alloy S2. The grain size of Alloy S1 is smaller than that of Alloy S2. Both the precipitates Fe2Nb in Alloy S1 and Fe2W in Alloy S2 are mostly located at the grain boundary. The density of dislocation in Alloy S1 is higher than that in Alloy S2, and the bending degree of dislocation lines caused by precipitate hindrance is also higher than that in Alloy S2. The orientation relationships between the Laves phase Fe2Nb and ferritic matrix in Alloy S1 are [011]α-Fe//[5 1 ̅9 ̅4 ̅]Fe2Nb, (011 ̅)α-Fe//(03 3 ̅ 1)Fe2Nb, with the atomic interface mismatch of 1.6%; the orientation relationships between the Laves phase Fe2W and ferritic matrix in Alloy S2 are [001]α-Fe//[01 1 ̅ 2]Fe2W, (1 1 ̅ 0)α-Fe//(01 1 ̅1 ̅) Fe2W, with the atomic interface mismatch of 1.9%. The results indicate that the Fe2Nb-type Laves phase may be more suitable to candidate for the strengthener in the ferritic matrix compared with Fe2W-type.
materials science, multidisciplinary,nanoscience & nanotechnology,metallurgy & metallurgical engineering
-
Effects of Si addition on crystallization process and soft magnetic properties of high-Fe and high-Cu-content Fe-Si-B-P-Cu nanocrystalline alloys
Lei Xie,Qiang Li,Chuntao Chang,Xueru Fan,Aina He,Yuanfei Cai,Qiang Chi,Guan Zhang,Yaqiang Dong
DOI: https://doi.org/10.1016/j.jmrt.2024.05.014
IF: 6.267
2024-05-06
Journal of Materials Research and Technology
Abstract:In this study, the effects of Si content on the glass-forming ability (GFA), thermal stability, annealing window, nanocrystallization process, and soft magnetic properties (SMPs) of Fe 86.3-x Si x B 10 P 2 Cu 1.7 (x = 0, 1, 2, 3, and 4, denoted as Si0, Si1, Si2, Si3, and Si4, respectively) alloys with high Fe and Cu contents were investigated. Moderate addition of Si (x = 1, 2, and 3) enhanced the GFA and suppressed the precipitation of compound phases, thus leading to a large crystallization temperature interval ( ΔT x ) exceeding 185 °C for the alloys. Appropriate addition of Si also resulted in the formation of high-density and fine pre-existing α-Fe nanocrystals in as-spun ribbons and a high growth active energy of α-Fe crystals during the subsequent nanocrystallization process for the Si1, Si2, and Si3 alloys, enhancing competitive growth between α-Fe crystals and resulting in fine nanostructure and excellent SMPs of the nanocrystalline alloys (NAs). As a result, the Si1, Si2, and Si3 NAs obtained by annealing at 420 °C for 30 min exhibited excellent SMPs with saturation magnetic flux density ( B s ) up to 1.84 T and a low coercivity ( H c ) of approximately 10 A/m. In addition, statistical analysis of the relationship between the average grain size ( D ) of α-Fe crystals and H c values of the NAs indicated that an H c α D 3 dependence is observed when the D is less than approximately 30 nm, while this dependence follows the well-known H c α D 6 relationship when the D is above 30 nm. The dependency relationship between D and H c of NAs can guide the selection of an appropriate annealing process to optimize their SMPs.
materials science, multidisciplinary,metallurgy & metallurgical engineering
-
Mechanisms of rapid magnetocaloric enhancement of La–Fe–Co–Si alloy by high-temperature hot compression with large deformation
Ruochen Zhang,He Liu,Pengyan Mao,Cean Guo,Shaohu Tao,Mingfang Qian,Xuexi Zhang
DOI: https://doi.org/10.1016/j.intermet.2024.108359
IF: 4.075
2024-08-01
Intermetallics
Abstract:In this study, the microstructure, phase composition, magnetic transition, and magnetocaloric effect of the LaFe10.6Co0.9Si1.5 alloy hot compressed at high temperatures over 1173 K with a strain rate 0.005 s−1 and reduction ratio 50%–70 % are studied. No La(Fe, Si, Co)13 phase is formed until the hot-compression temperature is elevated to 1273 K and the reduction ratio is increased to 70 %. As a result, 86.8 ± 2 wt% 1:13 phases are rapidly obtained in the LaFe10.6Co0.9Si1.5 ingot. The whole process can be completed within only 10 min and no post-annealing process is needed. This fast formation of the La(Fe, Si, Co)13 phases is possibly induced by the directional atomic diffusion, accelerated atomic diffusion, and the stability of the La(Fe, Si, Co)13 phase and structural relaxation caused by the sufficiently restored elastic energy during the hot compression. The LaFe10.6Co0.9Si1.5 ingot hot compressed at 1273 K with a reduction ratio 70 % at a strain rate 0.005/s exhibits a second-order phase transition and negligible magnetic hysteresis. A large magnetic entropy change of 4.4 J/kg.K and a wide working temperature range of 57 K under 2 T are acquired near room temperature. This study proposes a new efficient hot compression route for processing the La–Fe–Co–Si alloy and enhancing the magnetocaloric effect.
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering