Preparation and properties of FeNiMnCuC0.2Alx high-entropy alloy
Yafeng Li,Lijun Kong,Zhanghua Gan,Zexi Yuan
DOI: https://doi.org/10.3969/j.issn.1674-3644.2009.01.014
2009-01-01
Abstract:The FeNiMnCuC0.2Alx(x=0,0.1,0.2,0.5 mol) high-entropy alloy were prepared by high-frequency induction melting under vacuum condition,and the ingots were processed by solid-solution treatment.According to X-ray diffraction results,the FeNiMnCuC0.2Alx high-entropy alloy has simple fcc structure.Compressive properties of the alloy were tested by WAW-3100 testing machine.It is found that the FeNiMnCuC0.2 high-entropy alloy has high compressive strength,which reaches 5 218 MPa.With the increase of Al content,the compressive strength of the alloy decreases,When x=0.1 mol,a good combination of compressive strength and plastic strain is obtained,which are 4 037 MPa and more than 75%,respectively.When the content of Al reaches x=0.5 mol,the alloy exhibits brittle fracture.The results of microstructure and EDS show that the addition of a small amount of Al(x=0.1,0.2 mol) can make FeNiMnCuC0.2Alx grains finer;while x=0.5 mol,primary dendrite grains grow.EDS finds dendritic segregation area to be Fe,Ni rich,while interdendritic segregation area is found to be Mn,Cu rich.The distribution of C,Al is almost identical.