Abstract:Electroblowing and sol–gel reaction were combined to prepare mesoporous silica fibers. Poly(methyl methacrylate) (PMMA), a simple commercial polymer with weak hydrogen bonding to silica, was demonstrated to be valuable in improving the electrospinnability and as a porogenic agent. Compared with that in electrospinning, the jet stream in electroblowing was more stable and the resultant fibers were more uniform. The electroblown fibers were characterized by infrared spectroscopy, thermogravimetric analysis, scanning electron microscopy, transmission electron microscopy and nitrogen adsorption and desorption isotherms. The phase separation behavior and mechanism for the formation of the amorphous mesoporous structure were discussed. Although there was no covalent bonding between PMMA and silica, macrophase separation was completely prevented in the electroblown fibers and the pore size in the calcined silica fibers ranged from 10 to 20nm. However, the previously reported electrospun silica fibers, in which surfactants or polymers with strong hydrogen or covalent bonding to silanol groups were used as structure directing agents, had average pore sizes below 10nm. The present study offers a facile method for the preparation of highly mesoporous silica fibers with large mesopores.

Gram-scale Synthesis of Submicrometer-Long Polythiophene Wires in Mesoporous Silica Matrices.

Synthese von molekularen submikrometerlangen Polythiophen-Drähten im Gramm-Maßstab in mesoporösen Silicat-Matrices

Mesoporous Silica Fibers Prepared by Electroblowing of A Poly(Methyl Methacrylate)/Tetraethoxysilane Mixture in N,N-Dimethylformamide

Direct Synthesis of Mesoporous Carbon Microwires and Nanowires

Tiny SiO2 nano-wires synthesized on Si (1 1 1 ) wafer

Porphyrin-Acetylene-Thiophene Polymer Wires

Superlong Polypyrrole Nanowires Aligned Within Ordered Mesoporous Silica Channels

Tiny SiO2 nano-wires synthesized on Si (111) wafer

Ultra‐Long Single‐Crystalline Α‐si3n4nanowires: Derived from a Polymeric Precursor

Single Microwire Transistors Of Oligoarenes By Direct Solution Process

Electron Transport Investigation of Thiophene Oligomers Based Molecular Wires

Atomic study of molecular wires composed of thiophene oligomers

Synthesis of angstrom-scale anatase titania atomic wires.

Large-scale Synthesis of Ultra-Long Wire-Like Single-Crystal Selenium Arrays

First sub-kilogram-scale synthesis of high quality ultrathin tellurium nanowires

Fabrication and Characterization of Silica Nanotubes with Controlled Dimensions

Theoretical Study on the Self-Assembly of 1,3,5-Triethynylbenzene on Si(100)2 × 1 and in Situ Polymerization Via Reaction with CO to Fabricate a Single Surface-Grafted Polymer

Controllable Self‐Assembly of N‐type Semiconductors to Microtubes and Highly Conductive Ultralong Microwires

Nanowires Formed by the Co-Assembly of A Negatively Charged Low-Molecular Weight Gelator and A Zwitterionic Polythiophene

Polyol method synthesis and characterization of nanoscale Sb2Se3 wires

High-Yield Synthesis of Superhydrophilic Polypyrrole Nanowire Networks