Phase Behavior of Salt-Free Catanionic Surfactant Aqueous Solutions with Fullerene C-60 Solubilized

Hongguang Li,Jingcheng Hao
DOI: https://doi.org/10.1021/jp071332u
2007-01-01
Abstract:A salt-free catanionic surfactant system, tetradecyltrimethylammonium laurate (TTAL), was constructed by mixing tetradecyltrimethylammonium hydroxide (TTAOH) and lauric acid (LA). The H+ and OH- counterions form water (TTAOH + LA -> TTAL + H2O), leaving the solution salt-free. The phase behaviors at fixing the total surfactant concentration (c(TTAL)) to be 33.0 and 55.0 mmol L-1, respectively, were studied through varying the molar ratio of r = n(LA)/n(TTAOH) from 0.70 to 1.20. With an increasing value of r, one observed an L-1-region, an L-alpha/L-1 two-phase region with a birefringent L-alpha-phase at the top, and finally a single L-alpha-phase. The ability to solubilize a fullerene mixture of C-60 and C-70 of different phases in different regions was tested. The colloidal stability and phase behavior of different phases with embedded fullerenes were investigated as a function of r, c(TTAL), and weight ratio of fullerene to surfactant (W-F/W-TTAL). The 33.0 or 55.0 mmol L-1 zero-charged vesicle-phase at r = 1.00 could solubilize a considerable amount of fullerenes without macroscopic phase separation and obvious vesicular structure breakage. However, these colloidal solutions became unstable at lower concentrations of surfactants, and a precipitate would be observed at the bottom. The micellar (L-1-phase) solubilization at the TTAOH-rich side was less pronounced compared to the vesicular solubilization of the zero-charged vesicle-phase, and the solubilizing ability decreased at higher r values. In the L-alpha/L-1 two-phase region, a brown or dark-brown L-alpha-phase was usually found at the top of a colorless or yellowish L-1-phase, indicating that most of the fullerenes were embedded in the upper L-alpha-phase. The influence of fullerene incorporation on the property of the zero-charged TTAL vesicle-phase was also investigated, and evidence has been found that the system tended to be more fluid after fullerenes were incorporated into the hydrophobic microdomains of aggregates.
What problem does this paper attempt to address?