Preparation and Magnetism of Carbon Encapsulated Fe and Ni Nano Particles

ZHAO Jun,ZHOU Wei-Liang,XU Fu-Ming
2007-01-01
Abstract:Carbon encapsulated Fe and Ni nano particles were respectively prepared by pyrolysis of Fe and Ni-loaded cation exchange resin(Fe-Ni/D113) at 400 ℃,500 ℃,600 ℃ and 700 ℃.TG results show that the thermal stability of Fe-Ni/D113 was better than that of pure D113 resin.X-ray diffraction(XRD) and transmission electron microscopy(TEM) results show that the nano particle size increased with the pyrolysis temperature.Magnetic test result shows that the pyrolyzate obtained at 400 ℃ was superparamagnetic.The coercivities(Hc) at room temperature of the pyrolyzates obtained at 500 ℃,600 ℃,and 700 ℃ were much higher than that of the corresponding bulk materials,and the Hc value was influenced by the size of the nano particles.The saturation magnetizations(Ms) of all the pyrolyzates were lower than that of the corresponding bulk materials and increased with the pyrolysis temperature.