Proliferation and differentiation of preosteoblast MC3T3-E1 cells on titanium coated with gradient TiO2

L Zhu,YD Gong,NM Zhao,XF Zhang

DOI: https://doi.org/10.3321/j.issn:1673-8225.2007.44.003

2007-01-01

Abstract:AIM: To assess the bioactivity of titanium modified with gradient TiO2 coating by the study of the attachment, proliferation, morphology and differentiation of preosteoblast MC3T3-E1 cell cultured on it. METHODS: The experiments were completed in the State Key Laboratory of Biomembrane and Membrane Biotechnology, Tsinghua University from March to December in 2006.①The titanium was selected as substrate and a structural gradient TiO2 coating was produced by hybrid oxidation techniques. A dense oxide film as the inner layer was produced by anodic oxidation and a porous oxide film as the outer layer was produced by micro-arc oxidation.②The preosteoblast MC3T3-E1 cells were cultured on the titanium modified with the gradient coating. The untreated titanium and titanium coated with only an oxide film were used as controls.③After 3 and 6 hours of seeding, the attachment of MC3T3-E1 cells was determined by methyl thiazolyl tetrazolium (MTT) assay. After 3 days of culture, the morphology of cell growing on all specimens was observed by scanning electron microscope. After cell culturing for 7, 14 and 21 days, the proliferation of MC3T3-E1 cells was determined by MTT assay. The MC3T3-E1 cells on three specimens were cultured in inducing culture medium. After 28 days, the alkaline phosphatase (ALP) activity of cells cultured on all specimens was evaluated to assess the differentiation of cells to osteoblasts. RESULTS: ①After 3 hours of seeding, MC3T3-E1 cells had attached to all the specimens, while those controls were less attached. And there were more cells attached on the gradient coating after 6 hours of seeding, which was 1.5 times of the value for untreated titanium.②After 3 days of culture, the MC3T3-E1 cells grew well on the surface of all the specimens. Morphology of the cells on all the specimens was identical to be characteristics of normal MC3T3-E1 cells.③The number of cells on all the specimens increased with time. The cells of gradient coating were the most among all the specimens, whereas those of untreated titanium were the least. Although the number of cells cultured on gradient coating was a little more than the others on day 7, a statistically significant increase (4 times) in proliferation was measured for MC3T3-E1 cells on gradient coating than on the others after 21 days of culture.④After 28 days of culture in inducing medium, the ALP activity of MC3T3-E1 cells on the gradient coating was significantly increased, which was approximately 1 time more than that of untreated titanium. CONCLUSION: The attachment, proliferation and differentiation of preosteoblast MC3T3-E1 cells cultured on the gradient coating are the best of all specimens, which indicates that this gradient TiO2 coating can provide the titanium with good biocompatibility and bioactivity compared with untreated titanium or titanium coated with only an oxide film.