Abstract:The effects of the area reductions on the crystal orientation, eccentricity, and mechanical properties of GH4145 alloy tubes prepared by three-roller cold rolling were studied. Electron backscattered diffraction analysis showed that the equiaxed grains of the annealed tube blank gradually changed into elongated crystals along the axial direction (AD) with increased deformation. In addition, the grain orientations rotated from random distribution towards the <101>//radial direction (RD), <111>//AD, and <101> + <111>//tangential direction (TD). Brass, copper, S, and {123}< 111‾ > textures formed and increased in strength with increasing strain. Room-temperature tensile tests loaded along the AD and TD demonstrated yielding anisotropy of the tubes. With increasing strain, the work hardening increased continuously, and the dislocations slipped in three directions and then transformed into slip bands and dislocation cells, whereas a few deformation twins formed as the reduction reached 64%, and then slipped in two directions. When the reduction was 64%, the activated slip system transformed from {111}<110> to {110}<001> in most grains under applied AD loading, which was consistent with the loading in both directions at a reduction of 72%. As the grains in the preferential deformation zone near the inner and outer walls rotated to the <101>//RD orientation, the tubes plastically deformed, and the grains in the central layer then gradually begin to rotate. The ratio of radial length in the deformation hysteresis zone to wall thickness was used to represent the degree of non-uniformity of the deformation. A direct correlation was found between the eccentricity of the wall thickness and the non-uniformity of tube deformation as the area reduction increased from 13% to 50%. In addition, the radial delamination of the tubes disappeared, deformation became uniform, and the eccentricity decreased significantly as the area reduction increase up to 64%. Therefore, the dimensional accuracy and uniformity of the tubes can be further improved by controlling the strain of the tube.

Effect of forming parameters on the neck-spinning process of 3D non-axisymmetric tubes

Influence of Inner Roller Geometric Parameters on Counter-Roller Spinning with 6061 Aluminum Alloy Tube

Spinning Process of 2219 Aluminum Alloy Tubes for Used in Hydroforming

Plasticity Improvement of Ball-Spun Magnesium Alloy Tube Based on Stress Triaxiality

Effects of Forming Parameters on Deformation Uniformity of Thin-walled Parts during Multi-pass Spinning

Study of Dieless Radial Spinning for Thick-Walled Cylindrical Parts With External Grooves

Study on the spinning process of thin-walled aluminum alloy vessel head

Effect of Cold Rolling Degree on Texture Evolution, Eccentricity, and Yielding Anisotropy of GH4145 Alloy Tubes

Analysis of ball spinning formability of thin-walled tubular parts of aluminum alloy

Study of Deformation Mechanism of Backward Ball Spinning of Thin-Walled Tube with Longitudinal Inner Ribs

Mechanism of Increasing Spinnability by Multi-Pass Spinning Forming – Analysis of Damage Evolution Using a Modified GTN Model

Research on forming properties of 7075 aluminum alloy tubes by power staggered spinning

Study on Spinning Process of A Thin-Walled Aluminum Alloy Vessel Head with Small Ratio of Thickness to Diameter

Process factors influencing spinning deformation of thin-walled tubular part with longitudinal inner ribs

Influence of process parameters on the flow forming quality of thin-walled tube with large diameter-thickness ratio

The Rollers' Offset Position Influence on the Counter-Roller Flow-Forming Process

FEM Simulation of Tube Spinning with Non-Symmetric Distribution of Three Rollers

Experimental and Numerical Investigation on Axial Hydro-Forging Sequence of 6063 Aluminum Alloy Tube

Numerical simulation and experimental study on non-axisymmetric spinning with a groove at the middle of the tube

A Systematic Study on the Effects of Process Parameters on Spinning of Thin-Walled Curved Surface Parts With 2195 Al-Li Alloy Tailor Welded Blanks Produced by FSW

Axial Hydro-Forging Sequence for Variable-Diameter Tube of 6063 Aluminum Alloy