Abstract:Background/Objectives: Magnetic Fe3O4 nanoparticles (MNPs) are becoming more important every day. We prepared MNPs in a simple one-step reaction by following the solvothermal method, assisted by azide and alkyne functionalized polyethylene glycol (PEG400) polymers, as well as by PEG6000 and the polyol β-cyclodextrin (βCD), which played a crucial role as electrostatic stabilizers, providing polymeric/polyol coatings around the magnetic cores. Methods: The composition, morphology, and magnetic properties of the nanospheres were analyzed using Transmission Electron and Atomic Force Microscopies (TEM, AFM), Nuclear Magnetic Resonance (NMR), X-ray Diffraction Diffractometry (XRD), Fourier-Transform Infrared Spectroscopy (FT-IR), Matrix-Assisted Laser Desorption/Ionization (MALDI) and Vibrating Sample Magnetometry (VSM). Results: The obtained nanoparticles (@Fe3O4-PEGs and @Fe3O4-βCD) showed diameters between 90 and 250 nm, depending on the polymer used and the Fe3O4·6H2O precursor concentration, typically, 0.13 M at 200 °C and 24 h of reaction. MNPs exhibited superparamagnetism with high saturation mass magnetization at room temperature, reaching values of 59.9 emu/g (@Fe3O4-PEG6000), and no ferromagnetism. Likewise, they showed temperature elevation after applying an alternating magnetic field (AMF), obtaining Specific Absorption Rate (SAR) values of up to 51.87 ± 2.23 W/g for @Fe3O4-PEG6000. Additionally, the formed systems are susceptible to click chemistry, as was demonstrated in the case of the cannabidiol-propargyl derivative (CBD-Pro), which was synthesized and covalently attached to the azide functionalized surface of @Fe3O4-PEG400-N3. Prepared MNPs are highly dispersible in water, PBS, and citrate buffer, remaining in suspension for over 2 weeks, and non-toxic in the T84 human colon cancer cell line, Conclusions: indicating that they are ideal candidates for biomedical applications.

Magnetic nanoparticles encapsulated latexes prepared with photo-initiated miniemulsion polymerization

Preparation of magnetic polystyrene latex via the miniemulsion polymerization technique

Preparation of Magnetic Polymeric Particles Via Inverse Microemulsion Polymerization Process

Preparation of Polymer–nanoparticle Composite Beads by a Nanoparticle-Stabilised Suspension Polymerisation

Synthesis of Monodisperse, Magnetic Latex Particles with Polystyrene Core

Controllable preparation of high-yield magnetic polymer latex.

Controllable Preparation of Magnetic Polymer Nanospheres with High Saturation Magnetization by Miniemulsion Polymerization

Controllable preparation of magnetic polymer microspheres with different morphologies by miniemulsion polymerization.

Direct Synthesis of Hydrophilic Nancoscale Magnetic Polymer Particles in Inverse Microemulsion

Mini-Emulsification and Mini-Emulsion Polymerization of Methyl Methacrylate/Nanosilica Dipsersion

A Facile Method to Synthesize Magnetic Polymer Nanospheres with Multifunctional Groups

Miniemulsion-based assembly of iron oxide nanoparticles and synthesis of magnetic polymer nanospheres

Preparation of Hybrid Polymer Nanocomposite Microparticles by a Nanoparticle Stabilised Dispersion Polymerisation

Developing A Hybrid Emulsion Polymerization System to Synthesize Fe3o4/Polystyrene Latexes with Narrow Size Distribution and High Magnetite Content

Preparation and Characterization of Micron‐sized Magnetic Microspheres by One‐step Suspension Polymerization

Magnetic Nanoparticles with On-Site Azide and Alkyne Functionalized Polymer Coating in a Single Step through a Solvothermal Process

Facile Synthesis of Magnetic Microcapsules by Synchronous Formation of Magnetite Nanoparticles

Preparation of Magnetic Hybrid Nanoparticles via Surface-Initiated Polymerization from Magnetite

Fabrication and Characterization of Thermo-Sensitive Magnetic Polymer Composite Nanoparticles

Study on ultrasonic induced encapsulating emulsion polymerization in the presence of nanoparticles

One-pot fabrication of magnetic nanocomposite microcapsules