Preparation and application of microporous silica membranes

LI Tiansheng,YANG Jianhua,XIAO Wei,SHEN Dong,ZHOU Liang,LU Jinming,YIN Dehong,ZHANG Yan,WANG Jinqu

DOI: https://doi.org/10.3969/j.issn.1007-8924.2011.04.010

2011-01-01

Abstract:Amorphous microporous silica membranes with high flux were prepared by the non-traditional sol-gel and hot-coating method.And dehydration pervaporation of acetic acid was used to evaluate the separation performance of SiO2 membranes.Particle size analyzer and SEM were used to characterize the sols and selective membranes.The results show that the diameter of particles in the sols were 10~80 nm.The amorphous microporous silica membranes coated by hot-coating,show excellent separation performance and an approximate selectivity of water over acetic acid of 120 with the solution flux of 0.65 kg/(m2·h).The pervaportation was carried out at 353 K,and the feed of water and acetic acid were maintained at a mass fraction of 5% and 95%,respectively.After 35 h test,the separation factor increased to around 160,and the flux was maintained at 0.60 kg/(m2·h).