Preparation of ultra-pure ammonium metavanadate via heterogeneous self-assembly crystallization
Pingting Chen,Kunpeng He,Biao Yuan,Shuyuan Liu,Jian He,Pan Wu,Changjun Liu,Wei Jiang
DOI: https://doi.org/10.1016/j.colsurfa.2023.131461
2023-04-16
Abstract:Although the demand for ultra-pure V 2 O 5 in industry is significant, the current technologies used to obtain the principal precursor, ammonium metavanadate, in high purity are costly and low-yielding. In this study, a cost-efficient and high-yielding heterogeneous self-assembly crystallization (HSC) process is proposed for obtaining large, high-purity NH 4 VO 3 crystals. The method entails establishing a wide crystallization window, controlling the NH 3 mass transfer rate and buffering the pH of the mother liquor with CO 2 released during the pyrolysis of the ammonia source, (NH 4 ) 2 CO 3 to achieve the separation of chromium impurities, the most difficult-to-remove impurities in vanadium products, from the chromium-containing NaVO 3 solution, and purification of NH 4 VO 3 via reactive crystallization. Under the optimized crystallization conditions, namely an N/V mass ratio of 3.9, temperature of 60 °C, and pH of 12.5, the yield and purity of the obtained NH 4 VO 3 in 20 g·L -1 V(V) simulated solution containing 0.05 g·L -1 Cr(VI) reached 93.09% and 99.99%, respectively, and the obtained NH 4 VO 3 crystals were as large as 1.8 mm in size. In the case of a real leaching solution, the NH 4 VO 3 yield and purity were higher than 80% and 99.99%, respectively, and the purity of final V 2 O 5 reached 99.99%. The curbed pyrolysis rate of (NH 4 ) 2 CO 3 ensures heterogeneous nucleation and slow growth of NH 4 VO 3 crystals to acquire large and pure crystals, and the excessive adsorption of Cr(VI) onto the crystal surface during self-assembly is avoided at the appropriate pH, thus guaranteeing efficient precipitation, crystallization, and purification. This study provides a reference strategy for the low-cost preparation to obtain high-purity V 2 O 5.
chemistry, physical