Abstract:Although the demand for ultra-pure V 2 O 5 in industry is significant, the current technologies used to obtain the principal precursor, ammonium metavanadate, in high purity are costly and low-yielding. In this study, a cost-efficient and high-yielding heterogeneous self-assembly crystallization (HSC) process is proposed for obtaining large, high-purity NH 4 VO 3 crystals. The method entails establishing a wide crystallization window, controlling the NH 3 mass transfer rate and buffering the pH of the mother liquor with CO 2 released during the pyrolysis of the ammonia source, (NH 4 ) 2 CO 3 to achieve the separation of chromium impurities, the most difficult-to-remove impurities in vanadium products, from the chromium-containing NaVO 3 solution, and purification of NH 4 VO 3 via reactive crystallization. Under the optimized crystallization conditions, namely an N/V mass ratio of 3.9, temperature of 60 °C, and pH of 12.5, the yield and purity of the obtained NH 4 VO 3 in 20 g·L -1 V(V) simulated solution containing 0.05 g·L -1 Cr(VI) reached 93.09% and 99.99%, respectively, and the obtained NH 4 VO 3 crystals were as large as 1.8 mm in size. In the case of a real leaching solution, the NH 4 VO 3 yield and purity were higher than 80% and 99.99%, respectively, and the purity of final V 2 O 5 reached 99.99%. The curbed pyrolysis rate of (NH 4 ) 2 CO 3 ensures heterogeneous nucleation and slow growth of NH 4 VO 3 crystals to acquire large and pure crystals, and the excessive adsorption of Cr(VI) onto the crystal surface during self-assembly is avoided at the appropriate pH, thus guaranteeing efficient precipitation, crystallization, and purification. This study provides a reference strategy for the low-cost preparation to obtain high-purity V 2 O 5.

Study on agglomeration mechanism of ammonium paratungstate pentahydrate and controllable preparation of pure monodisperse crystals

Process optimization and crystallization kinetics of ammonium sulfate from wet ammonia‐based desulfurization

Study on Preparation of Size-Controllable Spherical Ag Powders with High Tap Density

Optimizing Technical Conditions in Super-high Pure APT Preparation Process by Double-ion-exchange and Saturation Adsorption Technology

Solventing out crystallization-basic magnesium carbonate percipitation for thorough phosphorus removal from ammonium tungstate solution

Prevention of Crystal Agglomeration: Mechanisms, Factors, and Impact of Additives

Preparation and characterization of ultra-fine ammonium perchlorate crystals using a microfluidic system combined with ultrasonication

Enhanced Thermal Stability and High-Quality of Α-Alh3 Via Crystal Seed Preparation Method

Study on Fabrication of Spherical Tungsten Powder by Spray-Drying and Reduction Process

A Novel Process to Prepare Ammonium Polyphosphate with Crystalline Form Ii and Its Comparison with Melamine Polyphosphate

Experimental and theoretical investigation on the mechanism of cationic surfactants-assisted phosphogypsum crystal transformation

Molecular engineering of microporous crystals: (III) The influence of water content on the crystallization of microporous aluminophosphate AlPO4-11

Application of surfactant in the preparation of ultrafine TATB

Preparation and performance of superhydrophobic surfaces with low surface energy modified attapulgite

Controllable synthesis and characterization of ammonium polyphosphate with crystalline form V by phosphoric acid process

Ammonium Polyphosphate with Crystalline Form V by Ammonium Dihydrogen Phosphate Process

Preparation and adsorption of Cd2+ of attapulgite modified by AMPS

Molecular engineering of microporous crystals: (IV) Crystallization process of microporous aluminophosphate AlPO 4-11

Phase Formation and Free Agglomeration of the PZT Perovskite Powders Prepared via Precipitation Route: Effects of PVA

Preparation and crystallization control of nanoparticle hydroxyapatite

Preparation of ultra-pure ammonium metavanadate via heterogeneous self-assembly crystallization