Abstract:A series of mesoporous molecular sieve samples have been synthesized hydrothermally by using cetyltrimethylammonium bromide (CTAB) as a template, tetraethyl orthosilicate (TEOS) as a silica source, tetramethyl ammonium hydroxide as a base source and water as a solvent. The samples were prepared by adding required amount of surfactant, TEOS, water and TMAOH to maintain pH, then the obtained mixture was stirred for 10 min. and then transferred into autoclave. pH of the gel was adjusted to 10. The molar ratio of surfactant (CTAB) and TEOS was kept at 0.11:0.48, 0.165:0.48, 0.22:0.48 and 0.274:0.48 for samples A-I, A-II, A-III and A-IV respectively, while the aging time was kept 4 days and temperature remained constant at 393 K. The as-synthesized samples were thoroughly washed with distilled water and then dried at 373 K for 24 h. The as-synthesized samples were calcined at 723 K for 6 h in air. The as synthesized samples were characterized for its morphology using Field Emission Scanning Electron Microscopy (FESEM), elemental analysis by using Energy Dispersive X-Ray (EDX), thermal stability by using Thermogravimetric Analysis (TGA), the functional groups within the samples before and after calcination was analyzed using Fourier Transform Infrared Spectroscopy (FTIR). Formation of the mesoporous material depends on the surfactant, which act as a structure directing agent. Micelles of the surfactant arrange themselves and interact with the silicate ions to form the mesoporous material. In this study, the effect of concentration was studied on the synthesis and found that due to increase in concentration of surfactant, more silica polymerized and formation of material increases.

Fluoride-Induced Reduction of CTAB Template Amount for the Formation of MCM-48 Mesoporous Molecular Sieve

Sio2-Template Synthesis of Mesoporous Mgf2 Highly Effective for Cl/F Exchange Reaction

Influences of anions X-(F-, Cl-, Br-) on synthesis and properties of mesoporous molecular sieve MCM -41

Effects of CTAB on Porous Silica Templated by Chitosan

The Synthesis of Mesoporous Molecular Sieve MCM-48

Sodium lignosulfonate as sacrificial agent and effectiveness in reducing CTAB cationic adsorption onto kaolinite

Ordering improvement of mesoporous silica materials templated from semi-fluorinated nonionic surfactants by introduction of organic additives

Experimental and DFT study of F- removed by Cl--hydrotalcite

Synthesis of Structurally Stable Mcm-48 Using Mixed Surfactants As Co-Template and Adsorption of Vitamin B12 on the Mesoporous Mcm-48

Controlled Synthesis of Mesoporous Silicas Mcm-48 and Mcm-41 by Using Mixed Templates

Effect of Surfactant Concentration on the Physico-chemical Characteristics of Mesoporous Molecular Sieve

A Reliable Synthesis of Cubic Mesoporous MCM-48 Molecular Sieve

One-step controllable strategy for synthesizing hierarchical Fe-MFI/MCM-41 composites using CTAB as a dual-functional template

Preparation of MCM-41 with high thermal stability and complementary textural porosity

Design and Synthesis of Ordered Mesoporous Silica Materials with High Degree of Silica Condensation at High Temperature from a Mixture of Polymer Surfactant with Small Organic Ammonium.

Semi-fluorinated Surfactant Syntheses of Ordered Porous Materials with Tailorable Pore Sizes

Study of under Etching Characters of Si (100) in Surfactant Added Tmah

Defluoridation of Drinking Water by Mg/Al Hydrotalcite-Like Compounds and Their Calcined Products

SYNTHESIS OF MESOPOROUS MOLECULAR SIEVES WITH SECONDARY BUILDING UNITS OF β ZEOLITE AT LOW SURFACTANT CONCENTRATION

Molecular Scale Assessment of Defluoridation of Coal-Mining Wastewater by Calcined Mg/Al Layered Double Hydroxide Using 19F Solid-State NMR, XPS, and HRTEM.

Preparation of La(III), Fe(III) Modified Zeolite Molecular Sieves for the Removal of Fluorine from Water