Fabrication of periodic microscale stripes of silver by laser interference induced forward transfer and their SERS properties
Huijuan Shen,Yaode Wang,Liang Cao,Ying Xie,Lu Wang,Xueying Chu,Kaixi Shi,Shenzhi Wang,Miaomiao Yu,Ri Liu,Jingran Zhang,Changli Li,Zhankun Weng,Zuobin Wang
DOI: https://doi.org/10.1088/1361-6528/ac3e34
IF: 3.5
2021-12-23
Nanotechnology
Abstract:Abstract The micro-stripe structure was prepared by laser interference induced forward transfer technique, composed of Ag nano-particles (NPs). The effects of the film thickness with the carbon nano-particles mixed polyimide (CNPs@PI), Ag film thickness, and laser fluence were studied on the transferred micro-stripe structure. The periodic Ag micro-stripe with good resolution was obtained in a wide range of CNPs@PI film thickness from ∼0.5 to ∼1.0 μ m for the Ag thin film ∼20 nm. The distribution of the Ag NPs composing the micro-stripe was compact. Nevertheless, the average size of the transferred Ag NPs was increased from ∼41 to ∼197 nm with the change of the Ag donor film from ∼10 to ∼40 nm. With the increase of the laser fluence from 102 to 306 mJ·cm −2 per-beam, the transferred Ag NPs became aggregative, improving the resolution of the corresponding micro-stripe. Finally, the transferred Ag micro-stripe exhibited the significant surface enhanced Raman scattering (SERS) property for rhodamine B (RhB). While the concentration of the RhB reached 10 –10 mol·L −1 , the Raman characteristic peaks of the RhB were still observed clearly at 622, 1359 and 1649 cm −1 . These results indicate that the transferred Ag micro-stripe has potential application as a SERS chip in drug and food detection.
materials science, multidisciplinary,physics, applied,nanoscience & nanotechnology