Microstructures and Mechanical Properties of Ti–24Al–17Nb (at.%) Laser Beam Welding Joints

AP Wu,GS Zou,JL Ren,HJ Zhang,GQ Wang,X Liu,MR Xie
DOI: https://doi.org/10.1016/s0966-9795(02)00049-3
IF: 4.075
2002-01-01
Intermetallics
Abstract:Laser beam welding of Ti–24Al–17Nb (at.%) alloy was conducted to investigate the microstructures and the mechanical properties of its joints. The results indicated that the weld microstructure consisted primarily of retained ordered β phase (namely B2 phase) and was independent of the laser welding parameters, while the size and the orientation of the weld solidification structures and then the bend ductility of the joints were related to the welding conditions. The microstructures became coarser and the strains of inducing crack and fracturing decreased as the heat input increased. The fracture occurred in the base metal when the transverse tensile test of the joints was conducted. The tensile strength of the joints was equal to that of the base material and the tensile ductility could reach 12∼17%, which was near to that of the base material.
What problem does this paper attempt to address?