Relationship Between Mechanical Properties and Crystalline Structure of PPR/iPP Blends Modified with β-Nucleator
Ya-ming Zhu,Shu-mei Liu,Wen-zhen Jiang,Yan-hui Zhou,Jian-qing Zhao
DOI: https://doi.org/10.3969/j.issn.1000-565X.2011.06.014
2011-01-01
Abstract:In this paper, the relationship between the mechanical properties and the crystalline structure of propylene random copolymer (PPR)/isotactic polypropylene (iPP) blends modified by a rare earth complex (β-nucleator) was investigated by means of DSC and XRD. When the dosage of β-nucleator is kept at 0.05%, it is found that (1) the impact strengths of PPR, PPR/iPP(70/30, 50/50 and 30/70 in mass ratio, respectively) blends and iPP increase from 42.7, 33.7, 14.5, 8.3 and 5.1 kJ/m 2 to 87.8, 63.4, 29.3, 13.9 and 8.2 kJ/m 2, respectively, while the tensile strengths all decrease by less than 10%; (2) the melting temperature of PPR/iPP (70/30 in mass ratio) blend decreases from 161.9°C to 149.8°C and the relative content of β-form crystal increases from 45.3% to 53.1%, which reveals a remarkable nucleating promotion to β-form crystal; and (3) there exist typical ductile fractures in the impact-fractured sections of the blend, which is verified by the SEM photographs. More-over, when the dosage of β-nucleator increases to 0.20%, the melting temperature of the blend and the relative content of β-form crystal respectively reach 159.8°C and 45.1%, and the nucleation to β-form crystal of the blend weakens, thus resulting in a decrease in the impact toughness.