Abstract:Bismuth tungstate (Bi2WO6) nanocrystals with the average size of ca. 12 nm had been successfully synthesized by a simple solvothermal method at 180 degrees C for 2 h. The as-synthesized Bi2WO6 nanocrystals were characterized by X-ray diffraction, scanning electron microscopy, transmission electron microscopy, UV-vis diffuse reflectance spectra. and N-2 adsorption-desorption measurements. The visible-light-driven photocatalytic activity of the sample was evaluated by photo-degradation of rhodamine-B (RhB) at room temperature, which is much higher than that of the hydrothermal synthesized Bi2WO6 square plates and the commercially available TiO2 (P-25). We believed that the high photocatalytic activity could be ascribed to the intrinsically small grain size and high surface-to-volume ratio associated with the Bi2WO6 nanocrystals. (C) 2009 Elsevier B.V. All rights reserved.

Preparation and Characterization, of Single-Crystalline Bismuth Nanowires by A Low-Temperature Solvothermal Process

Synthesis and Characterization of Bismuth Single-Crystalline Nanowires and Nanospheres

Preparation And Characterization Of Bismuth Sulfide Single Crystal Nanorods In Ionic Liquids

Long Bi2s3 Nanowires Prepared by A Simple Hydrothermal Method

Formation of Uniform Single-Crystalline Bismuth Sulfide Nanowires under Mixed-Solvent Condition

Formation of uniform single-crystalline bismuth sulfide nanowires under mixed-solvent condition.

Novel bismuth nanotube arrays synthesized by solvothermal method

A RAPID PREPARATION OF BISMUTH NANOWIRES VIA A MICROWAVE-ASSISTED POLYOL METHOD

Large-scale Polyol Synthesis of Single-Crystal Bismuth Nanowires and the Role of NaOH in the Synthesis Process

Low-temperature Synthesis and Growth Mechanism of Uniform Nanorods of Bismuth Sulfide

Synthesis and characterization well-aligned bismuth ferrite nanowires using hydrothermal method

Synthesis of single-crystalline bismuth nanobelts and nanosheets

Solvothermal Growth Of Single-Crystal Bismuth Sulfide Nanorods Using Bismuth Particles As Source Material

Low Temperature Growth of Bismuth Sulfide Nanorods by a Hydrothermal Method

Solvothermal Preparation of Bi2wo6 Nanocrystals with Improved Visible Light Photocatalytic Activity

Solvothermal synthesis of antimony nanowire bundles, tube-groove-like nanostructures and dendrites

Solvothermal Route to Semiconductor Nanowires

Synthesis Of Bismuth Nanorod Via Thermal Process

Solvothermal preparations of nanocrystalline Bi 2 Te 3 powders and the study on their characterizations

Synthesis and Characterization of Nanocrystalline Bi2Se3 by Solvothermal Method

Synthesis and characterization of nanocrystalline NiSb and NiSb2 at low temperature