Abstract:The study mainly investigates the effect of strain ratio on the multiaxial low cycle fatigue behaviour of 316L at 550 °C. The evolution of both axial and torsional stress amplitude is observed to go through three stages: cyclic hardening, softening and fracture. What's different is that the torsional loading experiences fewer cyclic hardening cycles compared to the axial loading. Regarding the interaction between axial and torsional stresses, it is observed that as the torsional strain increases, the axial deformation response presents a lower peak stress and a higher softening rate, while the torsional peak stress and softening rate hardly changes with the increase of axial strain amplitude. The fracture pattern is obtained through three-dimensional (3D) depth-of-field observation. It is discovered that as the strain ratio increases, the fracture pattern transits from tensile failure mode to shear failure mode. Furthermore, the orientation angle of the fracture surface increases and lies between the critical plane angle of maximum shear strain and maximum normal strain, indicating a mixed failure mode. Additionally, a comparison of nine representative critical plane models reveals that the energy-based models can better predict the multiaxial fatigue life influenced by the strain ratio. Finally, based on the analysis of deformation and failure mechanisms, a normal damage parameter weakening factor (NDWF) is introduced into the KBM-R model, and an improved normal stress component (INSC) is introduced into the Wu-R model. The two modified models well capture the impact of strain ratio and accurately predict the multiaxial fatigue life of both 316L and P92 steel.

Mixed mode fatigue behavior under inclined loading conditions for an austenitic 304L steel

Determination of fatigue mesoscopic mechanical properties of an austenitic stainless steel using depth-sensing indentation (DSI) technique

Variation In Mechanical Properties, Microstructures And Fracture Behavior Of 304 Stainless Steel During Low-Cycle Fatigue

Effects of low-cycle fatigue on static mechanical properties, microstructures and fracture behavior of 304 stainless steel

The low-cycle fatigue, deformation and final fracture behaviour of an austenitic stainless steel

Investigation of fatigue mechanical properties of apolycrystalline solid at mesoscopic scale using depth-sensing indentation (DSI) technique

Mesoscopic mechanical properties of 18Cr-8Ni austenitic steel subjected to low-cycle fatigue loading

Depth-Sensing Indentation-Based Studies of Surface Mechanical Behavior and Fatigue Damage Evolution of an Austenitic Stainless Steel Subjected to Cyclic Straining

Multi-scale Deformation Behavior Investigation of 18cr–8ni Austenitic Steel Subjected to Low-Cycle Fatigue Loading

A Study of the Back Stress and the Friction Stress Behaviors of Ti-6Al-4V Alloy During Low Cycle Fatigue at Room Temperature

Characterization of Low Cycle Fatigue Performance of New Ferritic P92 Steel at High Temperature: Effect of Strain Amplitude

Two-Parameter Characterization of Low Cycle, Hysteretic Fatigue Data

Modeling of Low Cycle Behavior of P92 Steel Based on Cyclic Plasticity Constitutive Equations

Characterization of Low Cycle Fatigue of Ferritic–Martensitic P92 Steel: Effect of Temperature

Low Cycle Fatigue Behavior of Original Ferritic P92 Steel at High Temperature: Experiments and Simulations

Mechanical and Magnetic Hysteresis As Indicators of the Origin and Inception of Fatigue Damage in Steel

The strain ratio-dependent multiaxial low cycle fatigue behaviour and life prediction of 316L stainless steel based on critical plane at elevated temperature

Strain energy-based low-cycle fatigue behaviour analyses of stainless-clad bimetallic steel

Mechanical Behavior and Fatigue Performance of Austenitic Stainless Steel under Consideration of Martensitic Phase Transformation

Cyclic Stress-Strain Response During Isothermal and Thermomechanical Fatigue

Multiaxial low cycle fatigue behavior and life prediction method of 316LN stainless steel at 550 °C