Abstract:Mesoporous silica materials were synthesized using tetraethoxysilane (TEOS) as precursor and liquid crystals (LCs) formed in mixtures of cationic cetyltrimethylammonium bromide (CTAB) and anionic sodium dodecyl sulfate (SDS) with additions of NaBr and 1-hexanol as templates. For this purpose, the formation of LCs in the mixtures under different conditions was first studied. It was found that the additions of 1-hexanol and NaBr can synergistically weaken the electrostatic interaction between CTAB and SDS and promote the growth of the ordered assemblies, leading to the significant expansion of the LC phase areas in both SDS excess area and CTAB excess area, respectively. The effects of 1-hexanol concentrations, surfactant concentrations, and pH values on the phase diagram and hence the structures of LCs were subsequently studied. These LCs are well-structured templates for the syntheses of mesoporous silica materials that were characterized using nitrogen adsorption/desorption analysis and scanning electron microscopy (SEM). It was shown that 1-hexanol played an important role in the formation of LC templates and hence effectively improved the specific surface area and order of mesoporous materials. The BET specific surface area was high up to 937 m(2)/g and the average pore diameter increased to 2.5 nm when the total concentration of CTAB and SDS was 0.2 mol/L, the molar fraction of CTAB in the mixture was 0.82, the concentration of 1-hexanol was 0.4 mol/L, and pH value was 2. These studies shed light on the syntheses of mesoporous materials with large specific surface area and highly ordered structure for multiple applications.

Synthesis Of 3d-Hexagonal (P6(3)/Mmc) Mesoporous Material Using C(N)Teabr-Type Surfactants Via Acidic Synthesis Route

Synthesis of 3D-Hexagonal (p63/mmc) Mesoporous Material Using CnTEABr-type Surfactants Via Acidic Synthesis Route

Synthesis Mechanism of Cationic Surfactant Templating Mesoporous Silica under an Acidic Synthesis Process

Counteranion effect on the formation of mesoporous materials under acidic synthesis process

Synthesis and Morphology Control of Sba-1 Mesoporous Silica with Surfactant of Cetyltrimethylammonium Bromide (Ctmabr)

Synthesis of Mesoporous Silica with A Three-Dimensional Hexagonal Ordered Structure Using Cationic and Amphoteric Mixed Surfactants

Synthesis of silica mesoporous crystals with controlled structure and morphology using gemini surfactant

Structural Study of Hexagonal Close-Packed Silica Mesoporous Crystal

Hybrid ethane–siloxane mesoporous materials with cubic symmetry

The effect of the counteranion on the formation of mesoporous materials under the acidic synthesis process.

Controlled Synthesis of Mesoporous Silicas Mcm-48 and Mcm-41 by Using Mixed Templates

Synthesis of Mesoporous Manganosilicates - Mn-Mcm-41, Mn-Mcm-48 and Mn-Mcm-L

Synthesis of Hollow-Shell MCM-48 Using the Ternary Surfactant Templating Method

Synthesis of Mesoporous Silica Single Crystal of Rhombic Dodecahedron Using Tri-head Group Quarternary Ammonium Cationic Surfactant

Synthesis of Continuous Mesoporous Silica Thin Films with Three-Dimensional Accessible Pore Structures

Formation Mechanism of Anionic Surfactant-Templated Mesoporous Silica

Structural Solution of Mesocaged Material Ams-8

Synthesis and Catalytic Performances of Mesoporous Aluminosilicates of Cubic and Hexagonal Structure with Stronger Acid Sites

Structural Investigations of Ams-N Mesoporous Materials by Transmission Electron Microscopy

Study on the Synthesis of Mesoporous Materials with Liquid Crystals Formed in SDS/CTAB/NaBr/1-Hexanol/H2O As Templates

Synthesis of Mesoporous Structured Material Based on Tin Oxide