Abstract:Quaternary ammonium (QA)-type polysulfone (PSf) anion exchange membranes (AEMs) with pendant carbonyl groups were synthesized by an environmentally friendly method. Low toxicity 3-chloro-2,2dimethylpropionyl chloride (CDPC) was chosen as an electrophilic reagent to introduce chloroalkyl groups to PSf, instead of highly toxic chloromethyl methyl ether. The experimental conditions were carefully optimized to avoid the Friedel-Crafts alkylation side reaction on the chloroalkyl group. After quaternizing with trimethylamine (TMA), AEMs were prepared by solution casting. The obtained AEMs showed good ionic conductivity and mechanical stability. The alkaline stability of these AEMs was excellent; the AEMs can maintain 95% of their initial conductivity after immersion in a 1 M NaOH aqueous solution at 80 degrees C for 10 days. The reason for this outstanding alkaline stability was evaluated by NMR and density functional theory calculations. The most severe degradation pathway, the S(N)2 reaction, can be weakened by the competing reaction between OH- and carbonyl groups. The formed intermediate oxygen anion can decrease the possibility of SN2 by reducing the electro-static potential of the QA groups. Because of the reversibility of the reaction between OH- and carbonyl groups, QA groups can survive longer in strong alkaline conditions at high temperature. Also, the possibility of S(N)2 reaction on the aromatic polymer chain can be decreased because of the positive charge carrier, QA groups, which are not directly attached to benzyl groups. Hoffmann elimination can not happen because there was no hydrogen atom on the beta-position of QA group. These structural advantages of the synthesized AEMs suggest another strategy that the potential for generalisation to other AEM systems and to improve the alkaline stability of QA-type AEMs.

Preparation and characterizations of novel zwitterionic membranes

Preparation of novel positively charged copolymer membranes for nanofiltration

Novel composite nanofiltration membranes containing zwitterions with high permeate flux and improved anti-fouling performance

A Novel Route for the Preparation of Hybrid Zwitterionic Membranes Containing Both Sulfonic and Carboxylic Acid Groups

Poly(olefin)-Based Anion Exchange Membranes Prepared Using Ziegler–Natta Polymerization

Preparation and Characterization of Novel Negatively Charged Hybrid Membranes

Fundamental Studies of Novel Inorganic–organic Charged Zwitterionic Hybrids

Fundamental studies of novel inorganic-organic charged zwitterionic hybrids: 2. Preparation and characterizations of hybrid charged zwitterionic membranes

Novel Cross-Linked Anion Exchange Membranes with Diamines As Ionic Exchange Functional Groups and Crosslinking Groups

Novel Composite Anion Exchange Membranes Based on Quaternized Polyepichlorohydrin for Electromembrane Application

Effect of Molecular Structure of Hybrid Precursors on the Performances of Novel Hybrid Zwitterionic Membranes

Synthesis of Novel Branched Fluorinated Poly(aryl Ether Oxadiazole)s for Anion Exchange Membranes

A general strategy to enhance the alkaline stability of anion exchange membranes

Intensification of mass transfer for zwitterionic amine monomers in interfacial polymerization to fabricate monovalent salt/antibiotics separation membrane

Zwitterion Membranes for Selective Cation Separation Via Electrodialysis

Preparation of high performance TFC RO membranes by surface grafting of small-molecule zwitterions

Novel synthetic route to prepare doubly quaternized anion exchange membranes for diffusion dialysis application

Preparation of novel zwitterionic polysulfone ultrafiltration membranes for the dual-enhanced antifouling and antibacterial properties by in-situ one pot crosslinking reaction

Novel Hollow‐fiber Anion‐exchange Hybrid Membranes: Preparation and Characterization

Surface Zwitterionicalization of Poly(Vinylidene Fluoride) Porous Membranes by Post-Reaction of the Amphiphilic Precursor

A Novel of Positively Charged Asymmetry Membrane Prepared from Poly (2,6-Dimethyl-1,4-phenylene Oxide) by in Situ Amination - Part Iii. Effect of Benzyl and Aryl Bromination Degrees of Polymer on Membrane Performance and Morphologies