Abstract:Earthquake-induced fractures in steel structures are characterised by high-strain low-cycle conditions. In order to investigate the ultra-low cyclic fatigue fracture of steel welded joints under earthquakes, two most commonly used structural steels (Q235B and Q345B) and the corresponding welds were studied by experiments and numerical analysis in this paper. Specimens were extracted from the base material, the weld metal and the heat affected zone to investigate the behaviour in different parts of the welded joint. Eighteen smooth round bars were tested under large strain amplitudes, the hysteretic properties, damage degradation characteristics and failure process were analyzed. Constitutive model named Chaboche model was calibrated to describe the cyclic hardening behaviour of these materials. Seventy-two notched round bars with three different notch sizes and two loading protocols were tested to study the fracture behaviour of different materials at different stress triaxialities and different strain amplitudes. Two micromechanical fracture models: cyclic void growth model and degraded significant plastic strain model were calibrated based on the test results. The micromechanical models and Chaboche model were incorporated into numerical simulations by software ABAQUS with subroutine VUMAT to predict the materials fracture. The results show that the failure process under cyclic loads is opposite to that of monotone loads. The dissipation capacity of Q345B is superior to that of Q235B. The fracture resistance deteriorate more in the weld zone under the same loading conditions. The validated models can be used to effectively and accurately evaluate the fracture in steel welded connections under ULCF conditions.

Acoustic emission during fatigue crack propagation in a micro-alloyed steel and welds

Low Cycle Fatigue Properties and Fracture Mechanism of Q345qC Steel and Its Welded Joint

Prediction of the Ultra-Low-Cycle Fatigue Damage of Q345qC Steel and Its Weld Joint

Fatigue damage evolution model of stainless-steel-cruciform-joint with weld defect using AE signal

Acoustic Emission of Metallic Specimen with Surface Defect During Fatigue Crack Growth

Study on Acoustic Emission Characteristics of Fatigue Damage of A7N01 Aluminum Alloy for High-Speed Trains

Evaluation of fatigue damage of structural steel based on attenuation of laser-induced surface acoustic wave

Tracing fracture damage evolution and identifying damage patterns in cast steel using advanced acoustic emission analysis

Fatigue life assessment of Q345 steel fillet welded joints with competitive failure modes

Study on the characteristics of magneto acoustic emission for mild steel fatigue

Experimental investigation on monitoring the evolution of fatigue microcracks in marine high-strength steel by nonlinear ultrasonic technique

Microstructure characterization and mechanism of fatigue crack propagation of 6082 aluminum alloy joints

FATIGUE DAMAGE OF STEEL WIRE BY ACOUSTIC EMISSION MONITORING

Evaluation of prediction models for crack length of duplex 2205 stainless steel based on acoustic emission technology

Study on fatigue temperature evolution and failure behavior of Q460 steel

Ultra-Low Cyclic Fatigue Fracture of Q235B and Q345B Steels and Their Butt Welded Joints

Characterization of Fatigue Damage in Hadfield Steel Using Acoustic Emission and Machine Learning-Based Methods

Fatigue crack propagation characteristics of aluminum/steel laser-metal inert gas fusion-brazed joints in different micro-zones

Fatigue Behaviour of 7N01-T4 Aluminium Alloy Welded by Ultrasonic-Assisted Friction Stir Welding

Research on the electromagnetic ultrasonic detection method of initiation crack based on multi-acoustic coefficients fusion

Prediction of fatigue crack growth in steel bridge components using acoustic emission