Solid-Solution Phosphor Ba-2(Zn,Mg)Si2o7:Eu2+,Ee(3+),Ce3+ Prepared In Air And Its Luminescent Properties
Deng Sheng-Zhi,Liu Chen,Yang Chu-Jun,Qiu Zhong-Xian,Zhou Wen-Li,Zhang Ji-Lin,Yu Li-Ping,Lian Shi-Xun
DOI: https://doi.org/10.11862/CJIC.2015.031
2015-01-01
Chinese journal of inorganic chemistry
Abstract:Ba1.97Zn1-xMgxSi2O7:0.03Eu and Ba1.97-gamma Zn0.9Mg0.1Si2O7:0.03 Eu,gamma-Ce3+ phosphors were synthesized in air condition by a high temperature solid-state reaction. Crystallization and optical properties were investigated by using powder X-ray diffraction and fluorescence spectrophotometer, respectively. Under the excitation of ultraviolet (330 similar to 360 nn), the emission spectra of these solid-solution phosphors exhibit multi-emission bands peaked at about 360 nm(blue-purple color), 500 nm (green color) and 590 similar to 725 run (red color), the two formers are corresponding to the 4f(6)5d(1)-4f(7) transition of Eu2+, the latter is originated from the (D0-FJ)-D-5-F-7(J=1,2,3,4) transitions of Eu3+. The investigated results indicate that part of En(3+) can be self-reduced to En' in the matrix and will reach the maximum when x=0.1 mol. When co-doping Ce3+ ions, the luminescent colors of the phosphors.Ba1.97-gamma Zn0.9 Mg0.1Si2O7:0.03Eu,gamma Ce3+ can be tunable from green to white to orange area. It had been found that the nominal composition Ba1.96Zn0.9Mg0.1Si2O7:0.03Eu,0.01Ce(3+) phosphor provides a white emission (0.323, 0.311) that is very close to the standard white (x=0.33, y=0.33), which shows that it is a potential white phosphor for LED-based. UV-chip: The energy transfer processes among rare earths and the luminescent mechanism were discussed.