Abstract:We report an efficient method to synthesize undoped and K-doped rare cubic tungsten trioxide nanowires through the thermal evaporation of WO3 powder without a catalyst. The WO3 nanowires are reproducible and stable with a low-cost growth process. The thermal evaporation processing was conducted in a three-zone horizontal tube furnace over a temperature range of 550–850 °C, where multiple substrates were placed at different temperature zones. The processing parameters, including pressure, temperature, type of gas, and flow rate, were varied and studied in terms of their influence on the morphology, aspect ratio and density of the nanowires. The morphologies of the products were observed with scanning electron microscopy. High resolution transmission electron microscopy, X-ray photoelectron spectroscopy, and X-ray diffraction studies were conducted to further identify the chemical composition, crystal structure and growth direction of the nanostructures. Additionally, the growth mechanism has been proposed. Furthermore, we investigated the potassium doping effect on the physical properties of the nanostructures. Photoluminescence measurements show that there were shorter emission bands at 360 nm and 410 nm. Field emission measurements show that the doping effect significantly reduced the turn-on electric field and increased the enhancement factor. Furthermore, as compared with related previous research, the K-doped WO3 nanowires synthesized in this study exhibited excellent field emission properties, including a superior field enhancement factor and turn-on electric field. The study reveals the potential of WO3 nanowires in promising applications for sensors, field emitters and light-emitting diodes.

Three‐Dimensional Tungsten Oxide Nanowire Networks

One-dimensional Sub-stoichiometric W3O8Nanowires Filled Carbon Nanotubes

Ultralight Interconnected Metal Oxide Nanotube Networks

A Study of Control Growth of Three-Dimensional Nanowire Networks of Tungsten Oxides: from Aligned Nanowires Through Hybrid Nanostructures to 3d Networks

Simple Approaches To Quality Large-Scale Tungsten Oxide Nanoneedles

Novel Route to WO<i><sub>x</sub></i>Nanorods and WS<sub>2</sub>Nanotubes from WS<sub>2</sub>Inorganic Fullerenes

Novel route to WOx nanorods and WS2 nanotubes from WS2 inorganic fullerenes.

An approach for synthesizing various types of tungsten oxide nanostructure.

ZnO Nanowire and $\hbox{ws}_{2}$ Nanotube Electronics

Fabrication and structural characterization of porous tungsten oxide nanowires

Large-Scale Synthesis of Tungsten Oxide Nanowires with High Aspect Ratio

Synthesis and Physical Characteristics of Undoped and Potassium-Doped Cubic Tungsten Trioxide Nanowires through Thermal Evaporation

Tungsten Oxide Nanowires on Tungsten Substrates

Xultraviolet-Visible Emission From Three-Dimensional Wo3-X Nanowire Networks

Synthesis and Electrical Characterization of Tungsten Oxide Nanowires

Filling Double-Walled Carbon Nanotubes with WO3 and W Nanowires Via Confined Chemical Reactions.

Synthesis and Applications of Γ-Tungsten Oxide Hierarchical Nanostructures

Synthesis of orthogonally assembled 3D cross-stacked metal oxide semiconducting nanowires

Tungsten oxide nanowire growth by chemically-induced strain

From Surfactant–Inorganic Mesostructures to Tungsten Nanowires The authors thank Prof. G. D. Stucky for helpful discussions. This work was supported by the National Science Foundation of China and the State key project of Fundamental Research for Nano-materials and Nano-structures.

Synthesis and Characterization of Tungsten Oxide Nanoscaled Fibers