Effect of Poly(ethylene Oxide) on Tribological Performance and Impact Fracture Behavior of Polyoxymethylene/polytetrafluoroethylene Fiber Composites

Yang Gao,Shuangyue Sun,Yadong He,Xiaodong Wang,Dezhen Wu
DOI: https://doi.org/10.1016/j.compositesb.2011.05.044
2011-01-01
Abstract:A novel type of polyoxymethylene (POM)-based composites with polytetrafluoroethylene (PTFE) fiber and poly(ethylene oxide) (PEO) was prepared via melt extrusion in order to enhance the friction lubrication and wear resistance of POM. The tribological experiments demonstrated that the coefficient of friction and wear rate of POM were both reduced by the incorporation of PTFE fiber, and furthermore, the higher the loading of PTFE fiber the better the tribological properties. The wear mechanism is derived from the thin film of PTFE formed on the contact-surfaces during sliding. The addition of PEO into POM/PTFE fiber composites can enhance the formation of transfer film on the mating surfaces during sliding contact, and thus further improves the friction and wear performance. The wear behaviors also depend on the normal loading and sliding duration, under which the transfer film could form appropriately. In addition, the abrasion of the dispersed PEO domains in matrix is also helpful to the heat dissipation when the counter-surface exerts oscillating forces on the POM surface. It should be emphatically mentioned that the use of PTFE fiber as tribological additive can improve the notched impact strength of POM, and the subsequent incorporation of PEO leads to a more significant toughening effect for POM. The morphological investigation reveals that the toughening effect is attributed to the dissipation of impact energy through the pullout of PTFE fiber and the plastic deformation of the POM matrix induced by PEO. Polarized optical microscopy demonstrates that the presence of PEO can interfere in the crystallization of POM and reduced the size of spherulites, and consequently weakened the sensitivity to notch. Although the POM-based composites underwent a different mode of thermal degradation from neat POM with a slight reduction in the temperature at rapid weight loss, their thermal stabilities were maintained well enough to meet the requirement for its application.
What problem does this paper attempt to address?