Abstract:Basalt fiber (BF) has high mechanical strength, good insulation performance and low cost. It is suitable to be used as reinforcement material in the manufacture of electrical equipment. However, the large surface inertia of basalt fiber makes it difficult to combine with the matrix material, which seriously limits its service life and application scenarios. In addition, the serious vacancy in the research of insulation properties also limits its production and application in the electrical field. Therefore, in order to solve the problem of difficult bonding between basalt fiber and resin matrix and make up for the research blank of basalt fiber composites in insulation performance, this paper provides a basalt fiber modification method—SiO2 coating, and tests the insulation and mechanical properties of the modified composite. We used nano-SiO2 coating solution to modify basalt fiber, and manufactured BF/resin composite (BFRP) by hand lay-up and hot-pressing technology, and experimentally analyzed the influence of nano-SiO2 content on the mechanical and insulation properties of the modified composite. Fourier transform infrared spectrum and scanning electron microscope analysis showed that nano-SiO2 was successfully coated on basalt fibers. Through the microdroplet debonding test, it was found that the IFSS of fiber/resin was improved by 35.15%, 72.97 and 18.9%, respectively, after the modification of the coating solution with SiO2 concentration of 0.5%, 1% and 1.5%, showing better interface properties; the single fiber tensile test found that the tensile strength of the modified fiber increased slightly. Among all composites, 1 wt% SiO2 coating modified composites showed the best comprehensive properties. The surface flashover voltage and breakdown field strength reached 13.12 kV and 33 kV/mm, respectively, which were 34.6% and 83% higher than unmodified composite. The dielectric loss is reduced to 1.43%, which is 33.8% lower than the dielectric loss (2.16%) of the untreated composite, showing better insulation ability; the tensile strength, bending strength and interlaminar shear strength were increased to 618.22 MPa, 834.74 MPa and 16.29 MPa, respectively, which were increased by 53%, 42.4% and 59.7%, compared with untreated composites. DMA and glass transition temperature showed that the modified composite had better heat resistance. TGA experiments showed that the resin content of the modified composite increased, and the internal structure of the composite became denser.

Interface Reaction and Property of Basalt Fiber Reinforced Al-based Composites

Microstructures and Mechanical Properties of Engineered Short Fibre Reinforced Aluminium Matrix Composites

Interface Reaction and Thermodynamic Analysis on Al2o3-Sio2(Sf)/Az91d Composite

Experimental Study on Basic Mechanical Properties of Basalt Fiber Reinforced Concrete

Mechanical Properties and Microstructures of Steel-basalt Hybrid Fibers Reinforced Cement-based Composites Exposed to High Temperatures

Interface reaction and thermodynamic analysis on the magnesium alloy matrix composite reinforced with alumina silicate short fibers

Enhanced interfacial interaction, mechanical properties and thermal stability of basalt fiber/epoxy composites with multi-scale reinforcements

Al2o3 Particles Reinforced Aluminium Matrix Composite Fabricated By Pressureless Infiltration Technique

Interface and Thermal Expansion of Carbon Fiber Reinforced Aluminum Matrix Composites

Effect of Interfacial BeO Content on Microstructure and Mechanical Properties of Beryllium/aluminum Composites

Processing and Mechanical Properties of Basalt Fibre-Reinforced Thermoplastic Composites

Effect of preset interfacial ZrB 2 particles on the microstructure and properties of C/C-AlSi composites

Microstructure and Properties of Csf/Al Composite Materials Prepaved by Squeezing-Infiltrating Process

Effect of Nano-SiO2 Modification on Mechanical and Insulation Properties of Basalt Fiber Reinforced Composites

Fabrication and Mechanical Characteristics of Multi-Laminated Aluminum Matrix Composites Reinforced by Continuous Basalt Fibers

Fabrication and Properties of Carbon Fibre - Basalt Fibre/Epoxy Resin Composites

Effect of Interfacial Microstructure on the Thermal-Mechanical Properties of Mesophase Pitch-Based Carbon Fiber Reinforced Aluminum Composites

SiC Fibre Reinforced Titanium Matrix Composite:Interface Evolution and Component Manufacturing

Interfacial Microstructure and Forming Mechanism of Brazing Cf/Al Composite with Al–Si Filler

Mechanical Properties under Compression and Microscopy Analysis of Basalt Fiber Reinforced Recycled Aggregate Concrete

Microstructure and mechanical properties of graphite fiber-reinforced high-purity aluminum matrix composite