Melting Point and Viscosity Measurement of Continuous Casting Mold Flux with Volatiles
Ze Wang,Junxue Zhao,Yi Kang,Ailin Hu,Xin Xin,Yaru Cui
DOI: https://doi.org/10.1002/srin.202100556
IF: 2.1258
2021-12-11
steel research international
Abstract:The composition of fluoride‐containing mold fluxes changes when their melting point or viscosity are measured because the fluoride in the mold fluxes evaporates at high temperatures. Therefore, the measured melting points and viscosities are not those of the original fluxes, and thus, the results are not accurate. Therefore, evaluating the effects of evaporation is essential to accurately investigate the relevant properties. Herein, the chemical composition of the slag is determined using thermogravimetric analysis (TGA), roasting tests, and evaporation mechanism after the physical properties of the slag are measured using conventional methods. The measured melting point and viscosity are then matched with the modified slag composition instead of the original composition. This method is applied to different fluoride‐containing mold fluxes. The weight of the mold fluxes is reduced by more than 10% during the measurements, indicating that a large amount of the volatiles react and evaporate. The actual flux compositions corresponding to the observed melting point or viscosity of the mold fluxes are obtained through roasting test and TGA; therefore, one can easily match the measured mold flux properties to the flux composition. This study will help in determining other physical properties of slag and other melts containing volatiles.
metallurgy & metallurgical engineering